Thermal insulation coating

A heat-insulating coating and magnesium carbonate technology, applied in coatings and other directions, can solve the problems of easy cracking and falling off, no heat insulation, low hardness, etc., and achieve the effects of not easy cracking and falling off, good heat insulation effect and high hardness

Inactive Publication Date: 2019-01-18
四会市中日化工实业有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of living conditions, architectural coatings have become an essential material for indoor and outdoor decoration. At present, the widely used thermal insulation coatings have disadvantages such as low hardness, easy cracking and falling off, easy whitening, and no heat insulation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A heat-insulating coating, consisting of the following components in parts by weight:

[0022] 90 parts of magnesium carbonate;

[0023] 10 parts of mica powder;

[0024] 10 parts of cellulose;

[0025] 10 parts of fluorescent powder;

[0026] 10 parts of porcelain calcium;

[0027] 4 parts of bentonite;

[0028] 15 parts of rubber powder;

[0029] 5 parts of benzoin powder;

[0030] 5 parts of brightening agent;

[0031] 15 parts of ceramic microbeads;

[0032] 20 parts of paraffin alkane.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a thermal insulation coating. The thermal insulation coating is prepared from components in parts by weight as follows: 90 parts of magnesium carbonate, 10 parts of mica powder,10 parts of cellulose, 10 parts of phosphor, 10 parts of vitrified calcium, 4 parts of bentonite, 15 parts of rubber powder, 5 parts of benzoin powder, 5 parts of a brightener, 15 parts of ceramic microspheres and 20 parts of paraffin alkane. The thermal insulation coating is high in hardness and not prone to cracking and peeling, the added benzoin powder can refresh mind and induce resuscitation, the added brightener has good whitening resistance, and the thermal insulation effect is good.

Description

technical field [0001] The invention relates to a thermal insulation coating. Background technique [0002] With the improvement of living conditions, architectural coatings have become an essential material for indoor and outdoor decoration. At present, the widely used thermal insulation coatings have disadvantages such as low hardness, easy cracking and falling off, easy whitening, and no heat insulation. Contents of the invention [0003] The invention aims to provide a heat-insulating coating with high hardness, which is not easy to crack and fall off, and the added benzoin can refresh the mind, and the added brightening agent has good anti-whitening property and good heat-insulating effect. [0004] The specific scheme is: a heat-insulating coating, comprising the following components in parts by weight: [0005] 90 parts of magnesium carbonate; [0006] 10 parts of mica powder; [0007] 10 parts of cellulose; [0008] 10 parts of fluorescent powder; [0009] 10 ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D1/00C09D7/61C09D7/63C09D7/65
CPCC09D1/00
Inventor 李韬
Owner 四会市中日化工实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com