Soundproof heat-insulating polycarbonate (PC) sunlight panel

A polycarbonate and solar panel technology, applied in the field of PC solar panels, can solve the problems of poor sound insulation and heat insulation effect, and achieve the effects of improving heat insulation performance, improving sound insulation effect, and simple preparation of raw materials

Inactive Publication Date: 2018-05-18
JIANGSU GUOWEIXING PLASTIC TECH CO LTD
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the technical problem of poor sound and heat insulation effects of PC polycarbonate solar panels in the prior art, and to propose a PC polycarbonate solar panel that can be sound-insulated and heat-insulated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Soundproof heat-insulating polycarbonate (PC) sunlight panel
  • Soundproof heat-insulating polycarbonate (PC) sunlight panel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] See attached Figure 1-Figure 2 As shown, a sound-insulating and heat-insulating PC polycarbonate solar panel of the present invention includes a sponge 1 and a solar panel substrate 2. The solar panel substrate 2 is a double-layer structure, and the two-layer structure are fixed to each other, and are provided with square holes, and the sponge 1 is filled in the square holes of the solar panel substrate 2;

[0028] The raw materials of the solar panel substrate 2 include in parts by weight: 100 parts of polycarbonate, 10 parts of phenolic resin, 10 parts of polyphenylene ether sulfone, 2 parts of formaldehyde scavenger, 30 parts of melamine resin, 1 part of plasticizer, 1 part of dispersant, 0.5 part of antioxidant, and 0.5 part of modifier.

[0029] The sponge 1 is a transparent sponge; the solar panel substrate 2 is filled with the sponge 1 and then evacuated inside; the modifier is: a silane coupling agent, a titanate coupling agent, an aluminum acid One or more m...

Embodiment 2

[0033] See attached Figure 1-Figure 2 As shown, a sound-insulating and heat-insulating PC polycarbonate solar panel of the present invention includes a sponge 1 and a solar panel substrate 2. The solar panel substrate 2 is a double-layer structure, and the two-layer structure are fixed to each other, and are provided with square holes, and the sponge 1 is filled in the square holes of the solar panel substrate 2;

[0034] The raw materials of the solar panel substrate 2 include in parts by weight: 125 parts of polycarbonate, 15 parts of phenolic resin, 14 parts of polyphenylene ether sulfone, 3 parts of formaldehyde scavenger, 35 parts of melamine resin, 1.5 parts of plasticizer, 1.5 parts of dispersant, 0.75 parts of antioxidant, and 0.75 parts of modifier.

[0035] The sponge 1 is a transparent sponge; the solar panel substrate 2 is filled with the sponge 1 and then evacuated inside; the modifier is: a silane coupling agent, a titanate coupling agent, an aluminum acid One...

Embodiment 3

[0039] See attached Figure 1-Figure 2 As shown, a sound-insulating and heat-insulating PC polycarbonate solar panel of the present invention includes a sponge 1 and a solar panel substrate 2. The solar panel substrate 2 is a double-layer structure, and the two-layer structure are fixed to each other, and are provided with square holes, and the sponge 1 is filled in the square holes of the solar panel substrate 2;

[0040] The raw materials of the solar panel substrate 2 include in parts by weight: 150 parts of polycarbonate, 20 parts of phenolic resin, 18 parts of polyphenylene ether sulfone, 5 parts of formaldehyde scavenger, 40 parts of melamine resin, 2 parts of plasticizer, 2 parts of dispersant, 1 part of antioxidant, 1 part of modifier.

[0041] The sponge 1 is a transparent sponge; the solar panel substrate 2 is filled with the sponge 1 and then evacuated inside; the modifier is: a silane coupling agent, a titanate coupling agent, an aluminum acid One or more mixture...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of a PC sunlight panel, particularly to a soundproof heat-insulating polycarbonate (PC) sunlight panel. The PC sunlight panel comprises sponge and a sunlight panel substrate, wherein the sunlight panel substrate has a double-layer structure, in which the two layers are joined to each other in a fixed manner, and is provided with a square hole, and sponge fills the square hole formed in the sunlight panel substrate. The sunlight panel substrate is made from, by weight, 100-150 parts of polycarbonate, 10-20 parts of a phenolic resin, 10-18 parts of polyethersulfone, 2-5 parts of a formaldehyde capture agent, 30-40 parts of a melamine resin, 1-2 parts of a plasticizer, 1-2 parts of a dispersant, 0.5-1 part of an anti-oxidant, and 0.5-1 part of a modifier. The polycarbonate (PC) sunlight panel is good in sound and heat insulation and can be widely applied to greenhouses, household awnings and sound insulation for office rooms.

Description

technical field [0001] The invention relates to the technical field of PC solar panels, in particular to a PC polycarbonate solar panel capable of sound and heat insulation. Background technique [0002] PC sunshine board is a kind of engineering plastic sheet made of polycarbonate resin (Polycarbonate) by extrusion molding method. Polycarbonate has good light transmission, and its board is mostly used for building lighting and agricultural greenhouses, so it is called It is a PC solar panel. As a new type of building material that has emerged in recent years, PC sunshine board has good light transmission, super impact resistance, excellent crush resistance and abrasion resistance, and its impact strength is more than 250 times higher than that of ordinary glass. At present, it has been widely used in roofs, curtain walls, partitions, lighting facilities and advertising signs of industrial, agricultural, civil and public buildings, and its application fields are very broad....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L61/06C08L81/06C08L61/28
CPCC08L69/00C08L2205/02C08L2205/035C08L61/06C08L81/06C08L61/28
Inventor 陆国兴
Owner JIANGSU GUOWEIXING PLASTIC TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com