390MPa level LP steel plate and production method thereof

A production method and technology for steel plates, which are used in casting molten material containers, manufacturing tools, metal processing equipment, etc., can solve the problems of complex production process, small changes in steel plate thickness and specifications, and low production efficiency, and achieve the effect of simple process flow.

Active Publication Date: 2018-08-14
ANGANG STEEL CO LTD
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] 1) The steel plate thickness change specification is small, and the scope of application is narrow;
[0008] 2) The wedge shape of the steel plate rolled in the last pass is adopted, and the control accuracy is poor;
[0009] 3) The production process is complicated, the production efficiency is low, and the control stability is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The chemical composition of molten steel in molten steel tank 1 is: C 0.04%; Si 0.35%; Mn 1.00%; P 0.020%; S0.015%; Cr 0.1%; V 0.3%; Impurities to avoid;

[0046] The second chemical composition of the molten steel in the molten steel tank 2 is: C 0.12%; Si 0.20%; Mn 0.30%; P 0.020%; S0.015%; Nb 0.01%; Ti 0.01%; V 0.4%; 0.005%; the rest is Fe and unavoidable impurities;

[0047] Two tanks of molten steel are used to mix and pour continuous casting billets. After sampling inspection, the chemical composition of the head (corresponding to the thin end of LP steel plate) is chemical composition 1, and the chemical composition of the tail (corresponding to the thick end of LP steel plate) is chemical composition 2. , the middle chemical composition is: C 0.089%; Si 0.28%; Mn 0.64%; V 0.35%; Nb 0.006%; Ti 0.005%; Cr 0.25%; Als 0.005%;

[0048] The continuous casting billet is rolled into a wedge-shaped LP steel plate, the thickness of the thin end is 12mm, the thickness of...

Embodiment 2

[0050] The chemical composition of molten steel in molten steel tank 1 is: C 0.07%; Si 0.55%; Mn 1.55%; P 0.015%; S0.010%; Cr 0.6%; V 0.6%; Impurities to avoid;

[0051] The second chemical composition of the molten steel in the molten steel tank 2 is: C 0.15%; Si 0.40%; Mn 0.60%; P 0.015%; S0.010%; Nb 0.03%; Ti 0.03%; 0.045%; the rest is Fe and unavoidable impurities;

[0052] Two tanks of molten steel are used to mix and pour continuous casting billets. After sampling inspection, the chemical composition of the head (corresponding to the thin end of LP steel plate) is chemical composition 1, and the chemical composition of the tail (corresponding to the thick end of LP steel plate) is chemical composition 2. , the middle chemical composition is: C 0.11%; Si 0.48%; Mn 1.1%; V 0.7%; Nb 0.015%; Ti 0.015%; Cr 0.56%; Als0.045%;

[0053] The continuous casting billet is rolled into a wedge-shaped LP steel plate, the thickness of the thin end is 20mm, the thickness of the thick e...

Embodiment 3

[0055] The chemical composition of molten steel in molten steel tank 1 is: C 0.06%; Si 0.5%; Mn 1.40%; P 0.010%; S0.005%; Cr 0.45%; V 0.5%; Impurities to avoid;

[0056] The chemical composition two of the molten steel in the molten steel tank 2 is: C 0.12%; Si 0.35%; Mn 0.50%; P 0.010%; S0.005%; Nb 0.02%; Ti 0.02%; 0.035%; the rest is Fe and unavoidable impurities;

[0057] Two tanks of molten steel are used to mix and pour continuous casting billets. After sampling inspection, the chemical composition of the head (corresponding to the thin end of LP steel plate) is chemical composition 1, and the chemical composition of the tail (corresponding to the thick end of LP steel plate) is chemical composition 2. , the middle chemical composition is: C 0.09%; Si 0.42%; Mn 1.02%; Nb 0.01%; V 0.065%; Ti 0.015%; Cr 0.42%; Als 0.030%;

[0058] The continuous casting billet is rolled into a wedge-shaped LP steel plate, the thickness of the thin end is 16mm, the thickness of the thick e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Impact energyaaaaaaaaaa
Yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a 390MPa level LP steel plate and a production method thereof. The LP steel plate is a wedge steel plate with one end thin and one end thick; the chemical component of the thin end of the LP steel plate is the first chemical component, and the chemical component of the thick end of the LP steel plate is a second chemical component. The chemical component of the middle of the LP steel plate is in transition from the first chemical component to the second chemical component from the thin end to the thick end, the yield strength of the LP steel plate ranges from 390 MPa to 455 MPa, and -20 DEG C impact power is larger than or equal to 120J. Two cans of molten steel with different chemical components are adopted to pour a continuous casting billet, the continuous casting billet has the evenly changed chemical component in the longitudinal direction, the continuous casting billet is rolled to directly produce the LP steel plate, the LP steel plate has the beneficialeffect that from the thin end to the thick end, the property is uniform and consistent, and the LP steel plate is excellent in whole property and high in adaptation.

Description

technical field [0001] The invention relates to the technical field of metallurgy, in particular to a 390MPa grade LP steel plate and a production method thereof. Background technique [0002] LP (longitudinal variable thickness) steel plate refers to a steel plate with a special longitudinal shape whose thickness changes continuously along the rolling direction. It is a steel plate whose longitudinal thickness is changed by continuously changing the opening of the roll during the rolling process. Since the longitudinal variable thickness steel plate can change its thickness according to the load bearing conditions, it can optimize the design of structural sections such as bridges, hulls, buildings, etc., which can not only reduce the amount of steel used, reduce the number of welding times, but also improve the thickness of the joints through equal thickness Operability, such as omission of backing plate and taper processing, etc. [0003] The Chinese patent with the appli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/38C22C38/02C22C38/04C22C38/06C22C38/24C22C38/26C22C38/28B22D41/22B21B1/38