Process for producing bio-based nylon 56 fiber with antibacterial function

A technology of bio-based nylon and production process, which is applied in the field of fiber processing, can solve the problems of inconvenience for staff, inconvenient for staff to wear or use, and reduce the market popularity of bio-based nylon 56 fiber, so as to improve blood vessel circulation, good The effect of antibacterial ability

Inactive Publication Date: 2019-04-16
南通东屹高新纤维科技有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that the original bio-based nylon 56 fiber proposed in the above background technology does not have antibacterial function, it is inconvenient for the staff to wear or use, and it brings inconvenience to the staff, and the problem of the market popularity of the reduced bio-based nylon 56 fiber

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for producing bio-based nylon 56 fiber with antibacterial function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A bio-based nylon 56 fiber with antibacterial function, which is composed of the following materials in proportion: 30 parts of bio-based nylon 56, 10 parts of coloring masterbatch, 30 parts of distilled water, 1 part of silver powder, 10 parts of copper powder, 10 parts Zinc powder, 30 parts ceramic powder, 30 parts lavender essential oil.

[0029] A manufacturing process, comprising the steps of:

[0030] S1-Mix 1 part of silver powder, 10 parts of copper powder, 10 parts of zinc powder, 30 parts of ceramic powder, 30 parts of lavender essential oil and 30 parts of distilled water to form a mixture A, and place the mixture A into the reactor for heating and stirring for 20 Minutes, the heating temperature is kept at 55°C;

[0031] S2-Put 30 parts of bio-based nylon 56 and 10 parts of colored masterbatch into the reactor to form a mixture B, and heat and stir the mixture B through the reactor for 20 minutes, and the heating temperature is kept at 55°C;

[0032] S3-Co...

Embodiment 2

[0042] A bio-based nylon 56 fiber with antibacterial function, which is composed of the following materials in proportion: 40 parts of bio-based nylon 56, 15 parts of coloring masterbatch, 40 parts of distilled water, 2 parts of silver powder, 15 parts of copper powder, 15 parts Zinc powder, 40 parts ceramic powder, 40 parts lavender essential oil.

[0043] A manufacturing process, comprising the steps of:

[0044] S1-Mix 2 parts of silver powder, 15 parts of copper powder, 15 parts of zinc powder, 40 parts of ceramic powder, 40 parts of lavender essential oil and 40 parts of distilled water to form a mixture A, and place the mixture A into the reactor for heating and stirring for 23 Minutes, the heating temperature is kept at 60°C;

[0045] S2- Put 40 parts of bio-based nylon 56 and 15 parts of colored masterbatch into the reactor to form a mixture B, and heat and stir the mixture B through the reactor for 23 minutes, and the heating temperature is kept at 60°C;

[0046] S3...

Embodiment 3

[0056] A bio-based nylon 56 fiber with antibacterial function, which is composed of the following materials: 50 parts of bio-based nylon 56, 20 parts of coloring masterbatch, 50 parts of distilled water, 3 parts of silver powder, 20 parts of copper powder, 20 parts Zinc powder, 50 parts ceramic powder, 50 parts lavender essential oil.

[0057] A manufacturing process, comprising the steps of:

[0058] S1-Mix 3 parts of silver powder, 20 parts of copper powder, 20 parts of zinc powder, 50 parts of ceramic powder, 50 parts of lavender essential oil and 50 parts of distilled water to form a mixture A, and place the mixture A into the reactor for heating and stirring for 25 Minutes, the heating temperature is kept at 65°C;

[0059] S2-Put 50 parts of bio-based nylon 56 and 20 parts of colored masterbatch into the reactor to form a mixture B, and heat and stir the mixture B through the reactor for 25 minutes, and the heating temperature is kept at 65°C;

[0060] S3-Control the te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of fiber processing, and particularly relates to a bio-based nylon 56 fiber with an antibacterial function. The fiber is prepared from, 30 parts-50 parts of bio-based nylon 56, 10 parts-20 parts of a coloring master batch, 30 parts-50 parts of distilled water, 1 part-3 parts of silver powder, 10 parts-20 parts of copper powder, 10 parts-20 parts of zincpowder, 30 parts-50 parts of ceramic powder and 30 parts-50 parts of lavender essential oil; the silver powder, the copper powder and the zinc powder are added into the nylon 56 fiber, the silver powder, the copper powder and the zinc powder are adhered through the ceramic powder, so that the silver powder, the copper powder and the zinc powder have synergistic effects, the bio-based nylon 56 fiber has a good antibacterial ability, the lavender essential oil is also added to the bio-based nylon 56 fiber, and the lavender essential oil can improve the blood vessel circulation of a user and bring convenience to the user.

Description

technical field [0001] The invention belongs to the technical field of fiber processing, and in particular relates to a production process of bio-based nylon 56 fiber with antibacterial function. Background technique [0002] Polyamide, commonly known as nylon, has a density of 1.15g / cm3. It is a general term for thermoplastic resins containing repeated amide groups—[NHCO]—on the main chain of the molecule, including aliphatic PA, aliphatic-aromatic PA and aromatic PA. Among them, aliphatic PA There are many varieties, large output, and wide application. Its name depends on the specific number of carbon atoms in the synthetic monomer. [0003] The original bio-based nylon 56 fiber does not have antibacterial function, which is inconvenient for staff to wear or use, which brings inconvenience to the staff and reduces the market popularity of bio-based nylon 56 fiber. Contents of the invention [0004] In order to solve the problem that the original bio-based nylon 56 fiber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/90D01F1/10D01D5/08D01D5/088D01D5/16D01D5/253
CPCD01D5/08D01D5/088D01D5/16D01D5/253D01F1/10D01F1/103D01F6/90
Inventor 张子睿
Owner 南通东屹高新纤维科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap