Magnetic surface molecularly imprinted polymer and preparation method and application thereof

A surface molecular imprinting and polymer technology, applied in the direction of electrochemical variables of materials, can solve the problems of poor selectivity and low sensitivity, and achieve the effect of high accuracy, high sensitivity and improving the degree of polymerization.

Active Publication Date: 2019-11-08
NANHUA UNIV
View PDF10 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it has been found in practice that conventionally prepared magnetic molecularly imprinted polymers still have the problems of low sensitivity and poor selectivity for the detection of AP.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Magnetic surface molecularly imprinted polymer and preparation method and application thereof
  • Magnetic surface molecularly imprinted polymer and preparation method and application thereof
  • Magnetic surface molecularly imprinted polymer and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] This example provides a method for preparing a molecularly imprinted polymer on a magnetic surface, such as figure 1 a. figure 1 b, including:

[0044] Add 2.5mmol AP (template molecule), 3mmol methacrylic acid MAA (functional monomer) and 30ml tetrahydrofuran into a beaker, stir for 30min, then add 2mmol 4-VP (functional monomer), stir for 10min, then add 0.05gFe 3 o 4 @SiO 2 , 4mmol ethyl tetrasilicate TEOS (crosslinking agent), and 20mg azobisisobutyronitrile AIBN (initiator), ultrasonic 60min, deoxygenation, sealed at 35 ℃ for 6h;

[0045] The obtained molecularly imprinted polymer was eluted in an eluent of acetic acid:methanol with a volume ratio of 2:8 for 35 minutes, and the final product was separated by a magnet, washed several times with distilled water, dried in vacuum at 60°C for 8 hours, and set aside.

Embodiment 2

[0047] This embodiment provides a method for preparing an electrochemical sensor, comprising: weighing 4g of graphite powder and 1ml of paraffin oil in a beaker, mixing and stirring until a paste is formed, and then taking an appropriate amount of the paste and pressing it into a mixture with a length of about 8 cm and an inner diameter of about 8 cm. In a 4mm polypropylene plastic tube, a pencil lead with a length of about 5cm is inserted at the end of the tube as a circuit connection point, and a round NdFeB magnet (diameter 4mm, thickness 2mm) is embedded in the other end about 1.5mm, and then filled with the above prepared Coated with graphite powder 2mm, and finally polished into a smooth mirror surface on paper, the magnetic carbon paste electrode (MCPE) was obtained.

[0048] Then ultrasonically disperse 1.0 mg of the magnetic polymer (MMIP) prepared in Example 1 in 1 ml of tetrahydrofuran, get 25 μL of the suspension and evenly drop it on the surface of MCPE to obtain t...

Embodiment 3

[0050] This embodiment provides an AP detection method, including:

[0051] The CHI660C electrochemical workstation (Shanghai Chenhua Co., Ltd.) was used as the detection platform, MCPE was used as the working electrode, the calomel electrode was used as the reference electrode, and the platinum electrode was used as the counter electrode.

[0052] Perform electrochemical experiments according to the optimized conditions. Before each experiment, immerse the working electrode in 5.0mL paracetamol standard solution for recombination for 25min, then wash the surface impurities with distilled water, and immerse the above electrode in 5.0ml of 0.2mmol / L PBS buffer (pH 5.0) for detection.

[0053] DPV experiments were performed over a potential range of 0.8 V to 0 V, with a pulse width of 170 ms, a potential increment of 20 mV, a pulse amplitude of 50 mV, and a scan rate of 25 mV s -1 .

[0054] The test results are as follows:

[0055] 1. Cyclic voltammetry characterization

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
areaaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of polymer materials and electrochemical analysis, in particular to a magnetic surface molecularly imprinted polymer and a preparation method and application thereof. The magnetic surface molecularly imprinted polymer comprises a magnetic surface molecularly imprinted polymer body, and the preparation method comprises the steps: adopting AP as a template moleculeand methyl propene and 4-vinylpyridine as functional monomers, and performing a reaction with nanomagnetic particles under the action of a crosslinking agent and an initiator so as to prepare the magnetic surface molecularly imprinted polymer. A sensor can be manufactured through combination of the magnetic surface molecularly imprinted polymer with a detecting electrode, and has the advantages of high sensitivity, high accuracy, good selectivity, good stability and the like when applied to AP detection.

Description

technical field [0001] The invention relates to the fields of polymer materials and electrochemical analysis, in particular to a magnetic surface molecularly imprinted polymer and its preparation method and application. Background technique [0002] Paracetamol (acetaminophen, AP), commonly known as paracetamol, chemical name is 4-acetaminophenol or N-(4-hydroxyphenyl) acetamide, used for cold fever, joint pain, neuralgia and migraine, and surgery It is a common acetanilide antipyretic and analgesic drug, which is widely used in Chinese and Western medicine and its preparations. [0003] The antipyretic and analgesic effect of AP is mild and long-lasting, safe and effective, so it is widely used clinically. However, because paracetamol has certain toxic and side effects on the human body, taking too much paracetamol will cause nausea, vomiting, and even cause myolysis and liver and kidney failure. , thereby threatening life. Therefore, the detection of AP is of great signi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/06C08F226/06C08K9/10C08K3/36C08K3/22C08J9/26G01N27/48G01N27/30
CPCC08F220/06C08J9/26C08J2201/0424C08J2333/02C08K3/22C08K3/36C08K9/10C08K2003/2275C08K2201/01C08K2201/011G01N27/30G01N27/48C08F226/06
Inventor 肖锡林苏昌霖郦志阳王志梅张迪
Owner NANHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap