High temperature phase change heat storage material

A heat storage material, high temperature phase change technology, applied in heat exchange materials, transportation and packaging, metal processing equipment, etc. Simple production process and high compressive strength

Active Publication Date: 2019-04-12
JIANGSU JIANAI HIGH TEMPERATURE MATERIAL
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, so far, there is still no mature high-temperature phase change heat storage system operating stably

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] The first step is to mix 40wt% of quartz sand powder, 30wt% of corundum powder, 15wt% of copper oxide, and 15wt% of zinc oxide in proportion according to the proportion, press molding at 100MPa, heat treatment at 900°C for 3 hours, crush and grind 1. Sieve to obtain sieve material A with particle size less than 0.088mm.

[0036] In the second step, mix 50wt% of sieve material A, 30wt% of carbon black, 10wt% of silicon powder, and 10wt% of aluminum oxalate according to the proportion, heat treatment at 200°C for 2 hours, grind and sieve to obtain a particle size smaller than Abrasive B of 0.045 mm.

[0037] In the third step, 20wt% corundum particles, 30wt% corundum powder, 20wt% abrasive B, 20wt% aluminum-silicon alloy, 5wt% silicon powder, 4wt% silicon carbide powder, 1wt% thermosetting phenolic resin Mix evenly according to the ratio, press and shape at 50 MPa, and heat-treat at 1000° C. for 2 hours to obtain the high-temperature phase-change heat storage material. ...

Embodiment 2

[0040] The first step is to mix 50wt% of quartz sand powder, 30wt% of corundum powder, 15wt% of copper oxide, and 5wt% of zinc oxide in proportion according to the proportion, press molding at 50MPa, place heat treatment at 1000°C for 2 hours, crush and grind 1. Sieve to obtain sieve material A with particle size less than 0.088mm.

[0041] In the second step, 60wt% of sieving material A, 20wt% of carbon black, 10wt% of silicon powder, and 10wt% of aluminum oxalate are mixed uniformly in proportion, placed in 150°C for heat treatment for 3 hours, ground and sieved to obtain a particle size smaller than Abrasive B of 0.045 mm.

[0042] In the third step, 30wt% corundum particles, 10wt% corundum powder, 10wt% abrasive B, 40wt% aluminum-silicon alloy, 4wt% silicon powder, 1wt% silicon carbide powder, 5wt% thermosetting phenolic resin Mix evenly according to the ratio, press and shape at 60 MPa, and heat treat at 1200° C. for 2 hours to obtain the high-temperature phase-change he...

Embodiment 3

[0045] The first step is to mix 60wt% of quartz sand powder, 10wt% of corundum powder, 15wt% of copper oxide, and 15wt% of zinc oxide in proportion according to the proportion, press molding at 70MPa, place heat treatment at 1000°C for 2 hours, crush and grind 1. Sieve to obtain sieve material A with particle size less than 0.088mm.

[0046] In the second step, mix 60wt% of sieve material A, 19wt% of carbon black, 1wt% of silicon powder, and 20wt% of aluminum oxalate in proportion, heat treatment at 250°C for 1 hour, grind and sieve to obtain a particle size smaller than Abrasive B of 0.045 mm.

[0047] In the third step, 40wt% corundum particles, 10wt% corundum powder, 10wt% abrasive B, 30wt% aluminum-silicon alloy, 1wt% silicon powder, 5wt% silicon carbide powder, 4wt% thermosetting phenolic resin Mix evenly according to the ratio, press and shape at 70 MPa, and heat-treat at 1000°C for 3 hours to obtain the high-temperature phase-change heat storage material.

[0048] The w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

Belonging to the technical field of ceramic materials, the invention provides a high temperature phase change heat storage material. The high temperature phase change heat storage material is preparedby the steps of: first, mixing quartz sand powder, corundum powder, copper oxide and zinc oxide evenly in proportion, conducting compression moulding, and then performing heat treatment to obtain a sieving material A; second, mixing the sieving material A, carbon black, silicon powder and aluminum oxalate evenly in proportion, and performing heat treatment to obtain an abrasive B; and third, mixing corundum particles, corundum powder, the abrasive B, aluminum-silicon alloy, silicon powder, silicon carbide powder and thermosetting phenolic resin evenly in proportion, conducting compression moulding, and then performing heat treatment to obtain a finished product. The high temperature phase change heat storage material prepared by the method provided by the invention has a working temperature above 600DEG C, and has the characteristics of large heat storage density, high heat conductivity coefficient, high compressive strength, high thermal shock stability, low production cost, simple process and the like.

Description

technical field [0001] The invention belongs to the technical field of ceramic materials, and in particular relates to a high-temperature phase-change heat storage material and a preparation method thereof. Background technique [0002] Phase change heat storage materials are mainly used in the fields of industrial waste / waste heat recovery, comprehensive solar energy development, and high temperature energy saving. At present, the hybrid sintering method and the melt infiltration method are mainly used to prepare phase change heat storage materials, but there are some shortcomings. The mixed sintering method is to mix the matrix material, phase change material, additives, etc., and obtain the heat storage material after molding and sintering. This method is relatively simple, but when the sintering temperature is too high or the content of the phase change material is large, the evaporation loss of the phase change material will be caused, thereby reducing the heat storage...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K5/06C22C1/05C22C29/00C22C29/12B22F1/00
CPCC09K5/063C22C1/051C22C29/00C22C29/12B22F1/10
Inventor 杨政宏徐华伟张品为李杰黄锋
Owner JIANGSU JIANAI HIGH TEMPERATURE MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap