A kind of preparation method of polylactone

A technology of polylactone and cyclic lactone, which is applied in the field of preparation of polylactone, can solve the problems of unfavorable material stability, uncontrollable reaction process, low molecular weight of the product, etc., and achieves narrow molecular weight distribution index and no monomer residue. , the effect of high catalytic efficiency

Active Publication Date: 2021-02-02
NANJING TECH UNIV
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional method of preparing polyester is mainly polycondensation method. This method usually requires high temperature, consumes a lot of energy, and the obtained product has a low molecular weight and a wide molecular weight distribution. The reaction process is uncontrollable, which is not conducive to the stability of the material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of polylactone
  • A kind of preparation method of polylactone
  • A kind of preparation method of polylactone

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] In a 10mL polymerization tube, add δ-valerolactone (0.27ml, 3mmol), hydantoin derivative (7) (0.016g, 0.1mmol), DBU (14.94ul, 0.1mmol), benzyl alcohol (10.34μL, 0.1mmol), stirred magnetically for 4 hours at 90°C, stopped the reaction, added a small amount of dichloromethane dropwise to the resulting mixture to dissolve, then slowly dropped the resulting solution into cold methanol, a white polymer was precipitated, and was centrifuged and vacuum-dried 0.38 g of the product was obtained, the conversion rate was 95.2%, the number average molecular weight Mn of polyvalerolactone was 3612 g / mol, and the molecular weight distribution PDI was 1.07. The hydrogen spectrum of polyvalerolactone is as follows figure 1 As shown, ( 1 H NMR (CDCl 3 ):δ(ppm),1.67–1.70(m,4H×n,(-CH 2 CH 2 CH 2 O-)n and (-COCH 2 CH 2 CH 2 -)n), 1.95(q, 2H, J=7.2Hz, ArCH 2 CH 2 CH 2 -),2.34(t,2H×n,J=6.9Hz,(-OCOCH 2 CH 2 -)n), 2.68(t, 2H, J=7.7Hz, ArCH 2 CH 2 -),3.65(t,2H,J=6.5Hz,-CH 2 CH ...

Embodiment 2

[0057] In a 10 mL polymerization tube, add D-lactide (0.072 g, 0.5 mmol), hydantoin derivative (3) (0.002 g, 0.01 mmol), 2-tert-butyl-1,1,3,3- Tetramethylguanidine (20.4ul, 0.1mmol), pentaerythritol (9.7μL, 0.1mmol), magnetically stirred at 200°C for 24 hours, stopped the reaction, added a small amount of dichloromethane dropwise to the resulting mixture to dissolve, and then dissolved the resulting solution Slowly drop into cold methanol, a white polymer precipitated, centrifuged and vacuum dried to obtain 0.034g of the product, the conversion rate was 67.9%, the number average molecular weight Mn of poly-D-lactide was 1310g / mol, and the molecular weight distribution PDI was 1.19.

Embodiment 3

[0059] In a 10mL polymerization tube, add L-lactide (7.2g, 50mmol), hydantoin derivative (4) (0.017g, 0.1mmol), tetramethylguanidine (12.55ul, 0.1mmol), benzyl alcohol ( 10.0 μL, 0.1 mmol), stirred magnetically at 130°C for 8 hours, stopped the reaction, added a small amount of dichloromethane dropwise to the resulting mixture to dissolve, then slowly dropped the resulting solution into cold methanol, a white polymer was precipitated, and centrifuged , Vacuum drying to obtain 5.9 g of the product, the conversion rate is 98.4%, the number average molecular weight Mn of poly-L-lactide is 37100 g / mol, and the molecular weight distribution PDI is 1.20. The hydrogen spectrum of polylactide is as image 3 As shown, ( 1 H NMR (400MHz, CDCl 3 ),δ(ppm),1.57-1.59(m,3H×n,(–CH 3 )n),4.34(m,1H,–CH(CH 3 )OH),5.13–5.21(q,1H×(n-1),–CH(CH 3 )O–; 2H, ArCH 2 O–), 7.33–7.34 (m, 5H, aryl).); Its size exclusion chromatography analysis spectrum is as Figure 4 As shown, it can be seen from th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
molecular weight distributionaaaaaaaaaa
molecular weight distributionaaaaaaaaaa
molecular weight distributionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of polylactone and relates to the technical field of polymer materials. The present invention uses initiator alcohol or amine to initiate the ring-opening of cyclic lactone monomers or cyclic lactide monomers or cyclic carbonate monomers, and initiates the ring-opening polymerization of small molecule monomers under the catalysis of organic catalysts to obtain Polylactone, the organic catalyst is a hydantoin derivative and a tertiary amine catalyst system. The technical solution of the invention has high catalytic efficiency, mild reaction, high-efficiency synthesis of precise polylactone, no metal residue, narrow molecular weight distribution, high product yield, no monomer residue, and snow-white color.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, in particular to a preparation method of polylactone. Background technique [0002] Among many synthetic polymer materials, aliphatic polyester occupies an important position due to its excellent biodegradability, bioabsorbability and biocompatibility, and has become a research hotspot in recent years. Due to the easily hydrolyzed ester group in the molecular structure of this kind of polyester, it is easy to gradually decompose into oligomers or monomers in the presence of water and microorganisms, and then be metabolized into carbon dioxide and water, so it can show certain biodegradability. Compatibility, which has great application potential in biomedicine, tissue engineering and other fields. [0003] The traditional method of preparing polyester is mainly polycondensation method. This method usually requires high temperature, consumes a lot of energy, and the obtained product has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G63/87C08G63/08C08G64/02C08G64/30
Inventor 郭凯李振江张婵李洁姚志威刘博
Owner NANJING TECH UNIV