Stainless steel A-TIG welding active agent and welding method

A welding method and activating agent technology, applied in welding medium, welding equipment, welding equipment and other directions, can solve the problems of human health impact, containing halide, etc., to improve welding quality, improve safety, and form welds.

Inactive Publication Date: 2018-07-06
CHINA NUCLEAR IND 23 CONSTR
View PDF6 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that the existing stainless steel A-TIG activator contains halides and has an impact on human health, the present invention proposes a stainless steel A-TIG welding activator

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stainless steel A-TIG welding active agent and welding method
  • Stainless steel A-TIG welding active agent and welding method
  • Stainless steel A-TIG welding active agent and welding method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The activator of the present invention is used to perform A-TIG welding on a 321 stainless steel plate with a thickness of 6 mm. Among them, the active agent powder is composed of SiO with a mass percentage of 30% 2 Powder, 8% Cr 2 o 3 Powder, 15% Al 2 o 3 Powder, 13% TiO 2 Powder, 7% MnO 2 Powder, 7% Fe 2 o 3 Powder, 15% B 2 o 3 powder and 5% La 2 o 3Powder composition. WSM-315D full-digital DC pulse argon arc welding machine is used for welding operation. The main welding parameters are: welding current value is 110A~130A, welding voltage value is 10V~14V, welding speed is 2~5m / h, welding torch inclination angle is 70°~80°, the protective gas is argon, and the gas flow rate is 10~20L / min.

[0039] eventually get as figure 1 Frontal photographs of welds shown and as figure 2 The photo of the back of the weld is shown, and the weld tension test is carried out on the welded stainless steel plate, and the test results shown in Table 1 are obtained.

[004...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of stainless steel welding, and particularly relates to a stainless steel A-TIG welding active agent and a welding method. To solve the problem that an existing stainless steel A-TIG welding active agent contains halide, influences are caused to the human body health, the stainless steel A-TIG welding active agent is disclosed. The stainless steel A-TIGwelding active agent comprises active agent powder. The active agent powder comprises, by mass percent, 10%-30% of SiO2 powder, 5%-20% of Cr2O3 powder, 15%-50% of Al2O3 powder, 10%-20% of TiO2 powder, 5%-20% of MnO2 powder, 5%-20% of Fe2O3 powder, 5%-30% of B2O3 powder and 3%-8% of La2O3 powder. The active agent is adopted for conducting stainless steel A-TIG welding, influences of the halide onthe operator health can be avoided, and the welding efficiency can be improved.

Description

technical field [0001] The invention belongs to the technical field of stainless steel welding, and in particular relates to a stainless steel A-TIG welding activator and a welding method. Background technique [0002] Because the traditional TIG welding, that is, non-melting inert gas tungsten shielded welding, has the advantages of high welding quality, stable welding process, many materials suitable for welding, strong reliability, and the weld metal is not easy to deteriorate, so it is widely used. However, with the continuous improvement of welding requirements, this welding method also has certain limitations. For example, due to the limited current bearing capacity of the tungsten electrode, the arc energy density is reduced and its power density is limited, resulting in low deposition efficiency, shallow welding penetration and low production efficiency. [0003] In recent years, under the same welding process, A-TIG welding can effectively increase the welding pene...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/36B23K9/167
CPCB23K9/167B23K35/3606B23K35/361
Inventor 任丽丽冯英超扈晓刚张东辉刘金平
Owner CHINA NUCLEAR IND 23 CONSTR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap