Animal skeleton plasticized specimen and preparation method thereof

A technology for animal bones and specimens, applied in the preservation of human or animal bodies, instruments, teaching models, etc., can solve the problems of easy loss of small bones, inconsistent color, easy osteoporosis, etc., to achieve long-term preservation and low reagent cost Low, no damage to health effects

Inactive Publication Date: 2019-05-14
河南中博科技有限公司
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The structure of the model specimen is simple, there is a certain deviation between the teaching and the real specimen, and the real structure of the specimen cannot be displayed
The production process of steamed bone specimens is simple, the production process is not easy to control, the specimens are easily damaged, the osteoporosis is easy, the small bones are easy to be lost, and the cartilage cannot be preserved
Grease is not easy to clean and easy to mold
Easily damaged during use
Naturally corroded specimens are easily damaged, osteoporosis is easy, small bones are easy to lose, and cartilage cannot be retained
Inconsistent colors, not aesthetically pleasing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Animal skeleton plasticized specimen and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The preparation method of the animal bone plasticized specimen of the present embodiment comprises the following steps:

[0032] 1) Selection of materials: select vertebrate specimens with intact bones, no fractures, and no lesions. In this embodiment, ostrich specimens are selected.

[0033] 2) Antiseptic treatment, using 18% formalin to perfuse the ostrich specimen, the specific perfusion method is: through large blood vessels, including femoral artery, carotid artery, etc., formalin perfusion is permeated into various parts of the ostrich specimen, After the perfusion is completed, the ostrich specimen is soaked in formalin with a volume concentration of 10% for 3 months to obtain a preservative-treated ostrich specimen.

[0034] 3) dissecting, peeling off the skeleton of the ostrich specimen after antiseptic treatment from the ostrich specimen, the peeling method is: cut the skin of the ostrich specimen in the middle of the abdomen and peel it off completely, and pe...

Embodiment 2

[0043] The preparation method of the animal bone plasticized specimen of the present embodiment comprises the following steps:

[0044] 1) Selection of materials: select vertebrate specimens with intact bones, no fractures, and no lesions. In this embodiment, ostrich specimens are selected.

[0045] 2) Antiseptic treatment, using 15% formalin to perfuse the ostrich specimen, the specific perfusion method is: through the large blood vessels, including the femoral artery, carotid artery, etc., the formalin perfusion is permeated into various parts of the ostrich specimen, After the perfusion is completed, the ostrich specimen is soaked in formalin with a volume concentration of 10% for 3 months to obtain a preservative-treated ostrich specimen.

[0046] 3) dissecting, peeling off the skeleton of the ostrich specimen after antiseptic treatment from the ostrich specimen, the peeling method is: cut the skin of the ostrich specimen in the middle of the abdomen and peel it off comple...

Embodiment 3

[0055] The preparation method of the animal bone plasticized specimen of the present embodiment comprises the following steps:

[0056] 1) Selection of materials: select vertebrate specimens with intact bones, no fractures, and no lesions. In this embodiment, ostrich specimens are selected.

[0057] 2) Antiseptic treatment, using 20% ​​formalin to perfuse the ostrich specimen, the specific perfusion method is: through the large blood vessels, including femoral artery, carotid artery, etc., perfusing formalin into various parts of the ostrich specimen, After the perfusion is completed, the ostrich specimen is soaked in formalin with a volume concentration of 8% for 4 months to obtain a preservative-treated ostrich specimen.

[0058] 3) dissecting, peeling off the skeleton of the ostrich specimen after antiseptic treatment from the ostrich specimen, the peeling method is: cut the skin of the ostrich specimen in the middle of the abdomen and peel it off completely, and peel off t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an animal skeleton plasticized specimen and a preparation method thereof and belongs to the technical field of biological plasticization. The preparation method of the animalskeleton plasticized specimen comprises the following steps: peeling off a skeleton of an animal specimen after preservative treatment from the animal specimen, maintaining cartilage and ligaments atjoint parts of the skeleton, and bleaching the peeled skeleton; soaking the peeled skeleton in an acetone solution for 50-60 days; leaving the skeleton specimen after dehydration and degreasing to stand still in silica gel in a vacuum pressure cabin for 40-50 days, adjusting the pressure of the vacuum pressure cabin to 0.8-1.2 kPa from 0.05-0.1 kPa gradually in standing, and extruding the silica gel into the skeleton specimen to replace the acetone solution; shaping and repairing the soaked skeleton specimen, putting into a curing tank, and curing by using silica gel curing agent steam, thereby obtaining the animal skeleton plasticized specimen. The animal skeleton plasticized specimen has a complete skeleton shape and structure without change, has a good three-dimensional feeling and is beneficial to later specimen observation.

Description

technical field [0001] The invention belongs to the technical field of biological plasticization, and in particular relates to a plasticized animal bone specimen and a preparation method thereof. Background technique [0002] At present, the commonly used biological specimens for teaching and learning in schools include: model specimens, boiled bone specimens, and naturally corroded bone specimens. The structure of the model specimen is simple, and there is a certain deviation between the teaching and the real specimen, which cannot show the real structure of the specimen. The production process of steamed bone specimens is simple, and the production process is not easy to control. The specimens are easily damaged, osteoporosis is easy, small bones are easy to be lost, and cartilage cannot be preserved. Grease is not easy to clean and easy to mold. It is easily damaged during use. Naturally eroded specimens are easily damaged, osteoporosis is easy, small bones are easy to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A01N1/00G09B23/36
Inventor 程明亮赵顺贠跃进户振国刘会民王永超
Owner 河南中博科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap