Method for synthesizing and preparing nano-particle reinforced composite through multi-dimension vibration assistance

A technology of reinforced composite materials and nanoparticles, which is applied in the field of nanoparticle-reinforced composite materials prepared by multi-dimensional vibration-assisted synthesis, can solve the problems of dynamic condition and speed limitation, achieve particle roundness, improve bonding strength, and improve comprehensive performance. Effect

Active Publication Date: 2018-08-24
JIANGSU UNIV
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is: according to the needs of the synthesis process dynamics of the in-situ particle reinforced composite material prepared by the melt reaction method, to provide a method for preparing nano-particle reinforced composite material using multi-dimensional vibration-assisted synthesis, to solve the in-situ synthesis of the melt reaction Problems caused by velocity-limited kinetic conditions in the process of preparing particle-reinforced composites

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for synthesizing and preparing nano-particle reinforced composite through multi-dimension vibration assistance
  • Method for synthesizing and preparing nano-particle reinforced composite through multi-dimension vibration assistance
  • Method for synthesizing and preparing nano-particle reinforced composite through multi-dimension vibration assistance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Embodiment one: preparation (Al 3 Zr (s) +Al 2 o 3(s) ) particle reinforced aluminum matrix composites

[0038] Raw materials: base metal: industrial pure aluminum; solid powder: industrial zirconium carbonate (Zr(CO 3 ) 2 ) powder, the purity is 99.20wt.%, refining degassing agent and slag removing agent;

[0039] In situ reaction equation: 13Al (l) +3Zr(CO 3 ) 2(s) =3Al 3 Zr (s) +2Al 2 o 3(s) +6CO 2 ↑

[0040] Particle reinforcement phase: Al 3 Zr (s) and Al 2 o 3(s)

[0041] The preparation process is as follows:

[0042] The first step: the reaction salt is preheated and dried, and the metal melt is smelted to the synthesis temperature;

[0043] 1Kg of industrial pure aluminum is melted in a 20kW crucible resistance furnace and heated up to 850°C for degassing and slag removal; all reagents used are fully dried at 250°C, of ​​which Zr(CO 3 ) 2 Grind into fine powder and sieve, the particle size is less than 100μm, weighed for later use, Zr(CO ...

Embodiment 2

[0053] Embodiment 2: Preparation of Al 2 o 3(s) Particulate Reinforced Aluminum Matrix Composites

[0054] Raw materials: base metal: industrial pure aluminum; solid powder: industrial cerium carbonate (Ce 2 (CO 3 ) 3 ) powder, the purity is 99.20wt.%, refining degassing agent and slag removal agent.

[0055] In situ reaction equation: 4Al+3CeO 2 →2Al 2 o 3 +3Ce

[0056] Particle reinforcement phase: Al 2 o 3(s)

[0057] The preparation process is as follows:

[0058] The first step: the reaction salt is preheated and dried, and the metal melt is smelted to the synthesis temperature;

[0059] 1Kg of industrial pure aluminum is melted in a 20kW crucible-type resistance furnace and heated up to 850°C for degassing and slag removal; all reagents used are fully dried at 250°C, and industrial cerium carbonate (Ce 2 (CO 3 ) 3 ) powder is ground into a fine powder and sieved, the particle size is less than 100 μm, and it is used after weighing, Ce 2 (CO 3 ) 3 The ad...

Embodiment 3

[0069] Embodiment three: preparation (Al 3 Zr (s) +Al 2 o 3(s) ) particle reinforced aluminum matrix composites

[0070] Raw materials: base metal: industrial pure aluminum; solid powder: industrial zirconium carbonate (Zr(CO 3 ) 2 ) powder, the purity is 99.20wt.%, refining degassing agent and slag removal agent;

[0071] In situ reaction equation: 13Al (l) +3Zr(CO 3 ) 2(s) =3Al 3 Zr (s) +2Al 2 o 3(s) +6CO 2 ↑

[0072] Particle reinforcement phase: Al 3 Zr (s) and Al 2 o 3(s)

[0073] The preparation process is as follows:

[0074] The first step: the reaction salt is preheated and dried, and the metal melt is smelted to the synthesis temperature;

[0075] 1Kg of industrial pure aluminum is melted in a 20kW crucible resistance furnace and heated up to 850°C for degassing and slag removal; all reagents used are fully dried at 250°C, of ​​which Zr(CO 3 ) 2 Grind into fine powder and sieve, the particle size is less than 100μm, weighed for later use, Zr(CO ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Purityaaaaaaaaaa
Login to View More

Abstract

The invention provides a method for synthesizing and preparing a nano-particle reinforced composite through multi-dimension vibration assistance, and belongs to the technical field of material preparation. In the melt reactive synthesis process of the in-situ particle reinforced composite, multi-dimension high-frequency low-amplitude vibration is applied to melt, melt reactive synthesis is promoted, and meanwhile the obvious function effect is achieved on particle dispersion promoting, clustering overcoming and residue-gold separation promoting. The method further has other advantages of beingsimple, free of contact, low in cost, obvious in effect and the like.

Description

technical field [0001] The invention relates to the technical field of preparation of particle-reinforced metal-based composite materials, in particular to a method for preparing nano-particle-reinforced composite materials through multidimensional vibration-assisted synthesis. Background technique [0002] Particle-reinforced metal matrix composites have good mechanical properties and physical and chemical properties due to their composite structural characteristics. One of the research hotspots of metal matrix composites; with the deepening of research, particle reinforced aluminum matrix composites are gradually becoming a new type of material that is more and more widely used; An important method for materials, this method is to form a reinforced particle phase through the in-situ chemical reaction between the reactant and the aluminum matrix by adding reactants to the melt; since the added reactants are basically solid phase, the reactants and aluminum matrix The react...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C1/10C22C1/02C22C32/00C22C21/00
CPCC22C1/1036C22C21/00C22C32/0036C22C1/1052B22F2999/00C22C1/1047C22C1/047B22F2202/01
Inventor 王宏明李桂荣赵玉涛
Owner JIANGSU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com