Manufacturing method of high-temperature-resistant enameled wire

A manufacturing method and technology of enameled wire, applied in the manufacture of cables/conductors, reducing the size of conductors/cables, insulating conductors/cables, etc., can solve the problems of poor stability of enameled wires in high temperature use, large use loss, and influence of wire use, etc. problem, to achieve the effect of long service life, improved stability and strong uniformity

Inactive Publication Date: 2020-03-20
湖州中洲电磁线有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies of the prior art, the present invention provides a method for manufacturing high-temperature-resistant enameled wire, which solves the problems of poor high-temperature use stability, large use loss and influence on the use of wires produced by the enameled wire in the prior art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of high-temperature-resistant enameled wire
  • Manufacturing method of high-temperature-resistant enameled wire
  • Manufacturing method of high-temperature-resistant enameled wire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A method for manufacturing a high temperature resistant enameled wire, comprising the following steps:

[0043] A: To make the inner core, first select the copper wire, detect the burr on the outer surface of the copper wire and remove the burr. When inspecting the outer surface of the copper wire, ensure that the copper wire has no oxidation and no cracks on the surface. Both ends of the copper wire are fixed, and the copper wire is straightened by stretching equipment. The copper wire is selected as pure copper with a high conductivity of more than 99.5%;

[0044] B: wire drawing, the copper wire is drawn by drawing equipment, the number of drawing is 7 times, and the copper wire is drawn to the required diameter;

[0045] C: Cleaning, clean the oil on the surface of the copper wire to keep the copper wire flat, clean the surface of the copper wire with clean water, and filter and recycle the waste water after use;

[0046] D: Annealing, place the copper wire in the ...

Embodiment 2

[0051] A method for manufacturing a high temperature resistant enameled wire, comprising the following steps:

[0052] A: To make the inner core, first select the copper wire, detect the burr on the outer surface of the copper wire and remove the burr. When inspecting the outer surface of the copper wire, ensure that the copper wire has no oxidation and no cracks on the surface. Both ends of the copper wire are fixed, and the copper wire is straightened by stretching equipment. The copper wire is selected as pure copper with a high conductivity of more than 99.5%;

[0053] B: wire drawing, the copper wire is drawn through the drawing equipment, the number of drawing is 8 times, and the copper wire is drawn to the required diameter;

[0054] C: Cleaning, clean the oil on the surface of the copper wire to keep the copper wire flat, clean the surface of the copper wire with clean water, and filter and recycle the waste water after use;

[0055]D: Annealing, place the copper wire...

Embodiment 3

[0060] A method for manufacturing a high temperature resistant enameled wire, comprising the following steps:

[0061] A: To make the inner core, first select the copper wire, detect the burr on the outer surface of the copper wire and remove the burr. When inspecting the outer surface of the copper wire, ensure that the copper wire has no oxidation and no cracks on the surface. Both ends of the copper wire are fixed, and the copper wire is straightened by stretching equipment. The copper wire is selected as pure copper with a high conductivity of more than 99.5%;

[0062] B: wire drawing, the copper wire is drawn through the drawing equipment, the number of drawing is 9 times, and the copper wire is drawn to the required diameter;

[0063] C: Cleaning, clean the oil on the surface of the copper wire to keep the copper wire flat, clean the surface of the copper wire with clean water, and filter and recycle the waste water after use;

[0064] D: Annealing, place the copper wir...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method of a high-temperature-resistant enameled wire, and relates to the related technical field of enameled wire production, which comprises the following steps: step A, manufacturing an inner core; b, wire drawing; step C, cleaning; step D, annealing; e, cooling is conducted; f, paint spraying is conducted; and G, lubricating and taking up. The invention is advantageous in that the production is time-saving and labor-saving, detection of copper wires, the use stability of the enameled wire after production is stronger; post annealing, the annealed copper wire is cooled through the drying furnace; the temperature of the copper wire is kept at 150-230 DEG C; the subsequent insulation paint spraying and copper wire connection is more stable; the stability of the overall high-temperature resistance of the produced enameled wire is further improved; the copper wire spraying device is simple in structure, longer in service life and higher in stability, insulating paint can be sprayed to copper wires passing through the middles of the first spraying parts and the second spraying parts through cooperation of the first spraying parts and the secondspraying parts, and inner-layer paint and outer-layer paint of the copper wires can be sprayed through the multiple sets of first spraying parts and second spraying parts correspondingly.

Description

technical field [0001] The invention relates to the technical field related to the production of enameled wires, in particular to a method for manufacturing high-temperature resistant enameled wires. Background technique [0002] Enameled wire is the most representative product in electronic wire. Enameled wire is a main variety of winding wire. It is composed of two parts: conductor and insulating layer. It is not easy to produce products that meet both standard requirements and customer requirements. [0003] Affected by environmental factors, the quality characteristics of various enameled wires are different, but they all have good mechanical and chemical properties. However, in high-temperature environments, the current enameled wires have a short service life and poor high-temperature resistance. The medium loss is serious, the use is not stable enough, and the normal use of the wire is easily affected during use. [0004] Therefore, it is necessary to propose a manu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01B13/00H01B13/06H01B13/16H01B13/22
CPCH01B13/00H01B13/0006H01B13/0016H01B13/002H01B13/065H01B13/165H01B13/22
Inventor 沈嘉诚
Owner 湖州中洲电磁线有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap