Aluminum profile surface polishing treatment agent and treatment method thereof

A surface polishing and treatment method technology, which is applied in the field of substrate surface polishing, can solve problems such as difficult to clean, uneven and not smooth aluminum profile surface, and achieve good planarity, smooth and smooth aluminum surface, and simple treatment methods Effect

Inactive Publication Date: 2019-02-05
徐州思迈德智能装备有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is difficult for the existing cleaning solution to remove the large protrusions that were originally fixed or attached to the surface of the aluminum profile, resulting in the phenomenon that the surface of the aluminum profile is still uneven or not smooth after being coated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A surface polishing treatment agent for aluminum profiles and a treatment method thereof, specifically comprising the following steps:

[0014] (1) prepare bright treatment liquid, this bright treatment liquid is made of the raw material of following weight portion: dilute hydrochloric acid 5 parts, sodium silicate 11 parts, potassium chromate 12 parts, sodium gluconate 20 parts, trisodium phosphate 12 parts, remove 80 parts of ionized water;

[0015] (2) Immerse the aluminum profile in the polishing treatment agent, which is required to be submerged on the surface of the aluminum profile;

[0016] (3) Spray and clean the surface of the aluminum profile for 1.5 minutes;

[0017] (4) Dry the cleaned aluminum profiles with high-temperature nitrogen.

[0018] Wherein, in step (2), soak for 10 minutes, and the soaking temperature is 30°C. The formulation of the aluminum profile surface polishing treatment agent also contains the components of the formulation in parts by ...

Embodiment 2

[0020] A surface polishing treatment agent for aluminum profiles and a treatment method thereof, specifically comprising the following steps:

[0021] (1) prepare bright treatment liquid, this bright treatment liquid is made of the raw material of following weight portion: 15 parts of dilute hydrochloric acid, 13 parts of sodium silicate, 16 parts of potassium chromate, 30 parts of sodium gluconate, 18 parts of trisodium phosphate, remove 100 parts of ionized water;

[0022] (2) Immerse the aluminum profile in the polishing treatment agent, which is required to be submerged on the surface of the aluminum profile;

[0023] (3) Spray and clean the surface of the aluminum profile, and the cleaning time is 2 minutes;

[0024] (4) Dry the cleaned aluminum profiles with high-temperature nitrogen.

[0025] Wherein, in step (2), soak for 20 minutes, and the soaking temperature is 40°C. The formulation of the aluminum profile surface polishing treatment agent also contains the compo...

Embodiment 3

[0027] A surface polishing treatment agent for aluminum profiles and a treatment method thereof, specifically comprising the following steps:

[0028] (1) prepare bright treatment liquid, this bright treatment liquid is made of the raw material of following weight portion: 10 parts of dilute hydrochloric acid, 12 parts of sodium silicate, 14 parts of potassium chromate, 25 parts of sodium gluconate, 15 parts of trisodium phosphate, remove 90 parts of ionized water;

[0029] (2) Immerse the aluminum profile in the polishing treatment agent, which is required to be submerged on the surface of the aluminum profile;

[0030] (3) Spray and clean the surface of the aluminum profile for 1.5 minutes;

[0031] (4) Dry the cleaned aluminum profiles with high-temperature nitrogen.

[0032] Wherein, in step (2), soak for 15 minutes, and the soaking temperature is 35°C. The formulation of the surface polishing treatment agent for aluminum profiles also contains the components of the for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aluminum profile surface polishing treatment agent and a treatment method of the aluminum profile surface polishing treatment agent. The treatment method specifically comprises the following steps of (1) preparing a brightness treatment liquid, wherein the brightness treatment liquid is composed of the following raw materials of 5-15 parts of dilute hydrochloric acid, 11-13 parts of sodium silicate, 12-16 parts of potassium chromate, 20-30 parts of sodium gluconate, 12-18 parts of trisodium phosphate and 80-100 parts of deionized water; (2) immersing an aluminum profile in the polishing treatment agent, wherein the surface of the aluminum profile is required to be covered; (3) spraying and cleaning the surface of aluminum profile for 1.5-2min; and (4) blow-dryingthe cleaned aluminum profile with high-temperature nitrogen. The formula of the polishing treatment agent is reasonable in compatibility, and the treatment method is simple. Additives in the formulaof the polishing treatment agent can play a role in accelerating aluminum dissolution, so that the aluminum surface is flat and smooth, the content can be further increased, the smoothness of productsurface polishing can be good, and the brightness and cleanness effect of the aluminum profile surface can be effectively improved.

Description

technical field [0001] The invention relates to the technical field of substrate surface polishing, in particular to an aluminum profile surface polishing treatment agent and a treatment method thereof. Background technique [0002] With the progress of the times and the development of various means of transportation, such as airplanes, ships, automobiles and even household products, office furniture all use aluminum shells, which are widely used and are closely related to people's lives. Aluminum profiles without surface treatment have a single appearance and are easy to corrode in humid air, making it difficult to meet the high decorative and weather resistance requirements of building materials. In order to improve the decorative effect, enhance corrosion resistance and prolong the service life, aluminum profiles must be surface treated. However, it is difficult for the existing cleaning solution to remove the larger protrusions that were originally fixed or attached to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23F3/03
CPCC23F3/03
Inventor 章微微
Owner 徐州思迈德智能装备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap