Modified porous material suitable for polypropylene material and use thereof

A polypropylene material and porous material technology, applied in the field of modified porous materials, can solve the problems of poor selectivity of small molecules and inconspicuous adsorption effect, so as to improve the adsorption effect and solve the emission effect

Inactive Publication Date: 2018-07-31
JIANGLIN GUIZHOU HI TECH DEV CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above adsorbents mainly rely on physical adsorption, which has the disadvantages of poor selectivity to small molecules and insignificant adsorption effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1: A modified porous material suitable for polypropylene materials is a modified porous material prepared with talcum powder as a matrix and urea as a modifier; the preparation method of the modified porous material includes the following steps :

[0022] 1) Dissolve urea in water to make 2mol / L urea solution, product A;

[0023] 2) Put 1Kg of talc powder into product 1LA, stir for 4 hours, filter out the talc powder and dry at 120°C to obtain product B;

[0024] 3) Grind product B and pass through a 800-mesh sieve to obtain a modified porous material.

Embodiment 2

[0025] Embodiment 2: A modified porous material suitable for polypropylene materials is a modified porous material made of mesoporous silica as a matrix and benzoylhydrazine as a modifier; the modified porous material The preparation method comprises the steps:

[0026] 1) Dissolve benzoic hydrazide in water to prepare a benzoyl hydrazide solution with a concentration of 1mol / L to obtain product A;

[0027] 2) Put mesoporous silica into product A, stir for 1 hour, filter out mesoporous silica and dry at 90°C to obtain product B;

[0028] 3) Grind product B and pass through a 900-mesh sieve to obtain a modified porous material.

Embodiment 3

[0029] Embodiment 3: A modified porous material suitable for polypropylene materials is a modified porous material prepared with artificial zeolite powder as a matrix and glycine as a modifier; the preparation method of the modified porous material includes the following step:

[0030] 1) Dissolve glycine in water to prepare a 2mol / L glycine solution to obtain product A;

[0031] 2) Put artificial zeolite powder into product A, stir for 2 hours, filter out artificial zeolite powder and dry at 105°C to obtain product B;

[0032] 3) Grind product B and pass through a 2000-mesh sieve to obtain a modified porous material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified porous material suitable for a polypropylene material and use thereof, the modified porous material is prepared by using a porous mineral as a matrix and a nucleophilic reagent capable of reacting with a carbonyl group as a modifier; a preparation method of the modified porous material comprises the following steps: 1) dissolving the nucleophilic reagent in waterfor preparing a nucleophilic reagent solution, an emulsion or a suspension to obtain a product A; 2) placing the porous mineral into the product A, stirring for 1-10h, filtering the porous mineral out and drying at 90-130DEG C to obtain a product B; 3) grinding and sieving the product B to obtain a modified porous material. The modified porous material can solve the emission of aldehyde and ketone molecules in the polypropylene material processing process, and has a good adsorption effect on small aldehyde and ketone molecules.

Description

technical field [0001] The invention relates to a modified porous material and its application, in particular to a modified porous material suitable for polypropylene material and its application. Background technique [0002] Modified polypropylene material has been widely used in automotive interior parts, and has the characteristics of low cost, light weight and good performance. The polypropylene material itself is non-toxic. During the use of the car, especially in the high-temperature interior environment, the low-level aldehydes and ketones remaining in the modified polypropylene material will emit and cause damage to the human body. The types of aldehydes and ketones include formaldehyde, acetaldehyde, acrolein, acetone, and volatile aromatic aldehydes, etc., which are mainly derived from residual monomers during the synthesis of polypropylene resins, and small molecules produced during the degradation of modified polypropylene materials. Wait. Therefore, in order ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08K9/12C08K7/26C08L23/12
CPCC08K9/12C08K7/26C08L23/12
Inventor 龙雪彬杜西兰石敏瞿进宋季岭
Owner JIANGLIN GUIZHOU HI TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products