Preparation method and product of self-repairing polythiourethane protective coating material

A polythiourethane, protective coating technology, applied in polyurea/polyurethane coatings, coatings, etc., can solve problems such as material failure, and achieve the effect of reinforcing materials, good self-healing performance, and terminating crack propagation

Active Publication Date: 2021-09-10
HUNAN UNIV OF SCI & TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a preparation method and product of a self-repairing polythiourethane protective coating material, thereby solving some problems in the prior art, such as the repair of intelligent materials and coating fillers, and realizing the problem of industrialized production; The surface coating materials of traditional marine ships and marine equipment are disturbed by collision, light and other factors during the service process to produce cracks and lead to material failure. It plays a role in stopping the crack propagation and can also be used as a coating filler for offshore wind power applications. Generating blades to achieve the purpose of repairing protection and strengthening materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and product of self-repairing polythiourethane protective coating material
  • Preparation method and product of self-repairing polythiourethane protective coating material
  • Preparation method and product of self-repairing polythiourethane protective coating material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A self-healing polythiourethane material is prepared from a small molecular compound containing a disulfide bond and an isocyanate-terminated polythiourethane, and the specific steps are as follows;

[0022] (1) Calculate and weigh raw materials.

[0023] (2) Preparation of small molecule compounds containing disulfide bonds: Weigh 0.9 mL of β-mercaptoethanol into a 150 mL beaker, stir well, then quickly add 1.1 mL of triethylamine (TEA) dropwise, and keep the reaction vessel open to air contact, slowly and dropwise add 1.3 mL of H 2 o 2 (30%), white turbidity will be produced during the dropping process, and a large amount of heat will be released. When the temperature of the beaker is cooled to room temperature, continue to add H 2 o 2 (30%), after the dropwise addition, continue to stir until the solution is colorless and transparent, remove the reaction solvent and dry in vacuum at 60 °C overnight to constant weight.

[0024] (3) Preparation of isocyanate-termin...

Embodiment 2

[0027] A preparation of a self-healing polythiourethane material, which is prepared from a small molecular compound containing a disulfide bond and an isocyanate group-terminated polythiourethane, and the specific steps are as follows;

[0028] (1) Calculate and weigh raw materials.

[0029] (2) Preparation of small molecule compounds containing disulfide bonds: Weigh 2.7 mL of β-mercaptoethanol solution in a 150 mL beaker, stir well, then quickly add 3.3 mL of triethylamine (TEA) solution dropwise, and keep the reaction vessel open In contact with air, slowly and dropwise add 3.9 mL of H 2 o 2 (30%) solution, white turbidity will be generated during the dropping process, and a large amount of heat will be released. When the temperature of the beaker is cooled to room temperature, continue to add H 2 o 2 (30%), after the dropwise addition, continue to stir until the solution is colorless and transparent, remove the reaction solvent and dry in vacuum at 60 °C overnight to co...

Embodiment 3

[0033] A preparation of a self-healing polythiourethane material, which is prepared from a small molecular compound containing a disulfide bond and an isocyanate group-terminated polythiourethane, and the specific steps are as follows;

[0034](1) Calculate and weigh raw materials.

[0035] (2) Preparation of small molecular compounds containing disulfide bonds: Weigh 2.7 mL of β-mercaptoethanol into a 150 mL beaker, stir well, then quickly add 3.3 mL of triethylamine (TEA) dropwise, and keep the reaction vessel open to the air. contact, slowly and dropwise add 5.2 mL of H 2 o 2 (30%), white turbidity will be produced during the dropping process, and a large amount of heat will be released. When the temperature of the beaker is cooled to room temperature, continue to add H 2 o 2 (30%), after the dropwise addition, continue to stir until the solution is colorless and transparent, remove the reaction solvent and dry in vacuum at 60 °C overnight to constant weight.

[0036] (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a self-repairing polythiourethane protective coating material. In the method, triethylamine (TEA) is used as a catalyst at first, and H 2 o 2 (30%) as an oxidizing agent, select one or more of thioglycerol, β-mercaptoethanol, and trimethylolpropane (TMMP) to prepare small molecular segments with dynamic reversible covalent bonds (containing Disulfide bond small molecular segment), followed by 4-4'-diphenylmethane diisocyanate (MDI) and trimethylolpropane tris (TMMP) to prepare isocyanate-terminated polythiourethane prepolymer, Finally, the above product is prepared through polycondensation reaction to prepare self-healing polythiourethane material. The synthesis method is simple, the reaction yield is high, the post-treatment method is simple, and it has good self-repair performance. It can be used as a coating filler and applied to offshore wind power blades to achieve the purpose of repairing and reinforcing materials.

Description

technical field [0001] The invention relates to the field of self-healing polymer materials, in particular to the preparation of disulfide bond-based intrinsic self-healing polymer materials. Background technique [0002] Coating is a corrosion control method commonly used in marine engineering equipment at present. However, traditional polymer materials are disturbed by factors such as collision and light during service or processing, and cracks will occur. If it is not repaired in time, corrosion will spread from microcracks, but it is difficult or impossible to detect externally, and the expansion of these microcracks will reduce the mechanical properties and stability of the material, and eventually lead to material failure. (Zhang Xiaoa, Jiang Shengling, etc. Supramolecular polymer composite materials and their self-healing behavior [J]. Polymer Bulletin, 2016 (11): 1-8.) After investigating the main anti-corrosion coating systems in my country, it can be seen that Dome...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/76C08G18/38C08G18/10C09D175/04
CPCC08G18/10C08G18/3876C08G18/7671C09D175/04
Inventor 欧宝立刘刚赵欣欣彭彩茹
Owner HUNAN UNIV OF SCI & TECH