Hot metal desulfurization method and desulfurization device

A desulfurization device, molten iron technology, applied in the manufacture of converters, etc., can solve the problem of low desulfurization rate, achieve the effect of improving the desulfurization rate and preventing the rise of equipment costs

Active Publication Date: 2021-01-05
NIPPON STEEL CORP
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is difficult for the desulfurizer to get involved in the molten steel, so the desulfurization rate is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot metal desulfurization method and desulfurization device
  • Hot metal desulfurization method and desulfurization device
  • Hot metal desulfurization method and desulfurization device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0054] use figure 1 The shown desulfurization device 0 of the present invention and the desulfurization device of the conventional example in which the blowing device 6 is removed from the desulfurization device 0 were obtained, and the desulfurization rate was obtained. That is, when tapping the molten steel 7 that has been blown by the converter 1 (primary refining) by conventional means, a desulfurizer is added, and the desulfurization rate is obtained from [S] before and after tapping.

[0055] The size of the tapping hole 13 of the converter 1 is 250 mm. The desulfurizing agent 7 was added by blowing the desulfurizing agent 7 toward the tapping stream 11 using the blowing device 0 . The nozzle diameter of the blowing nozzle 3 was 200 mm. Ar gas was used as the carrier gas of the desulfurizing agent 7 .

[0056] In the desulfurization device 0, the blowing nozzle 3 of the desulfurizing agent 7 is fixed and fixed by appropriate means such as welding and fastening in suc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a technology for desulfurization at a higher desulfurization rate during tapping of a converter. Using the blowing equipment (6), blowing the desulfurizer (7) from the blowing nozzle (3) to the tapping flow (11) when tapping from the refining vessel (1) to the ladle (2), the blowing equipment (6) includes : the blowing nozzle (3), which is located at the input chute (8); the container (hopper) (4), which stores the desulfurizer; and the piping (5), which connects the blowing nozzle (3) and the container (hopper) (4) )connect.

Description

technical field [0001] The invention relates to a desulfurization method and a desulfurization device for molten iron. Background technique [0002] In the past, when smelting low-sulfur steel such as [S]≤24ppm, in order to reduce the desulfurization load in the secondary refining, when the steel is tapped from the converter to the ladle, the desulfurizer and the deoxidizer are simultaneously injected from the slip The tank is poured into the ladle for desulfurization. However, it is difficult for the desulfurizer to get involved in the molten steel, so the desulfurization rate is low. [0003] Patent Document 1 discloses a method of desulfurizing by adding a deoxidizing agent, a desulfurizing agent, and a slag modifier to molten steel during tapping. In this method, the desulfurizing agent and the molten steel are stirred by using the stirring energy of the tapping flow during the tapping of the converter to make the desulfurizing agent and the molten steel react. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline