Method and application of partial plasma spraying nicraly coating on inner wall of aluminum alloy casing with boss

A local plasma, aluminum alloy technology, applied in the direction of metal material coating process, coating, melting spray plating, etc., can solve the problem of increasing the difficulty of qualified coating, achieve high coating processing yield, meet the operation requirements, good quality The effect of antioxidant properties

Active Publication Date: 2021-03-02
GUANGDONG INST OF NEW MATERIALS
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As the thickness of the coating increases, its internal residual stress is more likely to concentrate, and the difficulty of preparing a qualified coating is virtually increased

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method and application of partial plasma spraying nicraly coating on inner wall of aluminum alloy casing with boss
  • Method and application of partial plasma spraying nicraly coating on inner wall of aluminum alloy casing with boss
  • Method and application of partial plasma spraying nicraly coating on inner wall of aluminum alloy casing with boss

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The present embodiment provides a kind of method for the local plasma spraying NiCrAlY coating on the inner wall of the aluminum alloy casing with the boss, including:

[0032] Step 1: Remove dust and oil from the casing surface.

[0033] Step 2: Protect the non-painted parts of the casing with special metal protection tooling, and measure the original inner diameter of the area to be sprayed.

[0034] Step 3: Sand blast the area to be sprayed with 24# zirconium corundum. The sand blasting pressure is 0.35MPa, the sand blasting distance is 130mm, and the sand blasting angle is 40°. After the sand blasting is completed, use compressed air to blow off any remaining sand or dust.

[0035] Step 4: Put the sanded casing into the jig and fix it horizontally on the turntable. Install, adjust and fix the position of the cooling air duct. Use 2 air ducts, one for cooling the area to be sprayed on the inner wall of the casing, and the other for cooling the outer wall of the casi...

Embodiment 2

[0038] The present embodiment provides a kind of method for the local plasma spraying NiCrAlY coating on the inner wall of the aluminum alloy casing with the boss, including:

[0039] Step 1: Remove dust and oil from the casing surface.

[0040] Step 2: Protect the non-painted parts of the casing with special metal protection tooling, and measure the original inner diameter of the area to be sprayed.

[0041] Step 3: Sand blast the area to be sprayed with 24# zirconium corundum. The sand blasting pressure is 0.20MPa, the sand blasting distance is 100mm, and the sand blasting angle is 35°. After the sand blasting is completed, use compressed air to blow off any remaining sand or dust.

[0042]Step 4: Put the sanded casing into the jig and fix it horizontally on the turntable. Install, adjust and fix the position of the cooling air duct. Use 2 air ducts, one for cooling the area to be sprayed on the inner wall of the casing, and the other for cooling the outer wall of the casin...

Embodiment 3

[0045] The present embodiment provides a kind of method for the local plasma spraying NiCrAlY coating on the inner wall of the aluminum alloy casing with the boss, comprising:

[0046] Step 1: Remove dust and oil from the casing surface.

[0047] Step 2: Protect the non-painted parts of the casing with special metal protection tooling, and measure the original inner diameter of the area to be sprayed.

[0048] Step 3: Sand blast the area to be sprayed with 24# zirconium corundum. The sand blasting pressure is 0.30MPa, the sand blasting distance is 150mm, and the sand blasting angle is 60°. After the sand blasting is completed, use compressed air to blow off any remaining sand or dust.

[0049] Step 4: Put the sanded casing into the jig and fix it horizontally on the turntable. Install, adjust and fix the position of the cooling air duct. Use 2 air ducts, one for cooling the area to be sprayed on the inner wall of the casing, and the other for cooling the outer wall of the cas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method and application of a partial plasma spraying NiCrAlY coating on the inner wall of an aluminum alloy casing with a boss, and belongs to the technical field of material surface treatment. A method for locally plasma-spraying NiCrAlY coating on the inner wall of an aluminum alloy casing with a boss, comprising: carrying out dust and oil removal treatment on the casing, then protecting the non-sprayed area, and performing roughening treatment on the surface of the area to be sprayed. The casing is put into the fixture and fixed on the turntable, and the area to be sprayed is sprayed with NiCrAlY coating. During the spraying process, stop spraying when the temperature of the area to be sprayed exceeds 150°C, and continue spraying when the temperature drops below 100°C, and repeat until the thickness meets the requirements. This method ensures the temperature control of the spraying process and effectively controls the degree of deformation of the casing. The coated casing prepared by the invention is assembled on an aero-engine to achieve the index of stable operation, so the application prospect is broad.

Description

technical field [0001] The invention relates to the technical field of material surface treatment, and in particular to a method and application of a partial plasma spraying NiCrAlY coating on the inner wall of an aluminum alloy casing with a boss. Background technique [0002] The power, thrust and efficiency of an engine are directly related to the tightness between the rotating and stationary parts of the engine. The casing is an important fixed part in the engine, and the inside of the casing shell is usually prepared with protective coatings with properties such as wear resistance, erosion resistance, oxidation resistance and sealing. The casing parts usually have the characteristics of thin wall thickness and poor rigidity, and are prone to deformation and residual stress during the coating preparation process by thermal spraying. Especially for the aluminum alloy case with a large thermal expansion system, a boss on the inner wall, and only a part of the area below t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C4/073C23C4/134C23C4/02
CPCC23C4/02C23C4/073C23C4/134
Inventor 徐丽萍邓春明牛少鹏陈龙飞宋进兵邓畅光刘敏周克崧
Owner GUANGDONG INST OF NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com