A production method and technology of bamboo chips, which are applied in the field of plate manufacturing, can solve problems such as low bonding strength and poor water resistance, and achieve good bonding effect, improved waterproof performance, and good curing effect

Active Publication Date: 2018-08-24
广西艾尚嘉家居有限公司
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the adhesives used in the prior art contain formaldehyde, and the adhesives without formaldehyde can be natural po

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method for formaldehyde-free bamboo chip plate

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0027] Example 1

[0028] A manufacturing method of formaldehyde-free bamboo board includes the following steps:

[0029] (1) Heat treatment: Put the bamboo in hot steam for 5 hours;

[0030] (2) Making bamboo slices;

[0031] (3) Drying: Place the wood in a dryer with a relative air humidity of 10%, and dry it at a temperature of 50°C and a wind speed of 10m / s until the moisture content of the wood is 23%;

[0032] (4) Repairing: repairing and finishing the boards with bad shapes;

[0033] (5) One-time gluing: Coating A adhesive on the surface of the wood to form a glue layer, the coating amount of the A adhesive is 100g / m 2 The A adhesive is composed of the following raw materials in parts by mass: 30 parts of chitosan, 10 parts of konjac chitosan, 4 parts of lysozyme, 40 parts of fish gelatin, 10 parts of montmorillonite, 1 part of salicylic acid Parts, 6 parts of potassium dichromate;

[0034] (6) Tissue culture: The fiber angle between the two bamboo boards is 90 degrees, and the nu...

Example Embodiment

[0041] Example 2

[0042] A manufacturing method of formaldehyde-free bamboo board includes the following steps:

[0043] (1) Heat treatment: Put the bamboo in hot steam for 3 hours;

[0044] (2) Making bamboo slices;

[0045] (3) Drying: Place the wood in a dryer with a relative air humidity of 20%, and dry it at a temperature of 40°C and a wind speed of 20m / s until the moisture content of the wood is 15%;

[0046] (4) Repairing: repairing and finishing the boards with bad shapes;

[0047] (5) One-time gluing: Coating A adhesive on the wood surface to form a glue layer, and the coating amount of the A adhesive is 200g / m 2 The A adhesive is composed of the following raw materials in parts by mass: 20 parts of chitosan, 30 parts of konjac chitosan, 1 part of lysozyme, 50 parts of fish gelatin, 5 parts of montmorillonite, 5 parts of salicylic acid 1 part, potassium dichromate 1 part;

[0048] (6) Tissue culture: The fiber angle between the two bamboo boards is 90 degrees, and the number of...

Example Embodiment

[0055] Example 3

[0056] A manufacturing method of formaldehyde-free bamboo board includes the following steps:

[0057] (1) Heat treatment: Put the bamboo in hot steam for 4 hours;

[0058] (2) Making bamboo slices;

[0059] (3) Drying: Put the wood in a dryer with a relative air humidity of 15%, and dry it at a temperature of 45°C and a wind speed of 15m / s until the moisture percentage of the wood is 20%;

[0060] (4) Repairing: repairing and finishing the boards with bad shapes;

[0061] (5) One-time gluing: Coating A adhesive on the surface of wood to form a glue layer, the coating amount of the A adhesive is 150g / m2; the A adhesive is composed of the following raw materials in parts by mass : 25 parts of chitosan, 20 parts of konjac chitosan, 3 parts of lysozyme, 45 parts of fish gelatin, 8 parts of montmorillonite, 3 parts of salicylic acid, 5 parts of potassium dichromate;

[0062] (6) Tissue culture: The fiber angle between the two bamboo boards is 90 degrees, and the number of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production method for a formaldehyde-free bamboo chip plate. The production method comprises the steps of heat treatment, bamboo chip production, drying, repair, primary adhesive coating, assembly, pre-pressing, secondary adhesive coating, hot-pressing, cooling, edge cutting and polishing, wherein the heat treatment process is placing bamboo in hot steam and insulating heat for 3-5h; the drying is drying wood until the water percentage content of the wood is 15-23%; the primary adhesive coating process is coating the surface of the wood with an adhesive A to form an adhesive layer; the pre-pressing process is standing the assembled wood for 10-20min and then pre-pressing for 10-20min at 0-5 DEG C, wherein the pre-pressing pressure is 0.5-1.0Mpa; the secondary adhesive coating process is coating the surface of the wood with an adhesive B to form an adhesive layer; and the hot-pressing process is pressing the pre-pressed wood for 2-3min under the pressure of 1.0-1.5Mpa and at the temperature of 80-85 DEG C. The bamboo chip plate produced by the production method for the bamboo chip plate is formaldehyde-free, and high in adhesiveness and water resistance.

Description

technical field [0001] The invention relates to the technical field of board manufacture, in particular to a method for making formaldehyde-free bamboo boards. Background technique [0002] Adhesives containing formaldehyde are used in the board manufacturing process, so using adhesives containing formaldehyde to make furniture will release formaldehyde. In addition to causing respiratory and nervous system diseases, such as cough, sore throat, chest tightness, dizziness, nausea, limb weakness, dyspnea, lethargy and other symptoms, formaldehyde can also induce the development of cancers such as nose cancer, throat cancer, skin cancer and leukemia. occur. [0003] Most of the adhesives used in the prior art contain formaldehyde, and the adhesives without formaldehyde can be natural polymers, mainly soybean protein adhesives, etc., but this adhesive has low bonding strength and poor water resistance. shortcoming. Therefore, the preparation of a formaldehyde-free adhesive wi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27K9/00B27K5/00B27K5/04B27D1/08C09J105/08C09J11/08C09J11/04C09J105/02C09J11/06C10C5/00
CPCB27D1/08B27K5/0085B27K5/04B27K9/002C08L2205/02C08L2205/03C08L2205/035C09J11/04C09J11/06C09J11/08C09J105/02C09J105/08C10C5/00C08L89/00C08L5/08C08K3/346C08K5/098Y02E50/10Y02P20/54
Inventor 杨静
Owner 广西艾尚嘉家居有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka