High-temperature-resistant ferritic stainless steel for cold heading fastener nut and production process thereof

A production process and high-temperature-resistant technology, applied in the field of metallurgical materials, can solve problems such as high Ni content and affect the processing effect of use, and achieve the effect of low work hardening rate, small deformation resistance and appropriate hardness

Inactive Publication Date: 2019-08-23
苏州誉高紧固系统有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the stainless steel provided by this patent has a Ni content as high as 11.00-13.00wt%, and continuous operation in the high temperature region of 600°C will affect the processing effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A high temperature resistant ferritic stainless steel for cold heading fastener nuts according to the present invention, the high temperature resistant ferritic stainless steel is composed of the following components by weight percentage: 0<C≤0.06wt%, 0<Mn≤1.0 wt%, 0<Si≤1.0wt%, 0<P≤0.045wt%, 0<S≤0.04wt%, Cr: 10.5~11.75wt%, 0<Ni≤0.5wt%, Nb: 0.25~0.75wt% , Fe: 84.89~86.61wt%.

[0039] Further, the size of the inclusions in the high and low temperature resistant ferrite material within 2mm from the surface of the high and low temperature resistant ferrite material is ≤0.15Lm.

[0040] Further, the type B inclusions in the high and low temperature resistant ferrite material are ≤ grade 0.5, the type D inclusions are ≤ grade 1, and the sum of the inclusions is ≤ grade 3.

[0041] At the same time, the present invention also provides a production process of high temperature resistant ferritic stainless steel for cold heading fastener nuts. The production process includes the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
tensile strengthaaaaaaaaaa
reduction of areaaaaaaaaaaa
Login to View More

Abstract

The invention provides high-temperature-resistant ferritic stainless steel for a cold heading fastener nut and a production process thereof. The high-temperature-resistant ferritic stainless steel iscomposed of the following components including, by weight, larger than 0 and smaller than or equal to 0.06% of C, larger than 0 and smaller than or equal to 1.0% of Mn, larger than 0 and smaller thanor equal to 1.0% of Si, larger than 0 and smaller than or equal to 0.045% of P, larger than 0 and smaller than or equal to 0.04% of S, 10.5%-11.75% of Cr, larger than 0 and smaller than or equal to 0.5% of Ni, 0.25%-0.75% of Nb and 84.89%-86.61% of Fe. According to the high-temperature-resistant ferritic stainless steel, a product cannot deform and can be used for cold heading materials through heat treatment hardening under continuous working of a 500 DEG C high temperature area, and the high plasticity index, elongation and the area reduction rate are achieved. During cold plastic deformation, the deformation resistance of the materials is small, the work hardening rate is low, and the yield ratio of the materials is small, and the hardness is appropriate.

Description

technical field [0001] The invention belongs to the technical field of metallurgical materials, and in particular relates to a high-temperature-resistant ferritic stainless steel for cold heading fastener nuts and a production process thereof. Background technique [0002] The cold heading process is one of the few new processes for non-cutting metal pressure processing. It is a processing method that uses the plastic deformation of metal under the action of external force, and with the help of molds, redistributes and transfers the metal volume to form the required parts or blanks. The cold heading process is most suitable for the production of standard fasteners such as bolts, screws, nuts, rivets, and pins. [0003] High-temperature-resistant ferrite materials need materials that will not deform and can be used for cold extrusion under continuous operation in the high-temperature region of 700 °C. [0004] At present, similar materials in China have high surface strengt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/04C22C38/02C22C38/48C22C33/04C21D8/06
CPCC21D8/065C21D2211/005C22C33/04C22C38/02C22C38/04C22C38/48
Inventor 周民刘小姜
Owner 苏州誉高紧固系统有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products