Preparation method of noctilcent cement and noctilcent pavement

A preparation method and cement technology, applied in the field of cement, can solve the problems of easily damaged tires, traffic accidents, single function, low interest, etc., and achieve the advantages of increasing heat storage capacity and heat diffusion capacity, enhancing interest, and improving driving safety factor. Effect

Inactive Publication Date: 2018-11-06
湖南三恒建设园林工程有限公司
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies of the prior art, the present invention provides a preparation method of luminous cement and luminous pavement, which solves the problem that the existing cement pavement has single function and low interest, and at the same time, the temperature of the road surface is high after long-term exposure to the sun, which is easy to damage the tires Problems that cause traffic accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A preparation method of luminous cement, comprising the following steps,

[0031] (1) Raw materials are pulverized, and a certain amount of limestone, clay, gypsum, coal, iron ore and pure quartz sand are weighed in proportion, and then poured into the pulverizer for pulverization respectively, and coarsely filtered with a filter screen;

[0032] (2) Mixing of raw materials, mixing the pulverized raw materials, and then adding volcanic ash, dye and luminous powder into the mixture;

[0033] (3) Firing, pour the mixed raw materials into the rotary road for firing, take out the cement after firing and cool to normal temperature;

[0034] (4) Cement grinding, pour the cooled cement into a pulverizer to pulverize, and use a filter to filter.

[0035] A luminous cement is made of the following components in parts by weight: 60 parts by weight of limestone, 8 parts by weight of clay, 2 parts by weight of gypsum, 10 parts by weight of coal, 2 parts by weight of luminous powde...

Embodiment 2

[0048] A preparation method of luminous cement, comprising the following steps,

[0049] (1) Raw materials are pulverized, and a certain amount of limestone, clay, gypsum, coal, iron ore and pure quartz sand are weighed in proportion, and then poured into the pulverizer for pulverization respectively, and coarsely filtered with a filter screen;

[0050] (2) Mixing of raw materials, mixing the pulverized raw materials, and then adding volcanic ash, dye and luminous powder into the mixture;

[0051] (3) Firing, pour the mixed raw materials into the rotary road for firing, take out the cement after firing and cool to normal temperature;

[0052] (4) Cement grinding, pour the cooled cement into a pulverizer to pulverize, and use a filter to filter.

[0053] A luminous cement, made of the following components in parts by weight: 70 parts by weight of limestone, 9 parts by weight of clay, 4 parts by weight of gypsum, 12 parts by weight of coal, 5 parts by weight of luminous powder,...

Embodiment 3

[0066] A preparation method of luminous cement, comprising the following steps,

[0067] (1) Raw materials are pulverized, and a certain amount of limestone, clay, gypsum, coal, iron ore and pure quartz sand are weighed in proportion, and then poured into the pulverizer for pulverization respectively, and coarsely filtered with a filter screen;

[0068] (2) Mixing of raw materials, mixing the pulverized raw materials, and then adding volcanic ash, dye and luminous powder into the mixture;

[0069] (3) Firing, pour the mixed raw materials into the rotary road for firing, take out the cement after firing and cool to normal temperature;

[0070] (4) Cement grinding, pour the cooled cement into a pulverizer to pulverize, and use a filter to filter.

[0071] A luminous cement, which is made of the following components in parts by weight: 80 parts by weight of limestone, 10 parts by weight of clay, 6 parts by weight of gypsum, 14 parts by weight of coal, 8 parts by weight of luminous...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of noctilcent cement and a noctilcent pavement and relates to the technical field of cement. The preparation method comprises steps as follows: raw materialcrushing, raw material mixing, firing, cement grinding, roadbed laying, cement laying, coating preparation and coating laying. The noctilcent cement is prepared from components in parts by weight asfollows: 60-80 parts of limestone, 8-10 parts of clay, 2-6 parts of gypsum, 10-14 parts of coal, 2-8 parts of noctilcent powder, 4-8 parts of volcanic ash, 1-5 parts of iron ore, 10-20 parts of dyes and 6-10 parts of pure quartz sand. According to the preparation method of the noctilcent cement and a laying method of the noctilcent pavement, the pavement has noctilcent capacity, functions of the cement pavement are increased, interestingness of the pavement is improved, heat storage capacity and thermal diffusion capacity of the pavement are improved, so that the temperature of the pavement isnot easily increased after the pavement is exposed to the sun for a long time, tires are prevented from being damaged by high temperature of the pavement, and safety coefficient of driving on the pavement is increased.

Description

technical field [0001] The invention relates to the technical field of cement, in particular to a preparation method of luminous cement and a luminous pavement. Background technique [0002] Cement is a powdery hydraulic inorganic gelling material. It can be mixed with water to form a slurry. It can be hardened in air or better hardened in water, and can firmly bind sand, stone and other materials together. The existing cement pavement can provide good traffic capacity, but the function is single and the interest is low. At the same time, the temperature of the pavement is high after long-term exposure to the sun, which is easy to damage the tires and cause traffic accidents. Contents of the invention [0003] (1) Solved technical problems [0004] Aiming at the deficiencies of the prior art, the present invention provides a preparation method of luminous cement and luminous pavement, which solves the problem that the existing cement pavement has single function and low i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B7/22C04B7/36C04B28/02C04B41/65E01C7/14C04B111/80
CPCE01C7/142C04B7/22C04B7/36C04B28/02C04B41/009C04B41/5035C04B41/65C04B2111/807C04B2111/0075C04B41/4535C04B41/5001C04B41/50
Inventor 卜方明
Owner 湖南三恒建设园林工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com