Nickel-based catalyst used for preparation of hydrogenated petroleum resin as well as preparation method and application of catalyst

A technology for hydrogenating petroleum resins and nickel-based catalysts, applied in metal/metal oxide/metal hydroxide catalysts, physical/chemical process catalysts, chemical instruments and methods, etc., can solve the influence of catalyst life and reduce catalyst hydrogenation activity , irreversible deactivation and other problems, to achieve the effect of inhibiting the reduction of softening point, high industrial application value, and excellent hydrogenation performance
CN109999820AActive Publication Date: 2019-07-12FUZHOU UNIVERSITY
7 Cites 5 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
FUZHOU UNIVERSITY
Publication Date
2019-07-12

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention discloses a nickel-based catalyst used for preparation of hydrogenated petroleum resin as well as a preparation method and application of the catalyst. The method comprises the followingsteps: preparing carbonate radical intercalated NiMgAl-M-LDH (M=La or Cu) quaternary hydrotalcite by adopting a urea hydrolysis method, performing high-temperature calcination, and performing reduction in a reducing atmosphere to obtain the nickel-based catalyst having a high specific surface area and a highly-dispersed active center. According to the catalyst synthesized by the method, auxiliaryagent metal element La or Cu is doped, so that the acidity of the surface of the catalyst can be effectively neutralized, inhibition of hydrodegradation of petroleum resin is facilitated, the softening point of the hydrogenated product is improved, dispersity of the active center Ni can be effectively increased, and deep hydrogenation of unsaturated hydrocarbon bonds in the petroleum resin can bepromoted; and the catalyst has a simple and easy synthetic method, low preparation costs, a simple hydrogenation process and easy industrialization, and when the obtained catalyst is used for hydrogenation of the petroleum resin, the hydrogenated petroleum resin having a water white color and a high softening point can be prepared.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention belongs to the technical field of catalyst preparation, and in particular relates to a nickel-based catalyst used for the preparation of hydrogenated petroleum resin, a preparation method and application thereof. Background technique

[0002] Petroleum resin is a kind of thermoplastic resin produced by polymerizing the by-product distillate oil in the cracking ethylene production process. It is widely used in coatings, rubber additives, printing and other industries, but at the same time, petroleum resin contains A large number of impurities such as unsaturated hydrocarbon bonds and halogen elements make petroleum resins have disadvantages such as dark hue, pungent smell, poor adhesion, light and thermal stability, and poor oxidation stability, which limits its application in high-precision fields.

[0003] Hydrogenated petroleum resin is a special material with excellent performance obtained by catalytic hydrogenation of unsaturated C=C ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More