Non-ironing treatment method for chemical fiber fabric

A treatment method and fabric technology, which is applied in the treatment of textile materials, fiber treatment, spray/jet textile material treatment, etc., can solve the problems of troublesome, wrinkled chemical fiber fabrics, etc., to increase air permeability, protect the properties of chemical fiber fabrics, and cover Comprehensive and effective

Inactive Publication Date: 2018-11-23
ANHUI HENGYI TEXTILE TECH CO LTD
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Chemical fiber fabrics have many wrinkles after cleaning, and they need to be ironed to be flat, so that they can be worn beautifully, but they need to be ironed every time they are cleaned, which is very troublesome. Therefore, if you can keep the clothes in their original shape and reduce ironing, is an urgent problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-ironing treatment method for chemical fiber fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A non-ironing treatment method for chemical fiber fabrics, comprising the following steps:

[0028] (1) Immerse the chemical fiber fabric in 50°C water for 20 minutes, then quickly put it in 4°C cold water to cool, hang it to dry after cooling until there is no water dripping;

[0029] (2) spread the chemical fiber fabric after step (1) on the flat work surface, flatten it with a flat plate, and then hang it up;

[0030] (3) Add the non-ironing treatment agent to 30-40 times of water and mix evenly, atomize and spray on the erected chemical fiber fabric with an atomizer, and the consumption of the non-ironing treatment agent is 15% of the weight of the chemical fiber fabric;

[0031] (4) Bake the chemical fiber fabric sprayed with the non-ironing treatment agent at 120° C. for 10 minutes with a baking machine;

[0032] (5) Put the baked pure cotton products into steam at 130°C and 0.27Mpa saturated vapor pressure for 40 minutes, spread them on a flat work surface after...

Embodiment 2

[0035] A non-ironing treatment method for chemical fiber fabrics, comprising the following steps:

[0036] (1) Immerse the chemical fiber fabric in 70°C water for 30 minutes, quickly put it in 6°C cold water to cool, hang it to dry after cooling until there is no water dripping;

[0037] (2) spread the chemical fiber fabric after step (1) on the flat work surface, flatten it with a flat plate, and then hang it up;

[0038] (3) Add the non-ironing treatment agent to 40 times of water and mix evenly, atomize and spray on the erected chemical fiber fabric with an atomizer, and the consumption of the non-ironing treatment agent is 30% of the weight of the chemical fiber fabric;

[0039] (4) Bake the chemical fiber fabric sprayed with the non-ironing treatment agent at 150° C. for 12 minutes with a baking machine;

[0040] (5) Put the baked pure cotton products into steam at 130°C and 0.27Mpa saturated vapor pressure for 60 minutes, spread them on a flat work surface after cooling...

Embodiment 3

[0046] A non-ironing treatment method for chemical fiber fabrics, comprising the following steps:

[0047] (1) Immerse the chemical fiber fabric in water at 60°C for 25 minutes, then quickly put it in cold water at 5°C to cool, and hang it to dry after cooling until there is no water dripping;

[0048] (2) spread the chemical fiber fabric after step (1) on the flat work surface, flatten it with a flat plate, and then hang it up;

[0049](3) Add the non-ironing treatment agent to 35 times of water and mix evenly, atomize and spray on the erected chemical fiber fabric with an atomizer, and the consumption of the non-ironing treatment agent is 20% of the weight of the chemical fiber fabric;

[0050] (4) Bake the chemical fiber fabric sprayed with the non-ironing treatment agent at 130° C. for 11 minutes with a baking machine;

[0051] (5) Put the baked pure cotton products into steam at 130°C and 0.27Mpa saturated vapor pressure for 50 minutes, spread them on a flat work surface...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a non-ironing treatment method for chemical fiber fabrics, which relates to the technical field of the processing of the chemical fiber fabrics. The non-ironing treatment method comprises the following steps: (1) wetting the chemical fiber fabric by using water until the chemical fiber fabric is in a non-dripping state, laying the chemical fiber fabric on a smooth working table-board, flattening the chemical fiber fabric by using a flat plate, then suspending and erecting the chemical fiber fabric; (2) uniformly mixing a non-ironing treatment agent in 30 to 40 times ofwater, and atomizing and spraying the non-ironing treatment agent on the erected chemical fiber fabric by using an atomizer; (3) baking the chemical fiber fabric with the non-ironing treatment agent by using a baking machine; and (4) soaking and steaming the baken chemical fiber fabric under the saturated steam of 130 DEG C and 0.27Mpa, cooling, laying on a flat working table-board, and heating and drying by virtue of the radiation of high infrared rays; and performing the non-ironing treatment for a special treatment agent, processing the chemical fiber fabric to form clothing, cleaning the clothing to keep the shape, so that the ironing can be reduced; and gas permeability, strength and hardness of the chemical fiber fabric can be maintained, and the wearing comfort degree can be reduced.

Description

Technical field: [0001] The invention relates to the technical field of chemical fiber fabric processing, in particular to a non-ironing treatment method for chemical fiber fabrics. Background technique: [0002] Chemical fibers are fibers with textile properties that are made from natural polymer compounds or artificially synthesized polymer compounds through the processes of preparing spinning dope, spinning and post-treatment. With the further transfer of global fiber production to China, China has become the world's largest producer of chemical fiber. China's chemical fiber production accounts for more than 60% of the global total. my country's chemical fiber industry has continued to develop rapidly, and its comprehensive competitiveness has improved significantly. It has fully completed the planned objectives and tasks, strongly promoted and supported the development of the textile industry and related industries, and further enhanced its status and role in the world'...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/572D06M15/55D06M15/59D06M11/54D06M11/76D06M13/203D06M13/224D06M13/402D06M13/262D06B1/02D06B3/10D06B15/00D06B19/00D06C15/10
CPCD06B1/02D06B3/10D06B15/00D06B19/0029D06C15/10D06M11/54D06M11/76D06M13/203D06M13/224D06M13/262D06M13/402D06M15/55D06M15/572D06M15/59
Inventor 李贺
Owner ANHUI HENGYI TEXTILE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com