A kind of PVA sodium alginate double-network cold-resistant conductive hydrogel and preparation method thereof

A conductive hydrogel and sodium alginate technology, applied in the field of hydrogel preparation, can solve the problems of poor cold resistance of self-healing hydrogel, achieve good conductivity and self-healing performance, and expand the effect of temperature application range

Active Publication Date: 2022-03-15
CHANGCHUN UNIV OF TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem of poor cold resistance of existing self-healing hydrogels, and provide a kind of PVA sodium alginate double-network cold-resistant conductive hydrogel and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of PVA sodium alginate double-network cold-resistant conductive hydrogel and preparation method thereof
  • A kind of PVA sodium alginate double-network cold-resistant conductive hydrogel and preparation method thereof
  • A kind of PVA sodium alginate double-network cold-resistant conductive hydrogel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0022] The present invention firstly provides a preparation method of PVA sodium alginate double-network cold-resistant conductive hydrogel, the reaction process and principle schematic diagram are as follows figure 1 As shown, the method includes:

[0023] Step 1: Dissolve sodium alginate in deionized water, add EDC·HCl and m-aminophenylboronic acid to react, the reaction temperature is preferably room temperature, and the reaction time is preferably 20-24h, and the product is dialyzed, and the dialysis The time is preferably 5-7 days, then lyophilized, and then the lyophilized product is dissolved in deionized water and stirred, the stirring rate is preferably 800-1000r / min, and the stirring time is preferably 3-5h to obtain the first solution ;

[0024] The mass ratio of the sodium alginate, EDC·HCl and m-aminophenylboronic acid is preferably (1-1.5): (0.96-1.0): 0.33, more preferably 1: 0.96: 0.33; the lyophilized The mass g of the product: the volume mL of deionized wat...

Embodiment 1

[0032] Step 1: Take 2.5g (0.125mol) of sodium alginate and dissolve it in deionized water, add 2.4g (12.5mol) of EDC HCl and 0.825g (6.25mol) of m-aminophenylboronic acid, stir at room temperature for 24h, and dialyze the product. The size of the bag is 14000, dialysis for 7 days, change the water every 24 hours, put the dialysate into a freeze dryer and freeze-dry to obtain modified sodium alginate, weigh 0.5g of modified sodium alginate and dissolve it in 10ml of deionized water , magnetically stirred at a speed of 900r / min at room temperature for 4h until completely dissolved to obtain the first solution;

[0033] Step 2: Add 10ml of glycerin to 10ml of deionized water at room temperature and continue to stir with a magnetic stirrer for 10min until the two phases are completely miscible. Dissolve 2g of PVA and polyaniline 0.04 in 20ml of deionized water and glycerin mixture with a volume ratio of 1:1 , under the condition of 90°C, magnetically stir at a speed of 1000r / min f...

Embodiment 2

[0040] Step 1: Take 2.5g (0.125mol) of sodium alginate and dissolve it in deionized water, add 2.4g (12.5mol) of EDC HCl and 0.825g (6.25mol) of m-aminophenylboronic acid, stir at room temperature for 24h, and dialyze the product. The size of the bag is 14000, dialysis for 7 days, change the water every 24 hours, put the dialysate into a freeze dryer and freeze-dry to obtain modified sodium alginate, weigh 0.5g of modified sodium alginate and dissolve it in 10ml of deionized water , magnetically stirred at a speed of 900r / min at room temperature for 4h until completely dissolved to obtain the first solution;

[0041] Step 2: Add 10ml of glycerin to 10ml of deionized water at room temperature and continue to stir with a magnetic stirrer for 10min until the two phases are completely miscible. Dissolve 1.5g of PVA and polyaniline 0.05 in 20ml of deionized water and glycerin mixture with a volume ratio of 1:1 At 95°C, stir magnetically at a speed of 1000r / min for 2h until the PVA ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a PVA sodium alginate double-network cold-resistant conductive hydrogel and a preparation method thereof, belonging to the technical field of hydrogel preparation. The method is to dissolve sodium alginate in deionized water first, add EDC·HCl and m-aminophenylboronic acid to react, dialyze and freeze-dry the product, and then dissolve the freeze-dried product in deionized water and stir to obtain the first solution; dissolving PVA and polyaniline in deionized water and glycerin mixture to obtain a second solution; mixing the first solution and the second solution to obtain a PVA sodium alginate double network cold-resistant conductive hydrogel. The hydrogel of the present invention can still maintain good electrical conductivity and self-healing performance at low temperatures, and can be applied in the fields of electronic skin, biological or chemical sensors, and the like.

Description

technical field [0001] The invention belongs to the technical field of hydrogel preparation, and in particular relates to a PVA sodium alginate double-network cold-resistant conductive hydrogel and a preparation method thereof. Background technique [0002] Hydrogel is a material with a three-dimensional hydrophilic network structure, which can absorb a large amount of water and expand in volume, but is insoluble in water. Due to their unique structure, they are widely used in many fields such as medical treatment, pharmaceutical and chemical industry. The water retention capacity of hydrogel comes from the hydrophilic groups in the material, such as -OH, -COOH, -CONH 2 , -CONH-, -SO 3 H. Due to the affinity between water and the hydrogel network, water may exist in the three-dimensional network in the form of bound water, bound water and free water, and lose fluidity, so the hydrogel can maintain a certain shape. Self-healing hydrogels, as a type of hydrogel, have the a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/075C08L29/04C08L79/02C08L5/04C08K5/053C08B37/04
CPCC08J3/075C08B37/0084C08J2329/04C08J2479/02C08J2405/04
Inventor 吴广峰靳凯运张会轩
Owner CHANGCHUN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com