Bonding agent, polycrystalline cubic boron nitride composite sheet and preparation method of cubic boron nitride polycrystalline composite material

A cubic boron nitride and polycrystalline cubic technology, which is applied in the field of superhard materials, can solve the problems of decreased wear resistance and poor thermal conductivity of polycrystalline cubic boron nitride, and achieves avoiding soft spot effect, improving thermal conductivity and good hardness. and the effect of toughness

Inactive Publication Date: 2019-04-05
HENAN HAINADE NEW MATERIAL CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Among them, the metal binder usually softens at 700-800°C, which will lead to a decrease in the wear resistance of polycrystalline cubic boron nitride.
Ceramic binder has the advantages of high temperature wear resistance and strong chemical wear resistance, but ceramics have poor thermal conductivity at high temperatures, so that the cutting temperature is concentrated on the processed material and softens it.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bonding agent, polycrystalline cubic boron nitride composite sheet and preparation method of cubic boron nitride polycrystalline composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] This embodiment provides a kind of binder, and its average particle diameter is 300nm, is made of the following components by mass: 5 parts of metal aluminum, 24 parts of silicon dioxide, 22 parts of silicon carbide, 15 parts of titanium silicide and nitride 15 parts of titanium.

[0019] This embodiment provides a polycrystalline cubic boron nitride composite sheet, which includes the following raw materials in parts by mass: 75 parts of cubic boron nitride and 25 parts of the binder, wherein the average particle diameter of the cubic boron nitride is 10 μm.

[0020] This embodiment provides the preparation method of the polycrystalline cubic boron nitride composite sheet, which includes the following steps:

[0021] Mixing the binder and the cubic boron nitride uniformly to prepare a mixed material;

[0022] Under the condition of 60MPa, press the mixed material into a green body to obtain a green body;

[0023] The green body was sintered at 6.0 GPa and 1300° C. f...

Embodiment 2

[0025] This embodiment provides a kind of binder, and its average particle diameter is 267nm, is made up of the following components by mass: 10 parts of metal aluminum, 38 parts of silicon dioxide, 15 parts of silicon carbide, 15 parts of titanium silicide, nitride 15 parts of titanium and 1 part of graphene powder; wherein, the particle diameter of the graphene powder is 20-40nm.

[0026] This embodiment provides a polycrystalline cubic boron nitride composite sheet, which includes the following raw materials in parts by mass: 80 parts of cubic boron nitride and 20 parts of the binder; wherein, the average particle diameter of the cubic boron nitride is 7 μm.

[0027] This embodiment provides the preparation method of the polycrystalline cubic boron nitride composite sheet, which includes the following steps:

[0028] Mixing the binder and the cubic boron nitride uniformly to prepare a mixed material;

[0029] Under the condition of 80MPa, press the mixed material into a g...

Embodiment 3

[0032] This embodiment provides a kind of binder, and its average particle diameter is 200nm, is made up of the following components by mass: 15 parts of metal aluminum, 57 parts of silicon dioxide, 17 parts of silicon carbide, 13 parts of titanium silicide, nitride 12 parts of titanium and 2 parts of graphene fine powder; wherein, the particle diameter of the graphene fine powder is 20-40nm.

[0033] This embodiment provides a polycrystalline cubic boron nitride composite sheet, which includes the following raw materials in parts by mass: 85 parts of cubic boron nitride and 15 parts of the binder; wherein, the average particle diameter of the cubic boron nitride is 3 μm.

[0034] This embodiment provides the preparation method of the polycrystalline cubic boron nitride composite sheet, which includes the following steps:

[0035] Mixing the binder and the cubic boron nitride uniformly to prepare a mixed material;

[0036] Under the condition of 100MPa, press the mixed mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a bonding agent, a polycrystalline cubic boron nitride composite sheet and a preparation method of the polycrystalline cubic boron nitride composite sheet. The bonding agent iscomposed of metal aluminum, silicon dioxide, tungsten carbide, titanium diboride and titanium nitride, wherein the metal aluminum and the silicon dioxide can react during sintering to produce aluminumoxide and elemental silicon, the melting points of both the aluminum oxide and the elemental silicon are higher than that of the metal aluminum, and the elemental silicon is high in thermal conductivity, so that the bonding agent can effectively overcome the shortcomings of metal bonding agents and ceramic bonding agents. When applied to preparing the polycrystalline cubic boron nitride compositesheet, the bonding agent can effectively improve the hardness, the tenacity and the thermal conductivity of tools and accordingly achieve wide applicability.

Description

technical field [0001] The invention belongs to the field of superhard materials, and in particular relates to a binder, a polycrystalline cubic boron nitride composite sheet and a preparation method thereof. Background technique [0002] Polycrystalline cubic boron nitride is sintered by cubic boron nitride particles and a certain proportion of binder under high temperature and high pressure. The binder plays an important role in the process of synthesizing polycrystalline cubic boron nitride. Adding an appropriate amount of binder can reduce the sintering temperature and pressure, and can improve the performance of the sintered body. Polycrystalline cubic boron nitride binders mainly include metal binders and ceramic binders. [0003] Among them, the metal binder usually softens at 700-800°C, which will lead to a decrease in the wear resistance of polycrystalline cubic boron nitride. Ceramic binder has the advantages of high temperature wear resistance and strong chemica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/5831C04B35/63
CPCC04B35/5831C04B35/6303C04B35/6316C04B2235/3418C04B2235/3826C04B2235/3886C04B2235/3891C04B2235/425C04B2235/6567C04B2235/96C04B2235/9607
Inventor 王丽娜周青
Owner HENAN HAINADE NEW MATERIAL CO LTD
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com