What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of martensitic stainless steel and welding methods, applied in welding equipment, welding accessories, arc welding equipment, etc., can solve the problems of easy cracking of welds, avoid weld fractures, avoid cracking of annealing and pickling lines, and increase protection intensity effect
Active Publication Date: 2020-02-14
GANSU JIU STEEL GRP HONGXING IRON & STEEL CO LTD
View PDF7 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The purpose of this invention is to provide a martensitic stainless steel continuous annealing and pickling line welding me
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Example Embodiment
[0021] Example 1,
[0022] The specific MIG welding parameters for 50Cr15MoV stainless steel are shown in Table 1.
[0023]
[0024] The annealing and pickling line needs to weld two coils of annealed 50Cr15MoV stainless steel with a thickness of 5.0mm before and after welding. First, according to the coil thickness, use the corresponding parameters in Table 1 to weld the coil weld 1 to form. The welding wire is 309Si and the specification is 1.2mm.
[0025] The rib 3 is prepared in advance, the material is 304 annealed, the electrode material is 309L, and the specification is 2.5*350mm. The size of the ribs 3 is the same, the specific specification is 4.0 (thickness)*100*300mm, and the circumference is arc-shaped, and the arc radius is 10mm to avoid stress concentration and cracking at the corners. The specific shape is as figure 1 Shown.
[0026] Use a crescent-shaped incision shearing device to cut off the arc starting and ending arc sections of the steel coil weld 1 to avoid poo...
Example Embodiment
[0032] Example 2,
[0033] The annealing and pickling line needs to weld two coils of annealed 50Cr15MoV stainless steel with a thickness of 3.0mm before and after welding. First, according to the coil thickness, use the corresponding parameters in Table 1 to weld the coil weld 1 to form. The welding wire is 309Si and the specification is 1.2mm.
[0034] Prepare the rib 3 in advance, the material is 304 annealed, the size of the rib 3 is the same, the specific specification is 1.5 (thickness) *100*300mm, and the circumference is arc-shaped, the arc radius is 5mm, to avoid stress concentration cracking at the corners , The specific form is like figure 1 Shown.
[0035] Use a crescent-shaped incision shearing device to cut off the arc starting and ending arc sections of the steel coil weld 1 to avoid poor forming at these two places, causing the strip to first crack in the arc starting and ending arc sections during operation, and then welding Seam torn.
[0036] Two operators stand ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
Size
aaaaa
aaaaa
Arc radius
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a continuous annealing and pickling line welding method for martensitic stainless steel, and belongs to the field of stainless steel welding. The problem that the welding lineof martensitic stainless steel coils with the carbon content of 0.5% or above is likely to crack is solved. The method includes the following steps that an MIG welding machine is adopted for welding stainless steel coils at the inlet of an annealing and pickling line; a shearing device is used for cutting away the arc striking and arc extinguishing sections of a steel coil welding line to avoid poor forming of the two sections because the arc striking and arc extinguishing sections crack first in the strip steel moving process, which leads to welding line tearing; rib plates are welded to thetwo sides of the steel coil welding line at the same time, and then a rib plate is welded to the middle of the steel coil welding line, wherein it is required to weld the peripheries of the rib platescompletely with no seam left to avoid the situation that acid liquor remains in the seam and contaminates the surface after flowing out; and after the rib plates are welded, air cooling is performedto reduce the martensite formation amount and the hardness of a heat-affected zone. The method can effectively avoid the situation that the welding line of the martensitic stainless steel coils with the carbon content of 0.5% or above cracks in the annealing and pickling line.
Description
technical field [0001] The invention belongs to the field of stainless steel welding, in particular to a martensitic stainless steel continuous annealing pickling line welding method. Background technique [0002] With the development of the domestic knife and scissors market, 50Cr15MoV stainless steel, as a high-carbon martensitic stainless steel, has a hardness of 56-58 HRC after quenching. 50Cr15MoV stainless steel has good corrosion resistance, processability and grindability, and is widely used in the production of high-end knives. There are relatively few domestic steel mills that can produce this type of steel, mainly because its production is difficult, which is mainly reflected in smelting, hot rolling, cold rolling, welding and other processes. When the hot-rolled and cold-rolled coils of this steel type are produced on the annealing and pickling line, in order to ensure continuous production, the coils must be welded by welding machines. The current welding techn...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
IPC IPC(8): B23K9/173B23K9/32
CPCB23K9/173B23K9/32
Inventor 李照国李聚宝潘吉祥王军伟申德
Owner GANSU JIU STEEL GRP HONGXING IRON & STEEL CO LTD
Login to view more