A kind of rust-removing phosphating solution for wire drawing and preparation method thereof

A phosphating liquid and wire technology, applied in the direction of metal material coating process, etc., can solve the problems of phosphating agent containing highly corrosive components, phosphating film is not strong enough, high cost of wastewater treatment, to achieve high thermodynamics, improve hardness , the effect of low production cost

Active Publication Date: 2020-04-14
鞍山晨雷科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problem of separating wire pickling and phosphating treatment processes, resulting in high cost of wastewater treatment caused by water washing, phosphating film is not strong enough, breakage occurs when drawing, and phosphating agent contains highly corrosive components problem, provides a kind of rust removal phosphating solution for wire drawing and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of rust-removing phosphating solution for wire drawing and preparation method thereof
  • A kind of rust-removing phosphating solution for wire drawing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A rust-removing phosphating solution for wire drawing, consisting of the following chemical components in mass percent:

[0037] Phosphoric acid 50%, nitric acid 1%, zinc oxide 5%, zinc dihydrogen phosphate 2%, zinc nitrate, nickel nitrate and ferrous nitrate 5%, manganese carbonate 2.5%, sodium fluoride 1.5%, citric acid 1.5%, perfluorinated Potassium octanesulfonate YF-95: 0.05%, water: 31.45%;

[0038] Wherein, the molar ratio of zinc nitrate, nickel nitrate and ferrous nitrate is 100:7:25.

[0039] At room temperature, take materials according to the above chemical composition distribution ratio, add zinc oxide, nitrate, manganese carbonate and complexing agent into water, stir until completely dissolved, then add dihydrogen phosphate, phosphoric acid, nitric acid and fluorine-containing surfactant , after fully stirring evenly, the product of rust removal and phosphating solution is obtained.

[0040] Place the workpiece to be treated in a 4-fold diluted rust rem...

Embodiment 2

[0042] A rust-removing phosphating solution for wire drawing, consisting of the following chemical components in mass percent:

[0043] Phosphoric acid 20%, nitric acid 10%, zinc oxide 10%, manganese dihydrogen phosphate 10%, zinc nitrate, nickel nitrate and ferrous nitrate 1%, manganese carbonate 0.5%, sodium fluoride 0.1%, tartaric acid 0.1%, perfluorooctyl quaternary ammonium iodide YF-134: 1%, water: 47.3%;

[0044] Wherein, the molar ratio of zinc nitrate, nickel nitrate and ferrous nitrate is 100:12:15.

[0045] At room temperature, take materials according to the above chemical composition ratio, add zinc oxide, nitrate, manganese carbonate and complexing agent into water, stir until completely dissolved, then add phosphoric acid, nitric acid, dihydrogen phosphate and fluorine-containing surfactant , after fully stirring evenly, the product of rust removal and phosphating solution is obtained.

[0046] Place the workpiece to be treated in a 4-fold diluted rust-removin...

Embodiment 3

[0048] A rust-removing phosphating solution for wire drawing, consisting of the following chemical components in mass percent:

[0049] Phosphoric acid 30%, nitric acid 5%, zinc oxide 1%, manganese dihydrogen phosphate 2.5%, zinc dihydrogen phosphate 2.5%, zinc nitrate, nickel nitrate and ferrous nitrate 10%, manganese carbonate 5%, alanine 3%, Citric acid 2%, YF-001 fluorocarbon high-efficiency leveling agent 0.5%, water: 38.5%;

[0050] Wherein, the molar ratio of zinc nitrate, nickel nitrate and ferrous nitrate is 10:1:2.

[0051] At room temperature, take materials according to the above chemical composition ratio, add zinc oxide, dihydrogen phosphate, nitrate, manganese carbonate and complexing agent into water, stir until completely dissolved, then add phosphoric acid, nitric acid and fluorine-containing surfactant , after fully stirring evenly, the product of rust removal and phosphating solution is obtained.

[0052]Place the workpiece to be treated in a 4-fold dilut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The purpose of the present invention is to solve the problem that the wire pickling and phosphating treatment processes are carried out separately, resulting in high cost of wastewater treatment caused by water washing, insufficient firmness of the phosphating film, fracture phenomenon in drawing, and high corrosive components contained in the phosphating agent. The problem is to provide a rust-removing phosphating solution for wire drawing and a preparation method thereof, belonging to the technical field of rust-removing and phosphating treatment of metal surfaces. The derusting and phosphating solution for wire drawing is composed of the following chemical components in mass percentage: concentrated phosphoric acid: 20~50%; concentrated nitric acid: 1~10%; zinc oxide: 1~10%; dihydrogen phosphate: 2~ 10%; nitrate: 1~10%; manganese carbonate: 0.5~5%; complexing agent: 0.2~5%; fluorine-containing surfactant: 0.05~1%; water: balance. After being treated by the rust-removing phosphating solution of the present invention, a layer of gray-black uniform and dense phosphating film is formed on the surface of the steel wire and welded steel pipe, which plays a better lubricating role in the drawing and cold working process.

Description

technical field [0001] The invention belongs to the technical field of rust-removing and phosphating treatment on metal surfaces, and in particular relates to a rust-removing and phosphating solution for wire drawing and a preparation method thereof. Background technique [0002] Due to the existence of iron scale on the surface of the wire rod during production and storage, it seriously affects the subsequent drawing of the wire rod and the surface quality of the product. Therefore, pickling and phosphating are essential and important processes in the production of wire rods. The so-called phosphating is a process of forming a phosphate chemical conversion film on the metal surface through chemical and electrochemical reactions. The formed phosphating film plays a role of anti-friction and lubrication in the subsequent drawing process, and also improves the resistance of the wire. Oxidation properties and anti-corrosion properties. Most of the existing wire phosphating tre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C22/18C23C22/36C23G1/08
CPCC23C22/184C23C22/365C23G1/085C23G1/088
Inventor 徐红波吴勇奇陈雷尚雪薇
Owner 鞍山晨雷科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap