A fire hose and anti-mildew technology, which is applied in the field of fire hose, anti-mildew and antibacterial fire hose materials, can solve the problems of fire hose damage by heat, achieve superior anti-mildew and antibacterial performance, and a simple method Effect

Inactive Publication Date: 2019-04-09
HAILONG CHEM ASSISTANT JIANGDU
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the unpredictable high heat generated by different environments during a fire, some

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A anti-mildew and antibacterial fire hose material, comprising the following components in parts by weight: 20-35 parts of polyvinyl chloride, 2-8 parts of magnesium oxide, 3-9 parts of sulfur, 4-10 parts of paraffin, acrylate 1-5 parts, 10-15 parts of EPDM rubber, 4-9 parts of resorcinol formaldehyde resin, 5-10 parts of decabromodiphenylethane, 1-5 parts of vulcanizing agent, 2-6 parts of composite stabilizer share.

Embodiment 2

[0013] A anti-mildew and antibacterial fire hose material, comprising the following components in parts by weight: 21.6-33.4 parts of polyvinyl chloride, 2.7-7.3 parts of magnesium oxide, 3.8-8.2 parts of sulfur, 4.9-9.1 parts of paraffin, acrylate 1.6-4.4 parts, 10.4-14.6 parts of EPDM rubber, 4.5-8.3 parts of resorcinol formaldehyde resin, 5.6-8.9 parts of decabromodiphenylethane, 1.9-4.4 parts of vulcanizing agent, 2.4-5.6 parts of composite stabilizer share.

Embodiment 3

[0015] A anti-mildew and antibacterial fire hose material, comprising the following components in parts by weight: 23.7-31.3 parts of polyvinyl chloride, 3.2-6.8 parts of magnesium oxide, 4.2-7.8 parts of sulfur, 5.4-8.6 parts of paraffin, acrylate 2.1-3.9 parts, EPDM rubber 11.1-13.9 parts, resorcinol formaldehyde resin 5.3-7.5 parts, decabromodiphenylethane 6.2-8.3 parts, vulcanizing agent 2.4-3.9 parts, composite stabilizer 3.0-4.8 parts share.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-mildew and antibacterial fire hose material and belongs to the technical field of firefighting equipment accessories. The anti-mildew and antibacterial fire hose material is prepared from the following components in parts by weight: 20-35 parts of polyvinyl chloride, 2-8 parts of magnesium oxide, 3-9 parts of sulfur, 4-10 parts of paraffin, 1-5 parts of acrylate, 10-15 parts of EPDM, 4-9 parts of resorcinol formaldehyde resin, 5-10 parts of decabromodiphenyl ethane, 1-5 parts of a vulcanizing agent and 2-6 parts of a compound stabilizer. By compounding the polyvinyl chloride, magnesium oxide, sulfur, paraffin, acrylate, EPDM, resorcinol formaldehyde resin, decabromodiphenyl ethane, the vulcanizing agent and the compound stabilizer, the anti-mildew and antibacterial fire hose material is prepared by an existing preparation process. The method is simple, and the prepared product has relatively excellent anti-mildew and antibacterial performance.

Description

technical field [0001] The invention relates to a fire-fighting hose, in particular to a mildew-proof and antibacterial fire-fighting hose material, which belongs to the technical field of fire-fighting equipment accessories. Background technique [0002] The fire hose is a hose used to transport flame-retardant liquids such as high-pressure water or foam. It is easy to lay during use and has become one of the most important fire-fighting tools in daily life. Due to the unpredictable high heat generated by different environments during a fire, some combustibles will generate high radiant heat, which will cause the fire hose to be damaged by heat. Improve the existing fire hose to make the hose resistant to high pressure, abrasion, high temperature, durable, not easy to leak, low resistance, can also be bent and folded arbitrarily, easy to use, and can play a better role in fire fighting operations effect. The Chinese invention patent with the publication number CN 10634972...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L23/16C08L91/06C08L61/12C08K13/02C08K3/22C08K3/06C08K5/101C08K5/03
CPCC08L27/06C08K2003/222C08L2201/02C08L2205/03C08L23/16C08L91/06C08L61/12C08K13/02C08K3/22C08K3/06C08K5/101C08K5/03
Inventor 李东
Owner HAILONG CHEM ASSISTANT JIANGDU
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap