Vegetable protein friction nano-generator and application thereof

A nano-generator and tribo-generator technology, which is applied in tribo-generator, nanotechnology, nano-medicine and other directions, can solve the problems of triboelectricity properties and mechanism to be explored, cumbersome processing steps, difficult application, etc. Simple preparation process and growth-promoting effect

Active Publication Date: 2019-10-08
ZHEJIANG UNIV
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, cumbersome processing steps will make it difficult for practical application
So far, the application of plant prote

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Vegetable protein friction nano-generator and application thereof
  • Vegetable protein friction nano-generator and application thereof
  • Vegetable protein friction nano-generator and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] 1) First, the preparation of the protein film: the protein is dispersed in an aqueous solution or a concentration of 70%-90% ethanol solution (1-10%, w / w) to prepare a protein solution; then add a mass of Protein 10-60% (w / w) plasticizer (such as glycerin), heated and denatured in a water bath at 60-95°C, stirred for 30-60 minutes, degassed under vacuum for 10 minutes, then poured into a mold and placed in an oven Evaporate to dryness at 30-70°C.

[0040] In the specific implementation, the dried protein film is finally peeled off, and the specific implementation also places the protein film under constant temperature and humidity conditions, so that it can balance the moisture under certain temperature and humidity conditions for subsequent electrical tests.

[0041] 2) Triboelectric negative layer: The specific triboelectric negative layer is made of polytetrafluoroethylene (Teflon), polydimethylsiloxane (PDMS), polyvinyl chloride (PVC), polyimide (Kapton), silicon R...

Embodiment 1

[0046] 1) The first is the preparation of the protein film. The film-forming solution is prepared by dispersing rice protein, peanut protein isolate, soybean protein isolate, and wheat gluten in distilled water (5%, w / w). In addition, zein is dispersed in The concentration is 70% ethanol aqueous solution (5%, w / w). Then, 30% (w / w) glycerol with a mass of protein was added to the five protein solutions.

[0047] 2) In the present embodiment, for rice protein, peanut protein isolate, soybean protein isolate, and wheat gluten, the following are specifically: 5g vegetable protein and 1.5g glycerin are mixed in 100mL deionized aqueous solution, and after magnetic stirring for 10 minutes, , and then adjust the pH of the protein precursor solution. The pH value of the protein solution was adjusted to 12 using 1 M sodium hydroxide solution; then the protein solution was heated and stirred at 65 °C for 30 minutes, and degassed under vacuum for 10 minutes to remove air bubbles.

[004...

Embodiment 2

[0053] Taking rice protein as an example, 5 g of rice protein and 1.5 g of glycerol were mixed in 100 mL of deionized aqueous solution, and after magnetic stirring for 10 minutes, the pH of the protein solution was adjusted to 12 using 1 M sodium hydroxide solution. The protein solution was then heated and stirred at 65 °C for 30 min, and degassed under vacuum for 10 min to remove air bubbles. Finally, the final film-forming solution was poured into a circular Teflon mold (3 cm in diameter) and dried in an oven at 60 °C. Finally, the dried film was peeled off and placed in a constant temperature and humidity incubator at 25° C. and 40% relative humidity for 24 hours as a triboelectron-donating layer for testing.

[0054] Preparation of the triboelectric negative layer: the polylactic acid film was cut into a circle with a diameter of 3 cm.

[0055] Preparation of triboelectric nanogenerator: The above-mentioned rice protein film and polylactic acid film were combined to form ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a vegetable protein friction nano-generator and an application thereof. The friction generator comprises a triboelectric negative layer and a protein membrane. The protein membrane and the triboelectric negative layer are stacked face to face, the respective back surface is adhered or plated with an electrode, or only the back surface of the protein membrane or the back surface of the triboelectric negative layer is provided with a grounded electrode. Protein powder is dissolved in water or an aqueous solution of ethanol, and then a plasticizer is added. The protein isdenatured by heat treatment to acquire a more extended structure required for film formation. Finally, the solvent is evaporated and dried acquire the protein membrane with uniform texture and good transparency and flexibility. The friction generator is used for growth applications of crops. According to the invention, plant protein is innovatively used as a triboelectric material; the friction nano-generator is used as a biodegradable mulch film; a space electric field promoting system is created for agriculture; and the friction nano-generator can be further used for the growth of crops.

Description

technical field [0001] The invention relates to a friction nanogenerator, in particular to a vegetable protein friction nanogenerator and its application. Background technique [0002] With the rapid development of flexible and portable electronics, triboelectric nanogenerators capable of efficiently converting various forms of mechanical energy into electrical energy will be used as the mainstream of future world energy supply. So far, most research works on triboelectric nanogenerators have emphasized structural design or material innovation. [0003] Materials currently widely used in triboelectric nanogenerators include polyamide (nylon)-11 and polyethylene terephthalate (PET), etc. It is worth noting that these materials cannot be completely degraded and are prone to release dangerous chemicals. With the rapid upgrading of electronic products, they will become electronic waste, which undoubtedly brings a huge burden to the environment. Therefore, flexible devices fabr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H02N1/04B82Y5/00
CPCB82Y5/00H02N1/04
Inventor 平建峰姜成美
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap