Abrasion-resistant yarn processing technology
A processing technology and yarn technology, which is applied in the field of wear-resistant yarn processing technology, can solve the problems of poor wear resistance and easy fading of yarn, and achieve excellent wear resistance, reduce the degree of color fading, and simple operation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] A processing technology of wear-resistant yarn, comprising the following specific steps:
[0021] S1. Prepare the loose fibers and send them into the cleaning equipment for cleaning treatment. In the cleaning equipment, use clean water to spray the loose fibers three times. The time for each spray is 20 minutes, and the temperature of the clean water is 45°C; after cleaning, enter Dry in an oven, the oven temperature is 65°C, the drying time is 55min, take it out and cool to room temperature;
[0022] S2. Put the cleaned yarn into the first dipping tank for dipping treatment, the temperature is 75°C, the dipping time is 2h, and the first dipping solution includes the following components by weight: 37 parts of polyethylene Alcohol, 25 parts of chlorine dioxide, 24 parts of titanium dioxide, 11 parts of 2-chloro-N-(2-iodophenyl) pyridine-3-carboxamide and 13 parts of polycarbosilane; after impregnation, the yarn is sent to an oven for Drying, the oven temperature is 60°...
Embodiment 2
[0026] A processing technology of wear-resistant yarn, comprising the following specific steps:
[0027] S1. Prepare the loose fibers and send them into the cleaning equipment for cleaning treatment. In the cleaning equipment, use clean water to spray the loose fibers three times. The time for each spray is 25 minutes, and the temperature of the clean water is 47°C; after cleaning, enter Dry in an oven, the oven temperature is 65°C, the drying time is 55min, take it out and cool to room temperature;
[0028] S2. Put the cleaned yarn into the first dipping tank for dipping treatment, the temperature is 75°C, the dipping time is 2h, and the first dipping solution includes the following components by weight: 37 parts of polyethylene Alcohol, 25 parts of chlorine dioxide, 24 parts of titanium dioxide, 11 parts of 2-chloro-N-(2-iodophenyl) pyridine-3-carboxamide and 13 parts of polycarbosilane; after impregnation, the yarn is sent to an oven for Drying, the oven temperature is 60°...
Embodiment 3
[0032] A processing technology of wear-resistant yarn, comprising the following specific steps:
[0033] S1. Prepare the loose fibers and send them to the cleaning equipment for cleaning treatment. In the cleaning equipment, use clean water to spray the loose fibers three times. The time for each spray is 25 minutes, and the temperature of the clean water is 48°C; after cleaning, enter Dry in an oven, the oven temperature is 60°C, the drying time is 45min, take it out and cool to room temperature;
[0034] S2, put the cleaned yarn into the first dipping tank for dipping treatment, the temperature is 72°C, the dipping time is 1.8h, and the first dipping solution includes the following components by weight: 33 parts poly Vinyl alcohol, 22 parts of chlorine dioxide, 19 parts of titanium dioxide, 8 parts of 2-chloro-N-(2-iodophenyl)pyridine-3-carboxamide, and 10 parts of polycarbosilane; the yarn is sent to the oven after impregnation is complete For drying, the oven temperature ...
PUM
Property | Measurement | Unit |
---|---|---|
particle size (mesh) | aaaaa | aaaaa |
particle size (mesh) | aaaaa | aaaaa |
particle size (mesh) | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com