Bubble glaze for glass mosaic and process for preparing glass mosaic

A technology of glass mosaic and preparation process, which is applied in the field of glass mosaic, which can solve the problem of single surface effect and achieve the effect of strong three-dimensional effect, good bubble effect and clear texture

Active Publication Date: 2019-08-06
佛山市唯格建材有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the splicing pattern of glass mosaic is very rich, the surface effect of a single glass mosaic product on the market is very single, which is not enough to meet the needs of users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bubble glaze for glass mosaic and process for preparing glass mosaic
  • Bubble glaze for glass mosaic and process for preparing glass mosaic
  • Bubble glaze for glass mosaic and process for preparing glass mosaic

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0051] Embodiment group A-B-a kind of preparation technology of the glass mosaic with bubble effect, comprises the following steps:

[0052] (1) Weigh the glass powder, blowing agent and low-temperature lead-free frit according to the proportions in Table 1 below, and sieve them to the limits of the glaze fineness in Table 2 below, and set aside;

[0053] (2) Take the sieved glass powder, foaming agent and low-temperature lead-free frit, add stabilizer and suspending agent, add water and carry out ball milling, the ball milling process parameters are limited by the ball milling ratio and ball milling time in Table 2, and obtain the basic glaze pulp;

[0054] (3) Take 90-95 parts of the basic glaze slurry obtained in step (2), and 0-5 parts of the coloring material, stir evenly, add water to mix according to the mass-volume concentration limit in Table 2, and obtain the glazing glaze slurry-bubble Glaze A1, A2, A3;

[0055] (4) Apply the glazing slurry obtained in step (3) to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bubble glaze for glass mosaic. The bubble glaze comprises the following raw materials by mass: 80-90 parts of glass powder, 5-10 parts of a foaming agent, 5-10 parts of low temperature lead-free frit, 0-5 parts of pigment and water, with the fineness of the bubble glaze being 200-250 meshes. Correspondingly, glass mosaic with the bubble glaze and a process of preparing the same are disclosed. The glass mosaic with a bubble effect, which is prepared by the process, has uniform and fine glaze surfaces, good bubble effects, clear textures and a strong three-dimensional effect.

Description

technical field [0001] The invention relates to the technical field of glass mosaics, in particular to a bubble glaze for glass mosaics and a preparation process for glass mosaics. Background technique [0002] Made of natural minerals and glass powder, glass mosaic is the safest building material and an outstanding environmental protection material. With the continuous improvement of people's living standards, people's pursuit of home interior decoration is also changing, and the requirements for decorative mosaics are also increasing. At present, for home decoration, especially the decoration of bathrooms and kitchens, glass mosaics can be used to create richer pattern effects, so more people choose glass mosaics with rich pattern effects. Although the splicing pattern of glass mosaic is very rich, the surface effect of a single glass mosaic product on the market is very single, which is not enough to meet the needs of users. Therefore, in order to further improve the ri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More