Processing technology of baking-free bricks

A technology for processing and non-burning bricks, applied in the field of designing and building concrete, can solve the problems of unreasonable concrete mix design, high cost, inability to meet the needs of production and life, etc. reasonable effect

Inactive Publication Date: 2018-03-09
蔡建华
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing concrete mix design is unreasonable and cannot be applied to the needs of existing production and living, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The invention relates to a processing technology of non-fired bricks. The concrete is uniformly mixed with the following raw materials: sand 70~80, cement 7~12, lime 5~15, straw 0.5~1, additive 0.5~1 . 5. The sand is river sand or mountain sand, which is used to make non-burning bricks. The cement uses ordinary silicon broken salt cement as the cement, and slag cement or fly ash cement is used. Calcium oxide is used for lime, and fly ash is used as wet cement. For ash and dry ash, first, mix sand, cement, lime, straw and water according to the ratio, add additives and stir for 5 to 10 minutes, put it into a mold for molding, cut, and remove the mold after reaching the mold removal strength for natural maintenance.

[0015] The additives are triethanolamine and sodium sulfate. The fly ash binder is based on the organic binder sodium carboxymethyl cellulose, mixed with thickeners, enhancers and preservatives to become an organic binder for pellets, or added with oxidants,...

Embodiment 2

[0017] The concrete is uniformly mixed with the following raw materials: 70% sand, 70% cement, 5% lime, 0.5% straw, and 0.5% additive.

Embodiment 3

[0019] The concrete is uniformly mixed with the following raw materials: sand 80, cement 12, lime 15, straw 1, additive 1.5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to view more

Abstract

The invention discloses a processing technology of non-fired bricks. The concrete is uniformly mixed with raw materials in the following proportions: 70-80 sand, 7-12 cement, 5-15 lime, 0.5-1 straw, and 0.5-1 additive. 1.5. The sand is river sand or mountain sand, which is used to make unburned bricks. The cement uses ordinary silica-broken salt cement as the cement, and slag cement or fly ash cement is used. Calcium oxide is used for the lime, and fly ash is used as the wet cement. Ash and dry ash, first, mix sand, cement, lime, straw, and water according to the ratio, add additives and stir for 5 to 10 minutes, put them into a mold, shape, cut, and remove the mold after reaching the mold removal strength, then carry out natural maintenance, anti-corrosion Freeze disturbance compression strength twist loss is not more than 25%, water resistance saturated water strength is 5.0~10.0MPa water absorption rate> 20%.

Description

technical field [0001] The invention relates to the technical field of design concrete for construction, and in particular relates to a processing technology of unfired bricks. Background technique [0002] Concrete is a general term for engineering composite materials in which aggregates are cemented into a whole by cementitious materials. Generally speaking, the term concrete refers to the cement concrete obtained by using cement as the cementitious material, sand and stone as the aggregate; mixed with water (may contain admixtures and admixtures) in a certain proportion, and stirred. concrete. Concrete is the most widely used and used building material in civil engineering. Design and manufacture concrete according to the predetermined performance, and develop new varieties of lightweight, high-strength, and multi-functional concrete. [0003] The existing concrete mix design is unreasonable, cannot be applied to the needs of existing production and life, and the cost ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B28/02C04B28/08
CPCC04B28/04C04B28/021C04B28/08C04B14/06C04B22/064C04B18/24C04B24/122C04B22/147
Inventor 蔡建华
Owner 蔡建华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap