Aerated concrete block and preparation method thereof

A technology of aerated concrete and a manufacturing method, applied in ceramic products, other household appliances, applications, etc., can solve the problems of high brick cost, low fly ash mixing amount, and inability to control foaming efficiency well, etc. To achieve the effect of reducing the cost of brick making and reducing the utilization rate

Inactive Publication Date: 2018-06-19
安徽建鑫新型墙材科技有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The disadvantages of the above-mentioned traditional aerated concrete blocks are: the addition of fly ash is low, and the prices of lime and cement are high, resulting in high brick costs, and the foaming efficiency cannot be well controlled. Therefore, we propose an aerated concrete block and its manufacturing method to solve this problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An aerated concrete block and a manufacturing method thereof, wherein the raw materials for manufacturing the aerated concrete block are composed of slag, tailings, phosphogypsum, fly ash, graphite, concentrated high-foaming essence, vermiculite and natron. The mass parts of the manufacturing raw materials are 20 parts of slag, 30 parts of tailings, 20 parts of phosphogypsum, 10 parts of fly ash, 2 parts of graphite, 3 parts of concentrated high-foaming essence, 1 part of vermiculite, and 10 parts of natron.

[0019] The manufacturing method of described air-entrained concrete block comprises the following steps:

[0020] (1) Ingredients: Weigh a certain amount of slag, tailings, phosphogypsum and fly ash for mass ratio;

[0021] (2) Pulverization: Pulverize the ingredients that have been proportioned in step (1), and the pulverization time is 30 minutes. After the pulverization is completed, sieve through a 180-mesh sieve;

[0022] (3) Addition of auxiliary materials:...

Embodiment 2

[0029] An aerated concrete block and a manufacturing method thereof, wherein the raw materials for manufacturing the aerated concrete block are composed of slag, tailings, phosphogypsum, fly ash, graphite, concentrated high-foaming essence, vermiculite and natron. The mass parts of the manufacturing raw materials are 30 parts of slag, 35 parts of tailings, 30 parts of phosphogypsum, 20 parts of fly ash, 1 part of graphite, 1 part of concentrated high-foaming essence, 0.5 parts of vermiculite, and 7 parts of natron.

[0030] The manufacturing method of described air-entrained concrete block comprises the following steps:

[0031] (1) Ingredients: Weigh a certain amount of slag, tailings, phosphogypsum and fly ash for mass ratio;

[0032] (2) Grinding: Grinding the ingredients that have been proportioned in step (1) for 35 minutes, and sieving through a 1200-mesh sieve after the grinding is completed;

[0033] (3) Addition of auxiliary materials: Weigh a certain amount of graph...

Embodiment 3

[0040] An aerated concrete block and a manufacturing method thereof, wherein the raw materials for manufacturing the aerated concrete block are composed of slag, tailings, phosphogypsum, fly ash, graphite, concentrated high-foaming essence, vermiculite and natron. The mass parts of the manufacturing raw materials are 25 parts of slag, 30 parts of tailings, 30 parts of phosphogypsum, 15 parts of fly ash, 1.5 parts of graphite, 1 part of concentrated high-foaming essence, 0.5 parts of vermiculite, and 10 parts of natron.

[0041] The manufacturing method of described air-entrained concrete block comprises the following steps:

[0042] (1) Ingredients: Weigh a certain amount of slag, tailings, phosphogypsum and fly ash for mass ratio;

[0043] (2) Grinding: Grinding the ingredients proportioned in step (1), the grinding time is 33 minutes, and sifting through a 190-mesh sieve after the grinding is completed;

[0044] (3) Addition of auxiliary materials: Weigh a certain amount of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aerated concrete block and a preparation method thereof. The aerated concrete block is prepared from raw materials in parts by mass as follows: 20-30 parts of slag, 30-35 parts of tailings, 20-30 parts of phosphogypsum, 10-20 parts of fly ash, 1-2 parts of graphite, 1-3 parts of concentrated high foamer, 0.5-1 part of vermiculite and 7-10 parts of sodium silicate. The aerated concrete block can be produced in a factory in a large batch manner with the traditional aerated concrete block production process, the strength of the aerated concrete block also meets certainstandard, by means of industrial waste residues discharged by a chemical enterprise, industrial refuse produced by the chemical enterprise is used to the greatest extent, use rate of lime and cement is reduced, brick manufacture cost is reduced greatly, and foaming capacity can be controlled effectively by changing various parameters of the production process.

Description

technical field [0001] The invention relates to the technical field of aerated concrete blocks, in particular to an aerated concrete block and a manufacturing method thereof. Background technique [0002] Air-entrained concrete block is a kind of building material that fully foams the foaming agent by mechanical means, mixes the foam and cement slurry evenly, and uses the pumping system of the foaming machine for cast-in-place construction or mold molding. It has become a new type of lightweight insulation material with a large number of closed pores, and the aerated concrete block has certain sound insulation, light shock resistance and compression resistance, because these reasons are widely used in the production of buildings today. [0003] The disadvantages of the above-mentioned traditional aerated concrete blocks are: the addition of fly ash is low, and the prices of lime and cement are high, resulting in high brick costs, and the foaming efficiency cannot be well con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/26C04B38/10
CPCC04B28/26C04B18/10C04B18/12C04B22/144C04B18/08C04B14/024C04B14/202C04B2103/42C04B38/10
Inventor 孙坚强宋军徐林菲
Owner 安徽建鑫新型墙材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com