Method for preparing vacuum glass with negative pressure in cavity by common glass
A technology of ordinary glass and vacuum glass, applied in the field of vacuum glass production, can solve the problems such as the inability to realize ordinary glass vacuum glass, and achieve the effects of overcoming the difficulty of annealing failure, low welding heating temperature and simple operation.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
specific Embodiment approach 1
[0011] Embodiment 1: This embodiment is a method of using ordinary glass to prepare vacuum glass with negative pressure in the cavity, and it is specifically completed according to the following steps:
[0012] 1. Texturing treatment: use physical methods or chemical methods to perform texturing treatment on the position of ordinary glass to be welded to obtain ordinary glass after texturing treatment;
[0013] 2. Metallization treatment: Cut the aluminum foil or aluminum alloy foil into a strip shape with the same width as the welding position of ordinary glass after texturing treatment. The thickness of the aluminum foil is 0.05mm~1mm, and the thickness of the aluminum alloy foil is 0.05mm~1mm. , and then cleaned to obtain an aluminum strip; lay the aluminum strip on the position to be welded on the ordinary glass after texturing, and use a laser device, a micro-beam plasma device or a high-energy beam device to scan the surface of the aluminum strip to reach the aluminum str...
specific Embodiment approach 2
[0018] Specific embodiment two: The difference between this embodiment and specific embodiment one is: the specific operation process of the physical method described in step one is as follows: use a sandblasting machine or a water jetting machine to spray the position to be welded on the common glass, spray For corundum particles with a particle size of 0.1mm-0.5mm, when a sandblasting machine is used for spraying, the pressure of the high-pressure gas of the sandblasting machine is 150MPa-400MPa, and the continuous spraying time at the same position is 1s-5s; When the machine is spraying, the high-pressure water jetting pressure of the water cutting machine is 150MPa ~ 400MPa, and the continuous spraying time at the same position is 1s ~ 5s; that is, the texture treatment of the position to be welded of the ordinary glass is completed, and the ordinary glass after the texturing treatment is obtained. Others are the same as the first embodiment.
[0019] The roughened ordinar...
specific Embodiment approach 3
[0020] Specific embodiment three: the difference between this embodiment and specific embodiment one is: the specific operation process of the chemical method described in step one is as follows: apply or brush a layer of hydrofluoric acid on the position to be welded of ordinary glass, react 3 minutes to 5 minutes, and then wash and remove the hydrofluoric acid, that is, complete the texturing treatment of the position of the ordinary glass to be welded, and obtain the ordinary glass after the texturing treatment. Others are the same as the first embodiment.
[0021] The surface roughness of the ordinary glass at the position to be welded after the texturing treatment obtained in this embodiment is 1.6 μm to 100 μm.
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap