Fabrication method of black-white elastic napped twill printed fabrics

A production method and elastic technology, applied in the direction of fabric surface trimming, weaving, fabrics, etc., can solve the problem of difficult to meet the natural needs of partial comfort, and achieve the effects of natural and comfortable visual effect, outstanding color fastness, and suitable physical properties.

Inactive Publication Date: 2018-12-18
劲霸男装(上海)有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the appearance of this metallic luster is also easy to meet the needs of users who prefer comfort and natural needs due to high coldness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A method for making black and white elastic napped twill printed fabrics, after weaving black and white elastic twill fabrics with yarns composed of black silk and white silk, the black and white elastic twill fabrics are then unrolled, washed with alkali, raised, shaped, napped and printed. to get the finished product.

[0022] In this embodiment, the composite ratio of black silk and white silk in the yarn is 1:1.2. Among the yarns used, the warp yarn is T-75D black silk + T-75D white silk ATY SD, and the weft yarn is T-75D white silk ATY SD. -75D black silk + T-75D white silk ATY SD + 40D spandex machine bag, so that the product shows a good sense of color and layering.

[0023] The specific process of alkali reduction cleaning is as follows:

[0024] At 125°C, take caustic soda accounting for 14% of the weight of the black and white elastic twill gray fabric to be treated, and carry out weight reduction treatment according to the bath ratio of 1:8.

[0025] The sp...

Embodiment 2

[0039] A method for making black and white elastic napped twill printed fabrics, after weaving black and white elastic twill fabrics with yarns composed of black silk and white silk, the black and white elastic twill fabrics are then unrolled, washed with alkali, raised, shaped, napped and printed. to get the finished product.

[0040] In this embodiment, the composite ratio of black silk and white silk in the yarn is 1:1.1. Among the yarns used, the warp yarn is T-75D black silk + T-75D white silk ATY SD, and the weft yarn is T-75D white silk ATY SD. -75D black silk + T-75D white silk ATY SD + 40D spandex machine bag, so that the product shows a good sense of color and layering.

[0041] The specific process of alkali reduction cleaning is as follows:

[0042] At 125°C, take caustic soda accounting for 13% of the weight of the black and white elastic twill gray fabric to be treated, and carry out weight reduction treatment according to the bath ratio of 1:8.

[0043] The sp...

Embodiment 3

[0049] A method for making black and white elastic napped twill printed fabrics, after weaving black and white elastic twill fabrics with yarns composed of black silk and white silk, the black and white elastic twill fabrics are then unrolled, washed with alkali, raised, shaped, napped and printed. to get the finished product.

[0050]In this embodiment, the composite ratio of black silk and white silk in the yarn is 1:1.3. Among the yarns used, the warp is T-75D black silk+T-75D white silk ATY SD, and the weft is T-75D white silk. -75D black silk + T-75D white silk ATY SD + 40D spandex machine bag, so that the product shows a good sense of color and layering.

[0051] The specific process of alkali reduction cleaning is as follows:

[0052] At 125°C, take caustic soda accounting for 15% of the weight of the black and white elastic twill gray fabric to be treated, and carry out weight reduction treatment according to the bath ratio of 1:8.

[0053] The specific process of fl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a fabrication method of black-white elastic napped twill printed fabrics. Yarns formed by black silk and white silk are weaved to obtain black-white elastic twill grey fabrics, and then a finished product can be obtained through unwinding, alkali decrement cleaning, fuzzing, fixing, napping, and printing. Compared with the prior art, according to the fabrics, enough fine broken filaments with suitable length can be obtained, the hand feel of the fabrics is soft and woolen, and the visual effect is natural and comfortable.

Description

technical field [0001] The invention belongs to the technical field of preparation of functional fabrics, and relates to a method for producing black and white elastic brushed twill printed fabrics. Background technique [0002] The outer fabrics of the company's existing men's clothing such as Nikes, cotton clothes, and jackets are generally made of metallic luster fabrics to highlight the luxury of leather. However, the appearance of this metallic luster is also easy to satisfy users who prefer comfort and natural needs due to high coldness. Contents of the invention [0003] The object of the present invention is to provide a method for making black and white elastic brushed twill printed fabrics in order to overcome the above-mentioned defects in the prior art. It is mainly made of polyester 75D black and white composite air-varying fibers and then coated with 40D spandex and interwoven with herringbone diagonal weave. Fabric, after desizing, fluffing, shaping and bru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/08D03D15/00D06C11/00D06C7/02D03D15/56D03D15/283D03D15/54
CPCD06C7/02D06C11/00D10B2331/04D10B2331/10D03D15/54D03D15/56
Inventor 樊剑斌
Owner 劲霸男装(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap