Bicycle front fork enhanced treatment process

A strengthening treatment, bicycle technology, applied in bicycle accessories, coating, transportation and packaging, etc., can solve problems such as corrosion, easy paint peeling, exposed metal layer, etc.

Active Publication Date: 2018-11-02
上海凤凰自行车江苏有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of people's living standards, bicycles, as a healthy and green means of transportation, have increasingly attracted people's attention, and higher requirements have been put forward for the quality of bicycles. Impacted by the stones brought by the wheels, the outside is exposed to wind and sun for a long time, and the paint is prone to peeling off, which exposes the metal layer of the seat post and causes corrosion, which affects driving safety

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A process for strengthening the front fork of a bicycle, comprising the following steps:

[0024] S1. Sandblasting, blasting the outer surface of the front fork to make the surface roughness of the front fork reach Ra25;

[0025] S2, heat strengthening, heating the front fork after surface treatment at 1300 ℃;

[0026] S3, annealing, annealing the front fork, annealing is divided into three stages, the temperature of the first stage is 900 ℃, under nitrogen protection, the temperature of the second stage is 800 ℃, under nitrogen protection, the temperature of the third stage is 500 ℃, cooled in air;

[0027] S4, sol, smear the front fork surface with acrylic resin hot-melt adhesive, so that a layer of acrylic resin adhesive is formed on the front fork surface;

[0028] S5, bonding, heating the front fork to the hot-melting state of the adhesive, and bonding thermoplastic polyurethane elastic particles with a diameter of 2 mm on the outside of the adhesive;

[0029] S...

Embodiment 2

[0035] A process for strengthening the front fork of a bicycle, comprising the following steps:

[0036] S1. Sandblasting, blasting the outer surface of the front fork to make the surface roughness of the front fork reach Ra25;

[0037] S2, heat strengthening, heating the front fork after surface treatment at 1200 ℃;

[0038] S3, annealing, annealing the front fork, annealing is divided into three stages, the temperature of the first stage is 850 ℃, under nitrogen protection, the temperature of the second stage is 600 ℃, under nitrogen protection, the temperature of the third stage is 400 ℃, cooled in air;

[0039] S4, sol, smear the front fork surface with acrylic resin hot-melt adhesive, so that a layer of acrylic resin adhesive is formed on the front fork surface;

[0040] S5, bonding, heating the front fork to the hot-melting state of the adhesive, and bonding thermoplastic polyurethane elastic particles with a diameter of 2 mm on the outside of the adhesive;

[0041] S...

Embodiment 3

[0047] A process for strengthening the front fork of a bicycle, comprising the following steps:

[0048] S1. Sandblasting, blasting the outer surface of the front fork to make the surface roughness of the front fork reach Ra25;

[0049] S2, heat strengthening, heating the front fork after surface treatment at 1000 ℃;

[0050] S3, annealing, annealing the front fork, annealing is divided into three stages, the temperature of the first stage is 800 ℃, under nitrogen protection, the temperature of the second stage is 500 ℃, under nitrogen protection, the temperature of the third stage is 300 ℃, cooled in air;

[0051] S4, sol, smear the front fork surface with acrylic resin hot-melt adhesive, so that a layer of acrylic resin adhesive is formed on the front fork surface;

[0052] S5, bonding, heating the front fork to the hot-melting state of the adhesive, and bonding thermoplastic polyurethane elastic particles with a diameter of 2 mm on the outside of the adhesive;

[0053] S...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a bicycle front fork enhanced treatment process which includes the steps of sand blasting, heat strengthening, annealing, sol, bonding, cutting, surface filming. The structural strength of a treated bicycle front fork is higher, and the outer surface has a certain buffering capacity, which can reduce an external impact force and abandons a traditional painting process.

Description

technical field [0001] The invention relates to a surface treatment technology for metal materials, in particular to a surface strengthening treatment technology for a bicycle front fork. Background technique [0002] With the improvement of people's living standards, bicycles, as a healthy and green means of transportation, are increasingly attracting people's attention, and higher requirements are also put forward for the quality of bicycles. As an exposed component, the side of the front fork close to the wheel often Affected by the stones brought up by the wheels, and the outside is exposed to the wind and the sun for a long time, the paint is prone to peel off, and the metal layer of the seat post is exposed and corroded, which affects the driving safety. SUMMARY OF THE INVENTION [0003] In order to solve the above technical problems, the purpose of the present invention is to provide a process for strengthening the front fork of a bicycle. [0004] The technical sc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B62K21/02B24C1/00B05D7/14B29C63/02
CPCB05D7/14B05D2502/00B24C1/00B29C63/02B62K21/02
Inventor 曹中明鲍洪李发军陶启乾赵虎段道兵
Owner 上海凤凰自行车江苏有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products