A method for measuring tungsten content in steel

A determination method and technology of tungsten content, applied in the field of chemical analysis, can solve the problem of non-linearity of molybdenum interference
CN107664638BActive Publication Date: 2020-08-11PANGANG GROUP JIANGYOU CHANGCHENG SPECIAL STEEL
2 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN Β· China
Patent Type
Patents(China)
Current Assignee / Owner
PANGANG GROUP JIANGYOU CHANGCHENG SPECIAL STEEL
Publication Date
2020-08-11

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention belongs to the field of chemical analysis and particularly relates to a method for measuring tungsten content in steel. The method comprises the following steps: (a) mixing and heating the mixed acid of hydrochloric acid and nitric acid and a weighed steel sample, thereby dissolving the steel sample; (b) mixing with sulfur phosphor mixed acid and then heating till the sulfur phosphoric acid smoke appears in a mixed system, adding perchloric acid and then heating till pure perchloric acid smoke appears in the mixed system and separating the bottom of the appearing perchloric acidsmoke from the liquid level of the mixed system; (c) mixing with a dilute phosphoric acid solution, and then mixing with an ammonium ferrous sulfate solution, cooling to room temperature and then using a diluted phosphate solution for diluting and keeping constant volume, thereby acquiring to-be-developed mother liquor; and (d) taking some to-be-developed mother liquor, mixing with the thiocyanatesolution, stannous chloride solution, dilute sulfuric acid and a titanium trichloride solution, and then achieving the constant volume by using the stannous chloride solution, and developing to acquire the developing liquor; measuring the absorbency of the developing liquor; and calculating according to the measured absorbency value, thereby acquiring the tungsten content in the steel sample. Themeasuring method provided by the invention is high in accuracy, repeatability and reproducibility.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention belongs to the field of chemical analysis, in particular to a method for measuring tungsten content in steel. Background technique

[0002] Tungsten is silvery white and gray or black in powder form, and has the highest melting point among metals. As one of the alloying elements in steel, it is mainly used in the manufacture of special steel grades and hard alloys, permanent magnets, and black wire for electric lamps in steel production. It can increase the tempering stability, red hardness, and thermal strength of steel. And the formation of special carbides to increase wear resistance. The determination methods of tungsten content in steel introduced in the national standard are gravimetric method and tetraphenylarsenic chloride-thiocyanate-chloroform extraction spectrophotometric method. The above methods are relatively cumbersome and time-consuming.

[0003] In order to simplify the operation steps, researchers have applied thiocyan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More