A kind of phenolic resin modified metal protection anti-rust non-drying oil and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of phenolic resin and tert-butylphenol formaldehyde resin, which is applied in the field of phenolic resin modified metal protection anti-rust non-drying oil and its preparation, can solve the problems of reduced protection ability, easy dripping, low metal adhesion, etc., and achieve Slow down the electrode reaction, not easy to drip, high anti-peeling strength effect
Active Publication Date: 2021-02-23
SHANDONG NORTH MODERN CHEM IND
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0005] First of all, the metal adhesion of metal protection antirust oil is low, and there are finger touches after spraying, and the transfer after collision will cause damage, which reduces its protection ability; secondly, the existing metal protection antirust oil has finger touch transfer, and it is easy to drip after spraying Therefore, a kind of anti-rust oil with high adhesion to metal, not easy to transfer and damage during packaging and transportation, has good salt spray resistance and corrosion resistance, and can have a good protective effect on metal needs to be developed urgently
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0026] A phenolic resin modified metal protection anti-rust non-drying oil, composed of the following raw materials: No. 200 solvent oil 15kg, polyisobutylene 8kg, ethylene-propylene copolymer 5kg, lanolin 5kg, petroleum calcium sulfonate 5kg, dodecenyl Succinic acid 0.1kg, calcium carbonate 22kg, carbon black 1kg, magnesium carbonate 1kg, potassium aluminum silicate 8kg, manganese dioxide 0.01kg, nickel oxide 0.01kg, barium chromate 0.01kg, p-tert-butylphenol formaldehyde resin 8kg and bentonite 1kg.
Embodiment 2
[0028] A phenolic resin modified metal protection anti-rust non-drying oil, composed of the following raw materials: toluene 22kg, polyisobutylene 12kg, base oil 2.5kg, ethylene-propylene copolymer 10kg, lanolin 10kg, petroleum calcium sulfonate 10kg, twelve Alkenyl succinic acid 0.8kg, calcium carbonate 30kg, carbon black 2kg, magnesium carbonate 4kg, potassium aluminum silicate 15kg, manganese dioxide 0.08kg, nickel oxide 0.05kg, barium chromate 0.05kg, p-tert-butylphenol formaldehyde resin 18kg and bentonite 2kg.
Embodiment 3
[0030] A phenolic resin modified metal protection anti-rust non-drying oil, composed of the following raw materials: turpentine 18kg, polyisobutylene 9kg, base oil 1kg, ethylene-propylene copolymer 6kg, lanolin 9kg, petroleum calcium sulfonate 6kg, dodecene Succinic acid 0.7kg, calcium carbonate 24kg, carbon black 1.2kg, magnesium carbonate 2kg, potassium aluminum silicate 10kg, manganese dioxide 0.03kg, nickel oxide 0.04kg, barium chromate 0.02kg, p-tert-butylphenol formaldehyde resin 10kg and bentonite 1.8kg.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a phenolic resin modified metal protection antirust non-drying oil and a preparation method thereof, which is composed of the following raw materials: solvent, polyisobutylene, base oil, ethylene-propylene copolymer, lanolin, calcium petroleum sulfonate, ten Dienyl succinic acid, calcium carbonate, etc.; the solvent is at least one of No. 200 solvent naphtha, toluene or turpentine; the phenolic resin modified metal protection anti-rust non-drying oil of the present invention is compatible between each material Good performance, strong film-forming property, high bonding strength between oil film and metal parts, high anti-peeling strength, high adhesion, the metal layer of metal parts is not easy to be damaged during packaging and shipping, and the salt spray performance can reach 840h, Satisfy the adhesion and salt spray resistance requirements of metal parts to anti-rust non-drying oil; the phenolic resin modified metal protection anti-rust non-drying oil of the present invention will not transfer after finger touch and collision, and it is not easy to drip after spraying. Greatly improved the protection ability of metal parts.
Description
technical field [0001] The invention relates to the technical field of paints and coatings, in particular to a phenolic resin modified metal protection anti-rust non-drying oil and a preparation method thereof. Background technique [0002] Metal protection antirust oil is composed of solvents, antirust substances, corrosion inhibitors, film-forming substances, etc. It needs excellent adhesion and salt spray resistance to protect the metal surface well. However, the current antirust oil for metal protection is generally dry oil, and non-drying oil is prone to oil layer transfer and damage due to low adhesion to metal, which reduces its antirust effect, and rust occurs in hot and humid environments, affecting products quality. [0003] At present, due to the low adhesion of metal protection antirust oil to metal during the film forming process, especially for non-drying oil, the agent is easily damaged during the packaging and transportation of parts, so the corresponding pr...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.