Modified crosslinked maleic anhydride-1-octadecene alternating copolymer and preparation method and application thereof

A technology of alternating copolymers and maleic anhydride, which is applied in the direction of drilling compositions, chemical instruments and methods, etc., can solve the problems of asphalt-based fluid loss control agents such as reducing the drilling speed and increasing the amount of polluted environment, and achieves the improvement of filtration reduction Loss effect, good compatibility, obvious effect of filtration loss reduction

Active Publication Date: 2019-08-06
CHINA NAT OFFSHORE OIL CORP +2
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are fewer fluid loss control agents for oil-based drilling fluids than for water-based drilling fluids, and they are mainly divided into polymers, humic acid amines, lignin and asphalt products, of which asphalt Fluid loss additives have the advantages of wide selection of materials and low price, and have been widely used in the past period of time. However, asphalt fluid loss additives have the disadvantages of reducing drilling speed, polluting the environment, and large dosage. They are widely used in environmentally sensitive areas in China. In oil-based drilling fluid formulations in most parts of the country and abroad, its use has been restricted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified crosslinked maleic anhydride-1-octadecene alternating copolymer and preparation method and application thereof
  • Modified crosslinked maleic anhydride-1-octadecene alternating copolymer and preparation method and application thereof
  • Modified crosslinked maleic anhydride-1-octadecene alternating copolymer and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) Synthesis of maleic anhydride-1-octadecene alternating copolymer

[0034] Mix 4.9g of maleic anhydride and 12.5g of 1-octadecene with 17g of toluene, dissolve under magnetic stirring and pass nitrogen gas for 30min, add 0.35g of dibenzoyl peroxide (BPO) and raise the temperature to 95°C for 6h, rotate After evaporating the solvent and concentrating, it was washed with ethanol precipitation and dried to obtain about 17 g of white powder.

[0035] (2) Synthesis of Alternating Copolymer of Maleic Anhydride-1-Octadecene Modified by Polyenylamine

[0036] The maleic anhydride-1-octadecene alternating copolymer that 3.5g step (1) gained is dissolved in 80mL chloroform, and 1.89g tetraethylenepentamine is dissolved in the 20mL chloroform solution, to maleic anhydride-1-decacene The tetraethylenepentamine solution in chloroform was added dropwise to the chloroform solution of the octadecene alternating copolymer, reacted at 40° C. for 4 hours, and was spin-dried to obtain ...

Embodiment 2

[0038] The difference between this example and Example 1 is only that the amount of tetraethylenepentamine used in step (2) is 0.36g.

Embodiment 3

[0040] The only difference between this embodiment and embodiment 1 is: the amount of tetraethylenepentamine used in step (2) is 0.95g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a modified cross-linked maleic anhydride-1-octadecene alternating copolymer and a preparation method and application thereof. The modified crosslinked maleic anhydride-1-octadecene alternating copolymer has a chemical structure as shown in formula (I). The preparation method comprises the following steps of: carrying out modified cross-linking reaction on a maleic anhydride-1-octadecene alternating copolymer and polyene amine to obtain the modified cross-linked maleic anhydride-1-octadecene alternating copolymer. The modified crosslinked maleic anhydride-1-octadecene alternating copolymer has a good fluid loss reducing effect and can be used as a fluid loss reducing agent for drilling fluids.

Description

technical field [0001] This article relates to the synthesis technology of copolymers, especially a modified cross-linked maleic anhydride-1-octadecene alternating copolymer and its preparation method and application. Background technique [0002] The ever-increasing demand for oil puts forward requirements for industrially exploiting more difficult-to-develop and undeveloped reservoirs. Drilling fluid is a circulating flushing medium used in the well during the drilling process. Its function is to take out cuttings, cool and lubricate drilling tools, maintain wellbore stability, and balance formation pressure. There are a large number of high-temperature and high-pressure oil and gas fields in my country, and their extreme conditions make mining operations extremely difficult. Oil-based drilling fluids are more and more widely used in drilling deep and ultra-deep wells because of their advantages such as high temperature resistance, salt and calcium intrusion resistance, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F8/32C08F210/14C08F222/06C09K8/035
CPCC08F8/32C09K8/035C08F210/14C08F222/06
Inventor 赵春花孙强耿铁王伟陈晏如罗健生李自立苗海龙谭业邦刘刚吴若楠