Production method of anti-wrinkle wear-resistant suits
A production method and a wrinkle and wear-resistant technology, which are applied in the field of suit making, can solve the problems of creases on the surface and affect the appearance of clothes, and achieve the effects of preventing yellowing, improving anti-wrinkle performance and simple operation.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0029] The invention provides the following technical solution: a method for producing anti-wrinkle and wear-resistant suits, comprising the following steps:
[0030] A. Making suit fabrics and pre-processing;
[0031] B, dyeing the suit fabric after the pre-treatment;
[0032] C. Add the dyed fabric to the loom and process it into gray fabric;
[0033] D. Heat the gray cloth into the softener in a water bath;
[0034] E. Afterwards, the treated gray cloth is cleaned and dried;
[0035] F, finally the dried gray cloth is made into a suit.
[0036] In the present embodiment, the suit fabric making method in step A is as follows:
[0037] a. The wool fiber is treated with low-pressure plasma;
[0038] B, blending processed wool fiber, cotton fiber and pearl fiber to prepare surface layer fabric;
[0039] c. Coating anti-wrinkle hot-melt adhesive on the surface of the surface layer fabric, the components and parts by weight of the anti-wrinkle hot-melt adhesive are 10 parts...
Embodiment 2
[0048] A method for producing an anti-wrinkle and wear-resistant suit, comprising the following steps:
[0049] A. Making suit fabrics and pre-processing;
[0050] B, dyeing the suit fabric after the pre-treatment;
[0051] C. Add the dyed fabric to the loom and process it into gray fabric;
[0052] D. Heat the gray cloth into the softener in a water bath;
[0053] E. Afterwards, the treated gray cloth is cleaned and dried;
[0054] F, finally the dried gray cloth is made into a suit.
[0055] In the present embodiment, the suit fabric making method in step A is as follows:
[0056] a. The wool fiber is treated with low-pressure plasma;
[0057] B, blending processed wool fiber, cotton fiber and pearl fiber to prepare surface layer fabric;
[0058] c. Coating anti-wrinkle hot-melt adhesive on the surface of the surface layer fabric, the components and parts by weight of the anti-wrinkle hot-melt adhesive are 20 parts of polytetramethylene ether glycol, 16 parts of polyvi...
Embodiment 3
[0067] A method for producing an anti-wrinkle and wear-resistant suit, comprising the following steps:
[0068] A. Making suit fabrics and pre-processing;
[0069] B, dyeing the suit fabric after the pre-treatment;
[0070] C. Add the dyed fabric to the loom and process it into gray fabric;
[0071] D. Heat the gray cloth into the softener in a water bath;
[0072] E. Afterwards, the treated gray cloth is cleaned and dried;
[0073] F, finally the dried gray cloth is made into a suit.
[0074] In the present embodiment, the suit fabric making method in step A is as follows:
[0075] a. The wool fiber is treated with low-pressure plasma;
[0076] B, blending processed wool fiber, cotton fiber and pearl fiber to prepare surface layer fabric;
[0077] c. Coating anti-wrinkle hot-melt adhesive on the surface of the surface layer fabric, the components and parts by weight of the anti-wrinkle hot-melt adhesive are 12 parts of polytetramethylene ether glycol, 10 parts of polyvi...