A high-efficiency flame-retardant, smoke-suppressing, environmental-friendly dual-functional additive and PVC-u material prepared therefrom

A PVC-U, dual-function technology, applied in the field of high-efficiency flame-retardant, smoke-suppressing and environmental-friendly dual-function additives and PVC-U materials prepared from it, can solve the problem of poor dispersion, toxic and harmful smoke, flame retardants and smoke suppressants Large dosage and other problems, to achieve the effect of high flame retardant efficiency, low smoke generation, and low smoke toxicity

Active Publication Date: 2021-08-03
GUANGDONG LIANSU TECH INDAL
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a low-smoke and high-efficiency flame-retardant PVC material for the defects and deficiencies of the existing PVC material manufacturing technology, such as the large amount of flame retardant and smoke suppressant used, poor dispersion, and a large amount of toxic and harmful smoke generated during the flame-retardant process. Environmentally friendly dual-function additives

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-efficiency flame-retardant, smoke-suppressing, environmental-friendly dual-functional additive and PVC-u material prepared therefrom
  • A high-efficiency flame-retardant, smoke-suppressing, environmental-friendly dual-functional additive and PVC-u material prepared therefrom

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A high-efficiency flame-retardant, smoke-suppressing and environmental-friendly dual-functional additive, the specific preparation process is as follows:

[0029] According to the calculation, the total load of molybdenum and zinc is 15% (molar ratio: zinc / molybdenum = 2 / 1), then add a certain mass ratio of zinc borate, ammonium molybdate and nano halloysite carrier, stir at room temperature for 2 hours and then ultrasonically disperse 5 minutes, followed by rotary evaporation at 50°C to remove the solvent, and finally calcined at 250°C for 2 hours to obtain a molybdenum-zinc composite flame retardant and smoke suppressor supported by nano halloysite, which is the high-efficiency flame-retardant, smoke-suppressing and environmental protection dual-function assistant agent. The prepared bifunctional flame retardant and smoke suppressant is ground and sieved for use.

[0030] A low-smoke, high-efficiency, flame-retardant and environmentally friendly PVC-U material, the s...

Embodiment 2

[0033] A high-efficiency flame-retardant, smoke-suppressing, and environmental-friendly dual-function auxiliary agent, the specific preparation process is the same as in Example 1, except that the molar ratio of zinc and molybdenum is 5:4.

[0034] A low-smoke, high-efficiency, flame-retardant and environmentally friendly PVC-U material, the specific components are the same as in Example 1, except that the added flame-retardant and smoke suppressant is a dual-function additive prepared in this example.

Embodiment 3

[0036] A high-efficiency flame-retardant, smoke-suppressing, and environmental-friendly dual-function auxiliary agent. The specific preparation process is the same as in Example 1, except that the molar ratio of zinc and molybdenum is 1:1.

[0037] A low-smoke, high-efficiency, flame-retardant and environmentally friendly PVC-U material, the specific components are the same as in Example 1, except that the added flame-retardant and smoke suppressant is a dual-function additive prepared in this example.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-efficiency flame-retardant, smoke-suppressing, environmental-friendly dual-functional additive and a PVC-U material prepared therefrom. The preparation process of the dual-functional auxiliary agent is as follows: dissolving the flame retardant and smoke suppressant in water or ammonia water, then adding the nano halloysite carrier, mixing at room temperature, removing the solvent, and performing high-temperature calcination to prepare the Nano halloysite-loaded dual-functional additives for flame retardant and smoke suppressant. The present invention adopts a lead-free cadmium formula to provide a high-efficiency flame-retardant and smoke-suppressing dual-function auxiliary agent. The PVC-U material prepared by using it as a flame-retardant and smoke-suppressant agent not only has high flame-retardant efficiency, low smoke generation, and smoke The toxicity is very small, which can not only greatly improve the probability of human beings escaping in a fire, but also does not pollute the environment, which is conducive to ensuring the safety of human life and property; at the same time, the preparation process of the present invention is simple, low in cost, and convenient for large-scale popularization and application; in addition, it can It is of great economic and social significance to fill the gap in the existing market and improve the development level of the upstream and downstream industries of PVC‑U materials.

Description

technical field [0001] The invention relates to the technical field of PVC-U plastic materials, and more specifically relates to a high-efficiency flame-retardant, smoke-suppressing and environmental-friendly dual-functional additive and a PVC-U material prepared therefrom. Background technique [0002] PVC is the second largest general-purpose plastic in the world after PE. It has excellent comprehensive physical and chemical properties, chemical corrosion resistance, high strength, excellent insulation performance, long service life, low cost, and has natural properties due to its high chlorine content. Put out the flame retardant performance. Therefore, PVC is widely used in power cables, electronic appliances, automobiles, home furnishing, building materials and other fields. However, as humans have higher and higher requirements on the safety and environmental performance of materials, the PVC-U materials currently available on the market have been difficult to meet th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08K9/12C08K3/22C08L27/06C08L23/06C08K13/06
CPCC08K3/22C08K9/12C08K2003/2255C08K2003/2296C08L27/06C08L2201/02C08L2205/03C08L23/06C08K13/06
Inventor 陈勇李统一宋科明
Owner GUANGDONG LIANSU TECH INDAL