High-toughness rubber pet ball based on rubber material and preparation method thereof

A high-toughness, pet ball technology, applied in the field of rubber products, can solve problems such as easy damage to pet teeth and gums, pet balls or pet hazards, and achieve the effect of protecting dental health and stimulating play interest.

Inactive Publication Date: 2019-02-19
天长市富宝橡塑制品有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a high-toughness rubber pet ball based on rubber material and its preparation method, to solve the problem that the existing pet balls proposed in the above background technology often only change the diameter to target pets of different ages. Pets of different age groups have different tooth development and bite force. Pet balls with the same toughness may cause harm to the pet ball or the pet itself, and the existing pet ball is a solid ball made of a single material, which is easy to Problems that damage your pet's teeth and gums

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-toughness rubber pet ball based on rubber material and preparation method thereof
  • High-toughness rubber pet ball based on rubber material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] The specific preparation steps of the preparation method of the high toughness rubber pet ball based on rubber material are as follows:

[0023] a) Raw material selection: select natural rubber and translucent liquid silica gel, heat 50-70 parts of natural rubber to 56°C-60°C, take it out after heating for 24h-36h, divide it into small pieces weighing 10-20KG, and cut it Put the rubber block into the rubber breaking machine for the rubber breaking treatment and take it out to get the semi-finished product A, add 20-30 parts of translucent liquid silica gel to the silicone oil with a concentration of 5%-9% and stir evenly to get the semi-finished product B;

[0024] b) Masticating: put the semi-finished product A obtained in step a) into an open mill with a roller temperature of 30-40°C, and take it out after 15-20 minutes of plasticating to obtain a semi-finished product C;

[0025] c) Mixing: Put the semi-finished product C obtained in step b) into the internal mixer, ...

Embodiment 1

[0029] The raw materials are taken in parts by mass: 50 parts of natural rubber, 20 parts of translucent liquid silica gel, 2 parts of sulfur S-80, 0.5 part of N-cyclohexyl p-methoxyaniline, 30 parts of carboxyl-terminated liquid nitrile rubber, 2-sulfur Alcohol benzoimidazole 1, calcium carbonate 10, coloring agent 3 parts, the coloring agent is 1.5 parts of phthalocyanine blue, 1.5 parts of rubber scarlet LC;

[0030] a) Selection of raw materials: select natural rubber and translucent liquid silica gel, heat the natural rubber to 56°C, take it out after heating for 24 hours, divide it into small pieces with a weight of 10KG, put the cut rubber pieces into the rubber breaking machine to break the rubber Take it out after processing to get semi-finished product A, add translucent liquid silica gel to 9% silicone oil and stir evenly to get semi-finished product B;

[0031] b) Mastication: plastication: put the semi-finished product A obtained in step a) into the open mill with...

Embodiment 2

[0036] The raw materials are taken in parts by mass: 60 parts of natural rubber, 25 parts of translucent liquid silica gel, 3 parts of sulfur S-80, 1.5 parts of N-cyclohexyl p-methoxyaniline, 35 parts of carboxyl-terminated liquid nitrile rubber, 2-mercaptan 2 parts of benzoimidazole, 13 parts of calcium carbonate, 4 parts of colorant, the colorant is selected as phthalocyanine blue;

[0037] a) Selection of raw materials: select natural rubber and translucent liquid silica gel, heat the natural rubber to 58°C, take it out after heating for 30 hours, divide it into small pieces with a weight of 15KG, put the cut rubber pieces into the rubber breaking machine for breaking After processing, take it out to get semi-finished product A, add translucent liquid silica gel to 7% silicone oil and stir evenly to get semi-finished product B;

[0038] b) Put the semi-finished product A obtained in step a) into an open mill with a roller temperature of 35°C, and take it out after masticati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of rubber products, and particularly relates to a high-toughness rubber pet ball based on a rubber material. The high-toughness rubber pet ball comprises an inner core ball, and a rubber layer is arranged on the outer wall of the inner core ball. The preparation method of the high-toughness rubber pet ball based on the rubber material comprises the following specific preparation steps that a) raw materials are selected; b) plastification is carried out, wherein a semi-finished product A obtained in the step a) is placed into an open mill with the roller temperature of 30-40 DEG C for plastification for 15-20 minutes, and then is taken out so as to obtain a semi-finished product C; c) mixing is carried out; and d) injection molding is carried out, wherein a semi-finished product D obtained in the step c) is placed into a vulcanization molding machine with the temperature of 130-150 DEG C and the diameter of 45-60 mm, and is taken out to obtain the a semi-finished product F after being vulcanized for 39-54 minutes. According to the scheme, the steps are simple, the cost is low, high-toughness pet balls can be prepared for pets of differentages, so that damage to teeth of the pets is avoided.

Description

technical field [0001] The invention relates to the technical field of rubber products, in particular to a rubber-based high-toughness rubber pet ball and a preparation method thereof. Background technique [0002] As the name implies, the rubber pet ball refers to a spherical toy for pets to play with. It is used to exercise the gums and teeth for pets. The existing pet balls often only change the diameter to target pets of different ages. The bite force is different. Pets of different ages choose pet balls with the same toughness, which may cause harm to the pet ball or the pet itself, and the existing pet ball is a solid ball made of a single material, which is easy to damage the pet’s teeth and gums. , we propose a high tenacity rubber pet ball based on rubber material and its preparation method. Contents of the invention [0003] The purpose of the present invention is to provide a high-toughness rubber pet ball based on rubber material and its preparation method, to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29D22/04A01K15/02C08L7/00C08L13/00C08K13/02C08K3/06C08K5/378C08K5/18C08K3/26
CPCA01K15/026B29D22/04C08K2003/265C08L7/00C08L13/00C08K13/02C08K3/06C08K5/378C08K5/18C08K3/26
Inventor 周叶青
Owner 天长市富宝橡塑制品有限公司