Novel microlite polished brick production technology

A production process and technology of polished tiles, applied in the field of polished tiles, can solve the problems of insufficient hardness and complex production and processing technology of polished tiles, and achieve the effect of simple processing methods and improved hardness and wear resistance

Inactive Publication Date: 2019-08-02
佛山市东方安达建材有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The current production and processing technology of polished tiles is relatively complicated, which makes it easy to cause the hardness not to meet the requirements due to improper processing during processing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] In the embodiment of the present invention, a new microcrystalline polished brick production process includes the following raw materials: 25 parts of clay, 8 parts of albite, 5 parts of quartz, 14 parts of talc, 12 parts of Suzhou soil, and 15 parts of mica , 7 parts of marble waste, 9 parts of mixed water, 3 parts of additives, and 10 parts of microcrystalline stone. The new microcrystalline stone polished tile includes the following production process steps:

[0034] Step 1: Send clay, albite, quartz, talc, Suzhou soil, mica, and marble waste in the raw materials to the crushing equipment for crushing to obtain raw material powder, and then put the raw material powder into the sieving equipment , to remove impurities and metals in raw materials;

[0035] Step 2: Add the raw material powder to the spray drying equipment, and prepare the raw material powder with a certain size and viscosity through the spray drying equipment, and then add the raw material powder to the...

Embodiment 2

[0046] In the embodiment of the present invention, a new microcrystalline polished brick production process includes the following raw materials: 35 parts of clay, 10 parts of albite, 7 parts of quartz, 16 parts of talc, 14 parts of Suzhou soil, and 16 parts of mica , 8 parts of marble waste, 15 parts of mixed water, 6 parts of additives, and 12 parts of microcrystalline stone. The new microcrystalline stone polished tile includes the following production process steps:

[0047] Step 1: Send clay, albite, quartz, talc, Suzhou soil, mica, and marble waste in the raw materials to the crushing equipment for crushing to obtain raw material powder, and then put the raw material powder into the sieving equipment , to remove impurities and metals in raw materials;

[0048] Step 2: Add the raw material powder to the spray drying equipment, and prepare the raw material powder with a certain size and viscosity through the spray drying equipment, and then add the raw material powder to t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel microlite polished brick production technology. The novel microlite polished brick production technology is characterized in that a microlite polished brick is preparedfrom raw materials in the ratio as follows: 25-35 parts of clay, 8-10 parts of soda feldspar, 5-7 parts of quartz, 14-16 parts of talc, 12-14 parts of Suzhou soil, 15-16 parts of mica, 7-8 parts of marble waste, 9-15 parts of mixed water, 3-6 parts of auxiliaries and 10-12 parts of microlite. Compared with a traditional polished brick processing method, the technology is simpler, meanwhile, marble waste is effectively applied, the waste raw materials are effectively utilized, and besides, the microlite is added to the polished brick, so that hardness and wear resistance of the polished brickare improved.

Description

technical field [0001] The invention relates to the field of polished tiles, in particular to a novel production process for microcrystalline polished tiles. Background technique [0002] Polished brick is a kind of bright brick made by grinding the surface of the whole body brick body, which belongs to a kind of whole body brick. Compared with whole-body bricks, the surface of polished bricks is much smoother, and is suitable for use in indoor spaces such as toilets and kitchens. On the basis of using the bleeding technology, polished tiles can be made into various stone-like and wood-like effects. [0003] The current production and processing technology of polished tiles is relatively complicated, which makes it easy to cause the hardness not to meet the requirements due to improper processing during processing. Contents of the invention [0004] In order to overcome the disadvantages of the above-mentioned situation, the present invention aims to provide a technical ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/16C04B33/132B24B9/06C04B41/82
CPCB24B9/06C04B33/1305C04B33/131C04B33/1324C04B33/16C04B41/009C04B41/82C04B2235/3463C04B2235/3472C04B2235/447C04B2235/656Y02P40/60
Inventor 郭洪章
Owner 佛山市东方安达建材有限公司