Preparing method of elevator guide rail
A technology of elevator guide rail and preparation process, which is applied in the field of mechanical devices, can solve problems such as poor quality of elevators, manual correction errors, and instability of elevator guide rails, and achieve the effects of increasing anti-corrosion effects, good use effects, and improving anti-rust capabilities
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] During preparation, the profiles are first subjected to stress relief treatment, and the profiles are stacked together flatly in an open natural environment for 8 days. After being exposed to wind and sun under natural conditions, the stress-relieved profiles are obtained; De-rust the profile after stress relief, put the profile in the shot blasting machine, use composite metal shot with a particle size of Φ2.5mm, use compressed air as the power, and use the high-speed movement of the composite metal shot to clean and derust the surface of the profile , the composite metal shot is made of 65% steel, 20% nickel and 15% copper composite casting, and the duration is controlled within 10 minutes to obtain the derusted profile; the derusted profile is rough processed, and the profile Send it to the straightening machine for straightening, the straightening speed is 2.5m / s, and obtain the rough profile; process the guide surface of the rough profile, and use a special high-spe...
Embodiment 2
[0025] During preparation, the profiles are first subjected to stress relief treatment, and the profiles are stacked together in an open natural environment for 7 days. After being exposed to wind and sun under natural conditions, the stress-relieved profiles are obtained; The profile after stress relief is derusted, put the profile in the shot blasting machine, use composite metal shot with a particle size of Φ1mm, use compressed air as the power, and use the high-speed movement of the composite metal shot to clean and derust the surface of the profile. The metal shot is made of 65% steel, 20% nickel and 15% copper composite casting, and the duration is controlled within 15 minutes to obtain the derusted profile; the derusted profile is rough processed, and the profile is sent to Straightening is carried out in the straightening machine, the straightening speed is 4m / s, and the rough profile is obtained; the rough profile is processed on the guide surface, according to the siz...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Granularity | aaaaa | aaaaa |
Roughness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information

- R&D
- Intellectual Property
- Life Sciences
- Materials
- Tech Scout
- Unparalleled Data Quality
- Higher Quality Content
- 60% Fewer Hallucinations
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com