Louver leaf coating and preparation method thereof

A technology for blinds and blades, which is applied to coatings, devices for coating liquid on surfaces, and pre-treated surfaces, etc. It can solve the problems of poor bending resistance and single function of the coating of shutter blades, and achieve improved waterproof performance and decomposition The best effect, the effect of improving the bending resistance

Active Publication Date: 2019-06-18
HANGZHOU YOUPU PLASTIC NEW MATERIAL CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a kind of louver blade coating, by improving the ratio of stiffening agent and the first solvent in the inner coating film, and adding water repellent and nano-titanium dioxide in the outer coating film, the bending resistance of the textile blade coating is improved performance, and has the ability to absorb formaldehyde and harmful substances VOCS, which solves the defect that the existing louver blade coating has a single function and poor bending resistance when sprayed on textile blades

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Louver leaf coating and preparation method thereof
  • Louver leaf coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A louver blade coating provided by the invention includes: coating on the woven fabric blade, including an inner coating film and an outer coating film; the formula of the inner coating film contains modified polyvinyl acetate polymer Stiffening agent and water of polymer, wherein the percentage by weight of stiffening agent is 20%; In the prescription of described outer coating film, comprise waterproofing agent, nanometer titanium dioxide and water, wherein the weight percent of organic fluororesin C6 waterproofing agent, nanometer titanium dioxide are respectively 3% and 0.3%.

Embodiment 2

[0030] A louver blade coating provided by the invention includes: coating on the woven fabric blade, including an inner coating film and an outer coating film; the formula of the inner coating film contains modified polyvinyl acetate polymer Stiffening agent and water of polymer, wherein the percentage by weight of stiffening agent is 30%; In the formula of described outer coating film, comprise waterproofing agent, nanometer titanium dioxide and water, wherein the weight percent of organic fluororesin C6 waterproofing agent, nanometer titanium dioxide are respectively 8% and 0.8%.

Embodiment 3

[0032] like figure 1 , figure 2 Shown; The present invention also provides a kind of preparation method of louver blade coating, comprises the following steps:

[0033] 1) Mix the stiffening agent and water according to the ratio to form the inner coating film mixture;

[0034] 2) The louver blades are dipped, and the inner coating film mixture is evenly coated on the surface of the blades and the inside of the weaving gap; then baked at 60-℃ for 3 minutes to form a hardened inner coating film;

[0035] 3) Mix waterproofing agent, nano-titanium dioxide and water in proportion to form an outer coating film mixture;

[0036] 4) Dip the louver blades with the hardened inner coating film to evenly coat the coating on the surface of the protective film; then bake at 60°C for 3 minutes to form a hardened outer coating film.

[0037] The baking in step 2) and step 4) is carried out in a baking device. The baking device includes a long box 1, and the box includes an inverted bucket-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a louver leaf coating which coats woven fabric leaves and comprises an inner coating and an outer coating. The inner coating is composed of a stiffening agent and a first solvent, weight percent of the stiffening agent is 20-30%, the outer coating is composed of a waterproof agent, nano titanium dioxide and a second solvent, and weight percents of the waterproof agent and nano titanium dioxide are 3-8% and 0.3-0.8% respectively. By improving proportion of the stiffening agent and the first solvent, bending resistance of the textile leaf coating is improved; on the basisof improving bending resistance of the inner coating, the outer coating is sprayed on the outer surface of the inner coating, so that waterproof performance of textile leaves is further improved; by adding nano titanium dioxide into the outer coating, formaldehyde and harmful substances VOCS in surrounding air can be absorbed.

Description

technical field [0001] The invention relates to the field of louver blade manufacturing, in particular to a louver blade coating and a preparation method thereof. Background technique [0002] At present, shutters are curtains hung on windows with functions of shading, heat insulation and ventilation. Existing shutters generally consist of multiple blades strung together by ropes. Existing textile blades on the market are usually made by using solid acrylic hard-repellant and fluorine-based waterproof finishing. Although they have a certain hard-repellent effect and waterproof function, they have single functions and poor bending resistance. However, in the process of assembly and use, if the blade is slightly bent or touched by hard objects, scratches and marks will be left. The elasticity of the leaves is poor; it will affect the appearance after a period of use. [0003] In the prior art, just like the patent document 1: CN201620061120.7, this invention patent provides...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/04D06N3/00B05D3/04
Inventor 项建荣
Owner HANGZHOU YOUPU PLASTIC NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap