Electrochemical stripping solution formula for vacuum ion plating

A technology of deplating solution and ions, which is applied in the field of vacuum ion plating electrochemical deplating solution formula, and can solve problems such as stability defects

Active Publication Date: 2017-12-01
广州市双石金属制品有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Since the current domestic coating equipment has defects in stability, and the operation is mostly manual, there will inevitably be a certain number of unqualified products in the production process of ion-plating decorative panels.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrochemical stripping solution formula for vacuum ion plating
  • Electrochemical stripping solution formula for vacuum ion plating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The vacuum ion plating electrochemical deplating solution formula is 1% adenosine diphosphate, 5% hydrochloric acid, 0.1% sodium silicate, 0.1% EDTA, 2% sodium chloride, 0.1% urotropine, 0.1% triethanolamine, the rest is water.

[0015] When using this formula for stripping, the surface coating of unqualified products will be removed in 30 seconds, and the samples after stripping the surface coating are analyzed by X-ray diffraction, and no coating elements are found, which proves that the film layer is completely stripped; Scanning electron microscope (SEM) tests were performed on the samples after surface coating, and it was found that the substrates were not corroded.

Embodiment 2

[0019] The vacuum ion plating electrochemical deplating solution formula is 5% adenosine triphosphate, 15% sulfuric acid, 1% sodium silicate, 5% EDTA, 20% sodium acetate, 3% urotropine, 1 % of triethanolamine, the rest is ethanol.

[0020] When using this formula for stripping, the surface coating of unqualified products will be removed in 30 seconds, and the samples after stripping the surface coating are analyzed by X-ray diffraction, and no coating elements are found, which proves that the film layer is completely stripped; Scanning electron microscope (SEM) tests were performed on the samples after surface coating, and it was found that the substrates were not corroded.

Embodiment 3

[0022] The vacuum ion plating electrochemical deplating solution formula is 2.5% adenosine diphosphate, 10% nitric acid, 0.5% sodium silicate, 3% EDTA, 10% sodium nitrate, 1.5% urotropine, 0.5 % of triethanolamine, and the rest is a mixed solvent of ethanol and water.

[0023] When using this formula for stripping, the surface coating of unqualified products will be removed in 30 seconds, and the samples after stripping the surface coating are analyzed by X-ray diffraction, and no coating elements are found, which proves that the film layer is completely stripped; Scanning electron microscope (SEM) tests were performed on the samples after surface coating, and it was found that the substrates were not corroded.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an electrochemical stripping solution formula for vacuum ion plating. The electrochemical stripping solution formula for vacuum ion plating comprises, by mass, 1%-5% of adenosine diphosphate or adenosine triphosphoric acid, 5%-15% of strong acid, 0.1%-1% of sodium silicate, 0.1%-5% of EDTA, 2%-20% of salt, 0.1%-3% of urotropin, 0.1%-1% of triethanolamine and the balance solvent. Compared with a traditional stripping solution, the adenosine diphosphate or the adenosine triphosphoric acid is added, the stripping rate is increased through the unique molecular structure of the adenosine diphosphate or the adenosine triphosphoric acid and interaction with a film material, and remarkable improvement is achieved.

Description

Technical field: [0001] The invention relates to a vacuum ion plating electrochemical deplating solution formula. Background technique: [0002] Coating technology has been widely used in various sectors of the national economy, especially in the field of decoration. Coating on products can improve the effect and taste of decoration, increase the added value of products, and prolong the service life, which has great economic benefits. In addition, the beautiful decorative appearance can satisfy people's pursuit of a comfortable life, and has good social benefits. At present, the demand for colored metal sheets in the domestic architectural decoration market is increasing, and the requirements for the film layer are also getting higher and higher, for example: the film layer should have richer colors to improve the decorative effect; the production process is more environmentally friendly , energy saving and automation. [0003] Ion plating is a new technology developed in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25F5/00
CPCC25F5/00
Inventor 朱常锦朱元义
Owner 广州市双石金属制品有限公司