Stainless steel wiredrawing technology

A kind of stainless steel and process technology, applied in special surfaces, pretreatment surfaces, devices for coating liquids on surfaces, etc., can solve problems such as pollution, increase processing time, inconvenience in production, etc., to reduce pollution, reduce impurities, and improve work. The effect of efficiency

Inactive Publication Date: 2019-01-04
青岛河钢复合新材料科技有限公司 +2
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, this preparation method needs to be baked and cooled during wire drawing. During baking, the paint solvent will be evaporated, causing pollution; in addition, cooling is required after baking, which increases the processing time and is not convenient for production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1: a kind of stainless steel wire drawing process, comprises the following steps:

[0029] Stainless steel metal plate unwinding: place the coiled stainless steel plate on the uncoiler for unwinding, the thickness of the stainless steel metal plate is 0.2mm, and the line speed of unwinding is 1m / min.

[0030] Coating light-curing paint on the front of the stainless steel metal plate: use light-curing paint to coat the front of the stainless steel metal plate, so that the light-curing paint is evenly coated on the stainless steel metal plate, and the light-curing paint includes acrylic resin.

[0031] The membrane material is attached to the front of the stainless steel metal plate: after the light-curing paint is coated on the stainless steel metal plate, the membrane material is covered on one side of the stainless steel metal plate coated with the light-curing paint, and the side of the membrane material close to the stainless steel metal plate is provided w...

Embodiment 2

[0035] Embodiment 2: a kind of stainless steel wire drawing process, comprises the following steps:

[0036] Stainless steel metal plate unwinding: place the coiled stainless steel plate on the uncoiler for unwinding, the thickness of the stainless steel metal plate is 0.5mm, and the line speed of unwinding is 10m / min.

[0037] Degreasing the surface of the stainless steel metal plate: first degrease the surface of the stainless steel metal plate roughly, and use alkaline treatment solution to remove the anti-rust oil on the stainless steel metal plate; then perform fine degreasing on the surface of the stainless steel metal plate, and use pure water to remove the residual alkaline treatment solution ; The stainless steel metal plate after the degreasing treatment is cleaned with pure water, and the cleaned stainless steel metal plate is air-dried.

[0038] Coating light-curing paint on the front of the stainless steel metal plate: use light-curing paint to coat the front of t...

Embodiment 3

[0043] Embodiment 3: a kind of stainless steel wire drawing process, comprises the following steps:

[0044] Stainless steel metal plate unwinding: place the coiled stainless steel plate on the uncoiler for unwinding, the thickness of the stainless steel metal plate is 0.5mm, and the line speed of unwinding is 10m / min.

[0045] Degreasing the surface of the stainless steel metal plate: first degrease the surface of the stainless steel metal plate roughly, and use alkaline treatment solution to remove the anti-rust oil on the stainless steel metal plate; then perform fine degreasing on the surface of the stainless steel metal plate, and use pure water to remove the residual alkaline treatment solution ; The stainless steel metal plate after the degreasing treatment is cleaned with pure water, and the cleaned stainless steel metal plate is air-dried.

[0046] Passivation of the front side of the stainless steel metal plate: passivate the front side of the stainless steel metal p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a stainless steel wiredrawing technology, and relates to the field of stainless steel production. The stainless steel wiredrawing technology comprises the following steps that1, the surface of a stainless steel sheet is degreased; 2, the front face of the stainless steel sheet is covered with a photocureable coating material; 3, a film material is pasted onto the front face of the stainless steel sheet; and 4, photocuring is conducted. After the stainless steel sheet is subjected to degreasing, passivating, cleaning and air drying, the photocureable coating material issmeared onto the front face of the stainless steel sheet, the side with the treating agent is covered with the film material, thus, the photocureable coating material makes contact with the stainlesssteel sheet along lines on the film material, accordingly, the photocureable coating material reacts with the stainless steel sheet along the lines on the film material, and chemical wiredrawing is conducted on the stainless steel metal sheet.

Description

technical field [0001] The invention relates to the field of stainless steel production, more specifically, to a stainless steel wire drawing process. Background technique [0002] Stainless steel wire drawing is a metal processing technology and a treatment technology for the surface of stainless steel. [0003] In addition to industrial applications, stainless steel can also be used to make accessories such as ornaments and handicrafts, which are usually made by stainless steel wire drawing process. During the processing, the impurities contained in the stainless steel will be oxidized, which will make the color worse, easy to scratch, and the surface is easy to get dirty. Surface drawing treatment is a surface treatment method that forms lines on the surface of the workpiece through grinding. [0004] For traditional stainless steel wire drawing, the production process is very complicated, the production takes a long time, and the production produces a lot of pollution....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B05D7/14B05D5/06B05D3/06B05D3/00
CPCB05D3/002B05D3/067B05D5/062B05D7/14B05D2502/00
Inventor 范入豪邹炎斌赵秀娟管丽娜张丙炎
Owner 青岛河钢复合新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap