Modified plastic additive and preparation method thereof

An additive and modification technology, which is applied in the field of modified plastic additives and its preparation, can solve problems such as uneven distribution, unstable and single modified plastics, and achieve improved activity and stability, low cost, and simple preparation methods Effect

Inactive Publication Date: 2018-09-18
ANHUI NINE COWS PLASTIC TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nowadays, the key point of preparing modified plastics is to improve the compatibility of plastic additives. Generally, the actual production is direct additive blending, but this treatment also has the disadvantages of uneven distribution and single selectivity, which will cause the produced Modified plastics are unstable, and this method mainly depends on the functionality and stability of additives. If the composition of additives is stable, a large part of the modification process of modified plastics will be omitted in the case of direct blending. , so as to achieve a good cost reduction effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A modified plastic additive, comprising the following raw materials in parts by weight: 24 parts of thermoplastic elastomer, 8 parts of alumina fiber, 11 parts of magnesium oxide powder, 12 parts of tourmaline powder, 7 parts of titanium dioxide, 4 parts of compounding additives, modification treatment 14 parts of liquid, 3 parts of coupling agent, 3 parts of antioxidant and 7 parts of dispersant.

[0024] A preparation method of a modified plastic additive, comprising the following preparation steps:

[0025] a. Mix alumina fiber, magnesia powder, tourmaline powder and titanium dioxide, import into a pulverizer and pulverize until passing through a 300-mesh sieve, and then perform pretreatment to obtain material 1;

[0026] b. Add material 1 to compounding additives, introduce it into a high mixer, heat at 60°C, and stir at a speed of 300r / min for 15 minutes to obtain material 2;

[0027] c. Add modified treatment liquid and dispersant to material 2, heat up to 95°C, ...

Embodiment 2

[0034] A modified plastic additive, comprising the following raw materials in parts by weight: 19 parts of thermoplastic elastomer, 9 parts of alumina fiber, 7 parts of magnesium oxide powder, 8 parts of tourmaline powder, 8 parts of titanium dioxide, 6 parts of compound additives, modification treatment 9 parts of liquid, 3 parts of coupling agent, 7 parts of antioxidant and 3 parts of dispersant.

[0035] A preparation method of a modified plastic additive, comprising the following preparation steps:

[0036] a. Mix alumina fiber, magnesia powder, tourmaline powder and titanium dioxide, import into a pulverizer and pulverize until passing through a 300-mesh sieve, and then perform pretreatment to obtain material 1;

[0037] b. Add material 1 to compounding additives, introduce it into a high mixer, heat at 60°C, and stir at a speed of 300r / min for 15 minutes to obtain material 2;

[0038] c. Add modified treatment liquid and dispersant to material 2, heat up to 80°C, stir a...

Embodiment 3

[0045] A modified plastic additive, comprising the following raw materials in parts by weight: 22 parts of thermoplastic elastomer, 11 parts of alumina fiber, 10 parts of magnesium oxide powder, 8 parts of tourmaline powder, 12 parts of titanium dioxide, 6 parts of compounding additives, modification treatment 9 parts of liquid, 5 parts of coupling agent, 7 parts of antioxidant and 3 parts of dispersant.

[0046] A preparation method of a modified plastic additive, comprising the following preparation steps:

[0047] a. Mix alumina fiber, magnesia powder, tourmaline powder and titanium dioxide, import into a pulverizer and pulverize until passing through a 300-mesh sieve, and then perform pretreatment to obtain material 1;

[0048] b. Add material 1 to compounding additives, introduce it into a high mixer, heat at 70°C, and stir at a speed of 500r / min for 25min to obtain material 2;

[0049] c. Add modified treatment liquid and dispersant to material 2, heat up to 95°C, and sti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a modified plastic additive and a preparation method thereof. The modified plastic additive is prepared from the following components: a thermoplastic elastomer, alumina fiber,magnesium oxide powder, tourmaline powder, titanium dioxide, a compound auxiliary agent, a modified treatment liquid, a coupling agent, an antioxidant and a dispersant. The additive prepared by usingthe preparation method provided by the invention has good compatibility with main plastic, integrates the effects of increasing toughness and whiteness, resisting bacteria and protecting the environment, and can effectively modify the main plastic to enable the main plastic to obtain the above-mentioned effects; meanwhile, the preparation method provided by the invention is simple, has low cost and is applicable to large-scale industrial production.

Description

technical field [0001] The invention belongs to the technical field of modified plastics, and in particular relates to a modified plastic additive and a preparation method thereof. Background technique [0002] Modified plastics are intermediate products in the petrochemical industry chain. It is a new type of plastic product processed on the basis of general-purpose plastics and engineering plastics through filling, blending, and reinforcement. It is mainly processed from the five major general-purpose plastics and the five major engineering plastics as the plastic matrix, and has the characteristics of flame retardancy, impact resistance, high toughness, and easy processing. The current overall development level of the modified plastics industry is relatively low, and the production scale of enterprises in the industry is generally small. The market conditions of the products also show the characteristics of many primary products, unstable quality of intermediate products,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L101/00C08L79/02C08K13/06C08K9/04C08K7/08C08K3/22C08K3/38
CPCC08K2003/222C08K2003/2241C08K2003/387C08L101/00C08L79/02C08K13/06C08K9/04C08K9/08C08K7/08C08K3/22C08K3/38
Inventor 龚业斌龚业龙
Owner ANHUI NINE COWS PLASTIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap