Composite waterproof coiled material and preparation process thereof
A technology for waterproofing membranes and substrates, applied in fire-resistant coatings, building insulation materials, infrastructure engineering, etc., can solve the problems of easy breakage and damage, poor elasticity and ductility of polypropylene fibers, and weak strain capacity of the base layer of waterproofing membranes. To achieve the effect of strengthening the bond strength, reducing the rheological properties, improving its own strength and thermal stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0021] A composite waterproof roll material, the waterproof roll material is made of a modified polyethylene waterproof base material and a blended fiber cloth; the modified polyethylene waterproof base material includes the following raw materials in parts by weight: chlorosulfonated polyethylene 100 parts, 50 parts of high chlorinated polyethylene, 25 parts of fluorocarbon resin, 10 parts of maleic anhydride grafted EPDM rubber, 0.2 parts of 3-aminopropyl trimethoxysilane, 0.8 parts of di-tert-butyl p-cresol part, 40 parts of filling reinforcing agent; the co-spun fiber cloth is formed by mixing and weaving 60% polym-phenylene isophthalamide fiber and 40% polyethylene terephthalate fiber.
[0022] Wherein, filling reinforcing agent comprises following components by weight:
[0023]
[0024]
[0025] The preparation process of the above-mentioned composite waterproof coiled material is characterized in that it comprises the following steps:
[0026] S1: Mix chlorosulfo...
Embodiment 2
[0030] A composite waterproof roll material, the waterproof roll material is made of a modified polyethylene waterproof base material and a blended fiber cloth; the modified polyethylene waterproof base material includes the following raw materials in parts by weight: chlorosulfonated polyethylene 100 parts, 60 parts of high chlorinated polyethylene, 30 parts of fluorocarbon resin, 15 parts of maleic anhydride grafted EPDM rubber, 0.6 parts of 3-aminopropyltrimethoxysilane, 1.4 parts of phenyl-α-naphthylamine part, 50 parts of filling reinforcing agent; the co-spun fiber cloth is formed by mixing and weaving 65% polym-phenylene isophthalamide fiber and 35% polyethylene terephthalate fiber.
[0031] Wherein, filling reinforcing agent comprises following components by weight:
[0032]
[0033] The preparation process of the above-mentioned composite waterproof coiled material is the same as in Example 1, the difference is that: S1: Chlorosulfonated polyethylene has a chlorine...
Embodiment 3
[0035] A composite waterproof roll material, the waterproof roll material is made of a modified polyethylene waterproof base material and a blended fiber cloth; the modified polyethylene waterproof base material includes the following raw materials in parts by weight: chlorosulfonated polyethylene 100 parts, 70 parts of high chlorinated polyethylene, 35 parts of fluorocarbon resin, 20 parts of maleic anhydride grafted EPDM rubber, 1 part of 3-aminopropyltrimethoxysilane, 2 parts of vulcanized diphenylamine, filling reinforcement 60 parts of agent; the co-spun fiber cloth is formed by mixing and weaving 70% polym-phenylene isophthalamide fibers and 30% polyethylene terephthalate fibers.
[0036] Wherein, filling reinforcing agent comprises following components by weight:
[0037]
[0038]
[0039] The preparation process of the above composite waterproof coiled material is the same as in Example 1, the difference is: S1: Chlorosulfonated polyethylene has a chlorine conten...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap