Process for engraving metal on ceramic

A ceramic and metal technology, applied in the field of ceramic process preparation, can solve the problems of lack of perfection, easy to fall off, easy to breed bacteria, etc., to achieve the effect of improving appearance and broad application prospects

Inactive Publication Date: 2018-11-23
杨志强
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, although there are many kinds of craft ceramics on the market, there has never been a perfect solution for the combination of metal and ceramics. Previously, inlays or low-temperature imitation glazes have been used for combination, but both have technical and practical advantages. For example, the workpieces combined by the mosaic process have the disadvantages of not being strong and easy to loosen, and the bonding layer is prone to water accumulation, which may cause bacteria to breed
Although the low-temperature imitation glaze has strong sealing performance, because the characteristics of the low-temperature imitation glaze are similar to glue, and its joint is small, it is easy to fall off when it is worn or used normally. Therefore, the existing technologies have defects in varying degrees. The main reason why this type of product cannot be mass-produced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for engraving metal on ceramic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0018] Embodiment: The technical process of engraving metal on a ceramic pot is: Step 1. Make ceramic slurry, mix the formula of ceramic slurry with dragon rock soil, mother-child joint, bone powder, quartz, feldspar, clay and water and then grind it. After completion, remove iron and sieve to make ceramic slurry; the ceramic slurry in the step 1 contains the following mass fraction raw materials: Longyan soil 30%, mother and child joint 5%, bone meal 45%, quartz 5%, feldspar 5% %, clay 10%;

[0019] Step 2, making the ceramic glaze, mixing the main solvent, co-solvent, suspending agent and filler of the ceramic glaze according to the mass percentage before use;

[0020] Step 3: Make ceramic pot blanks, press the mud into the required pot shape with a pressure grouting machine to form the mud blank, wait for the mud blank to dry and form holes in the dry blank according to the attachment point of the silver ornaments, because the mud blank has a certain Shrinkage, so it is ne...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a process for engraving metal on ceramic, and in particular relates to the technical field of ceramic preparation. The process comprises the specific flow as follows: preparingceramic slurry; preparing ceramic glaze, and mixing a main solvent, a cosolvent, a suspending agent and a filler in percentage by mass according to the formula of the ceramic glaze for later use; preparing ceramic blank, firing to obtain a biscuit, firing to obtain ceramic whiteware, and painting for decoration. The process combines metal and ceramic and has greatly broad application prospects, and artware produced with the process is beautiful and elegant as well as solid and durable, and not only retains the beauty of ceramics, but also incorporates the unique texture of metal, so that theattractiveness of the product is greatly improved.

Description

technical field [0001] The invention relates to a process for engraving metal on ceramics, and specifically belongs to the technical field of ceramic process preparation. Background technique [0002] The Chinese invented pottery as early as the Neolithic Age. The utensils fired with clay are called pottery, and the utensils fired with china clay are called porcelain. Porcelain is the general term for pottery, stoneware and porcelain. Any utensils made of two different types of clay, pottery clay and porcelain clay, as raw materials, through batching, molding, drying, roasting and other processes can be called ceramics. [0003] At present, although there are many kinds of craft ceramics on the market, there has never been a perfect solution for the combination of metal and ceramics. Previously, inlays or low-temperature imitation glazes have been used for combination, but both have technical and practical advantages. For example, the workpieces combined by the mosaic pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/132C04B33/13C04B33/24C04B41/90C04B37/02B44C1/20B44C5/00
CPCB44C1/20B44C5/00C04B33/13C04B33/132C04B33/24C04B37/023C04B41/52C04B41/90C04B2235/3418C04B2235/3472C04B2235/3481C04B2235/602C04B2235/612C04B2235/656C04B2237/10C04B41/5022C04B41/4543C04B41/5116C04B41/4572Y02P40/60
Inventor 杨志强
Owner 杨志强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com