Preparation method of colorful composite material for art

A composite material and colorful technology, which is applied in the field of art manufacturing and architectural decoration, can solve the problems of not forming multi-metal, multi-color and colorful composite materials preparation process, difficult to meet the needs of arts and crafts products, and the number of composite materials is small, and achieves diversity. Abundant, low cost, suitable for industrial production

Active Publication Date: 2020-02-21
CHINALCO MATERIALS APPL RES INST CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The metal composite material prepared by the above method has fewer composite numbers, and the color and shape are relatively single. There is no multi-metal, multi-color, multi-shape colorful composite material preparation process, and the products are difficult to meet the requirements of arts and crafts products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of colorful composite material for art

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The material of the mosaic rod is red copper alloy and yellow brass. The shape of the rod is cylindrical and square, and the cross-sectional area of ​​a single rod is 20mm. 2 , clean the surface of the inlay rod with cleaning solution, and dry it in an oven at 50°C for 2 hours, and reserve it for later use; fix the inlay rod in the casting mold, and the volume ratio of the inlay rod accounts for 1 / 3 of the casting space of the casting mold 5%, set the induction heating coil outside the casting mold, preheat the inlaid rod material and the casting mold 5 minutes before casting, the preheating temperature of the inlaid rod material is 100°C; place 10 split vents above the casting port of the casting mold The funnel-shaped pouring cap, the diameter of the split port is 10mm. The base metal is made of white color metal. The white color metal is smelted by directly prepared alloy, and the melting is completed in the melting furnace. The inlaid rod materials form a metallurg...

Embodiment 2

[0028] The material of the mosaic rod is white metal and yellow brass. The shape of the rod is square and irregular. The cross-sectional area of ​​a single rod is 80mm 2 , clean the surface of the inlay rod with cleaning solution, and dry it in an oven at 100°C for 30 minutes, and save it for later use; fix the inlay rod in the casting mold, and the volume ratio of the inlay rod accounts for 1% of the casting space of the casting mold 90%, set the induction heating coil outside the casting mold, preheat the inlaid rod material and the casting mold 30 minutes before casting, the preheating temperature of the inlaid rod material is 400 ° C; place 5 split ports above the casting port of the casting mold The funnel-shaped pouring cap, the diameter of the split port is 20mm. The base metal is made of red copper alloy. The red copper alloy is smelted by the directly prepared alloy. The melting is completed in the melting furnace. The melted and heat-preserved base metal liquid is po...

Embodiment 3

[0030] The material of the mosaic rod is red color copper alloy and white color metal, the shape of the rod is cylindrical and special-shaped, and the cross-sectional area of ​​a single rod is 50mm 2 , clean the surface of the inlay rod with cleaning solution, and dry it in an oven at 150°C for 1 hour, and save it for later use; fix the inlay rod in the casting mold, and the volume ratio of the inlay rod accounts for 1 / 3 of the casting space of the casting mold 10%, set the induction heating coil outside the casting mold, preheat the inlaid rod material and the casting mold 10 minutes before casting, the preheating temperature of the inlaid rod material is 200°C; place a split vent above the casting port of the casting mold The funnel-shaped pouring cap, the diameter of the split port is 30mm. The base metal is made of yellow brass, and the brass is smelted by a directly prepared alloy. The smelting is completed in the melting furnace. The molten and heat-preserved base metal ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
areaaaaaaaaaaa
areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a colorful composite material for art. The preparation method comprises the following steps of firstly, cleaning the surface of an inlay rod material, fixing the inlay rod material in a casting mold, arranging an induction heating coil on the periphery of the casting mold, and placing a casting cap with a plurality of diverting openings above the casting mold; and casting molten heat-insulated base metal liquid into the casting cap and then into the casting mold through the diverting openings, and forming metallurgical bonding with the inlay rodmaterial to prepare the colorful composite material. According to the method, compared with an existing bimetallic production method, the shape of the inlay material and the color diversity of the alloy are richer. The preparation process is suitable for industrial production, and can be applied to the fields of art manufacturing, building decoration and the like.

Description

technical field [0001] The invention relates to a preparation method of a composite material, in particular to a preparation method of a colorful composite material, which is mainly used in art manufacturing, architectural decoration and other fields. Background technique [0002] Since metals have various metal colors such as white, red, yellow, rose gold, etc., in recent years, with the increasing demand for metal arts and crafts products, people hope that the developed alloy materials have a variety of alloy colors, so that In the subsequent process development process, the original color of the metal can be used to prepare a variety of arts and crafts products. At present, the traditional metal composite materials mainly use plates and plates to perform bimetallic or trimetallic composites through casting, hot rolling or cold rolling to form layered composite materials; or tubes and tubes or The tube and rod method is compounded by casting, drawing, etc., and the final ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22D19/16
CPCB22D19/0081B22D19/16
Inventor 陈忠平娄花芬王金华向朝建张曦杨春秀
Owner CHINALCO MATERIALS APPL RES INST CO LTD