Smoke formation matrix for electronic cigarette cartridge and preparation method
A technology for electronic cigarettes and cartridges, applied in the field of electronic cigarettes, can solve problems such as harming the health of smokers, endangering public health, and polluting the environment, and achieves the effects of low cost, reduced production cost, and wide sources.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0027] Example one
[0028] Preparation of tea particles
[0029] Cementing: Cementing fresh tea leaves at a temperature of 130°C and a cementing time of 30 minutes to reduce the moisture content of the tea material to 15%;
[0030] Drying: Dry the above-mentioned deactivated product at 100°C for 30 minutes to reduce the moisture content to less than 5%;
[0031] Grinding: The above-mentioned dried product is sequentially passed through coarse powder and fine powder to obtain a powdered tea material with a particle size of 300-2000 mesh.
[0032] S6: Granulation: Weigh 70g of propylene glycol, 80g of glycerol, 25g of essential oil, and 25g of vanillin, and mix them evenly to obtain a mixed solution. Weigh 800g of powdered tea material, spray the mixed solution while stirring, and shake to obtain The tea particles are sieved to obtain tea particles with a particle size of 20-50 mesh.
Example Embodiment
[0033] Example two
[0034] Preparation of tea silk
[0035] Cementing: Cement fresh tea leaves at a temperature of 110°C and a cementing time of 50 minutes to reduce the moisture content of the tea material to 15%;
[0036] Shredding: shredding the finished product to obtain tea silk with a length of 1mm-10mm and a width of 0.2mm-1.5mm;
[0037] Drying: Drying at 110°C for 30 minutes to obtain product two, the moisture content of which is reduced to less than 5%, to obtain dried tea silk.
Example Embodiment
[0038] Example three
[0039] Preparation of tea powder
[0040] Cementing: Cementing fresh tea leaves at a temperature of 130°C and a cementing time of 30 minutes to reduce the moisture content of the tea material to 15%;
[0041] Drying: Dry the above-mentioned deactivated product at 100°C for 30 minutes to reduce the moisture content to less than 5%;
[0042] Grinding: The above-mentioned dried product is sequentially passed through coarse powder and fine powder to obtain tea powder with a particle size of 300-2000 mesh.
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Length | aaaaa | aaaaa |
Width | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap